Method of making thin film heterojunction solar cell
Assignee: Siemens Solar Industries International Inc
•
Filing: 1994-10-28
•
Granted: 1995-12-12
•
Expires: 2014-10-28
Abstract
Abstract A thin film photovoltaic device comprises a metal back contact having a first p-type semiconductor film of CVD CIS thereon; a second, transparent, n-type semiconductor film of CVD zinc oxide on the CIS and a thin interfacial film of transparent, insulating zinc oxide between the p-type CIS film and the n-type metal oxide. The interfacial zinc oxide film is formed by depositing zinc hydroxide on the CIS from a solution of one of zinc sulfate, zinc chloride, and zinc acetate and complexing agents comprising ammonium hydroxide and TEA and annealing the deposit to convert the zinc hydroxide to form the zinc oxide.
Inventors
- 👤 Gary A. Pollock
- 👤 Kim W. Mitchell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 00:40
CPC Classifications
H; H10; H10F; H10F10/00; H10F10/10; H10F10/16; H10F10/167; H10F71/00; H10F71/138; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/541
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
73 words
A process for making a thin film heterojunction photovoltaic device comprising the steps of: depositing a first film of p-type copper indium diselenide film on a metal back contact; chemically depositing from solution a thin film of zinc hydroxide on said first film; converting said zinc hydroxide to a transparent, insulating zinc oxide thin film; and depositing a second film of n-type transparent zinc oxide on said transparent, insulating zinc oxide thin film.
Claim 2
Dependent Claim
73 words
A process for making a thin film heterojunction photovoltaic device comprising the steps of: depositing a first film of p-type copper indium diselenide film on a metal back contact; chemically depositing from solution a thin film of zinc hydroxide on said first film; converting said zinc hydroxide to a transparent, insulating zinc oxide thin film; and depositing a second film of n-type transparent zinc oxide on said transparent, insulating zinc oxide thin film.
Claim 3
Dependent Claim
83 words
A process according to claim 1 in which the film of transparent, insulating zinc oxide is deposited by the steps of: mixing a zinc salt with a suitable complexing agent to dissolve the zinc salt and form a zinc/ammonium (Zn/NH 4 ) complex in solution; contacting the first film with the solution to deposit said thin film of zinc hydroxide from the solution thereon; annealing the deposited zinc hydroxide film to convert the zinc hydroxide to said transparent, insulating zinc oxide thin film.
Claim 4
Dependent Claim
21 words
A process according to claim 2 in which the zinc salt is one of zinc sulphate, zinc chloride, and zinc acetate.
Claim 5
Dependent Claim
13 words
A process according to claim 2 wherein the complexing agent comprises ammonium hydroxide.
Claim 6
Dependent Claim
20 words
A process according to claim 4 wherein the zinc salt is zinc acetate and the complexing agent further comprises triethanolamine.
Claim 7
Dependent Claim
22 words
A process according to claim 5 wherein the solution comprises 0.001M to 0.1M zinc salt dissolved in 0.001M to 1.5M ammonium hydroxide.
Claim 8
Dependent Claim
22 words
A process according to claim 6 wherein the solution comprises 0.01M to 0.1M zinc salt dissolved in 0.1M to 1.5M ammonium hydroxide.
Claim 9
Dependent Claim
20 words
A process according to claim 7 wherein the solution comprises approximately 0.01M zinc salt dissolved in approximately 0.7M ammonium hydroxide.
Claim 10
Dependent Claim
25 words
A process according to claim 5 wherein the solution comprises 0.01M to 0.1M zinc acetate, 0.01M to 0.1M TEA and 0.6M to 1.5M ammonium hydroxide.
Claim 11
Dependent Claim
20 words
A process according to claim 9 wherein the solution comprises approximately 0.01M zinc acetate, 0.01M TEA and 0.64M ammonium hydroxide.
Claim 12
Dependent Claim
22 words
A process according to claim 9 wherein the thickness of the film of insulating zinc oxide is no greater than 10 angstroms.
Claim 13
Dependent Claim
24 words
A process according to claim 9 wherein the first film is contacted with the solution for a period of between 1 and 10 minutes.
Claim 14
Dependent Claim
13 words
A process according to claim 4 wherein the zinc salt is zinc sulfate.
References Cited (Backward Citations)
US4335266A
Cited
US4611091A
Cited
US4612411A
Cited
US5045409A
Cited
US4915745A
Cited
US4915745B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-12-11 | 1999-06-12 | 1999-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-12-11 | 2003-06-12 | 2003-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-12-11 | 2007-06-12 | 2007-12-12 | $7700.00 | Window Closed / Lapsed |