US5474820A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Biaxially-oriented multilayer polyolefin film with a silk-matt finish, process for its preparation and use thereof
Assignee: Hoechst AG
•
Filing: 1993-03-30
•
Granted: 1995-12-12
•
Expires: 2013-03-30
Abstract
Abstract A multilayer polypropylene film is disclosed that has at least one base layer containing polypropylene and at least one outer layer containing a mixture of two mixture components I and II. Mixture component I is essentially a polypropylene homopolymer or a copolymer of ethylene and propylene or ethylene and butylene or propylene and butylene or ethylene and another α-olefin having 5 to 10 carbon atoms or propylene and another α-olefin having 5 to 10 carbon atoms or a terpolymer of ethylene and propylene and butylene or ethylene and propylene and another α-olefin having 5 to 10 carbon atoms or a mixture of two or more of said homopolymers, copolymers and terpolymers or a blend of two or more of said homopolymers, copolymers and terpolymers, if desired mixed with one or more of said homopolymers, copolymers and terpolymers. Mixture component II is essentially an HDPE or a blend of two blend components A and B. Blend component A is essentially an HDPE. Blend component B is essentially a polypropylene homopolymer or a copolymer of ethylene and propylene or ethylene and butylene or propylene and butylene or ethylene and another α-olefin having 5 to 10 carbon atoms or propylene and another α-olefin having 5 to 10 carbon atoms or a terpolymer of ethylene and propylene and butylene or ethylene and propylene and another α-olefin having 5 to 10 carbon atoms or a mixture of two or more of said homopolymers, copolymers and terpolymers or a blend of two or more of said homopolymers, copolymers and terpolymers. The film has a silk-matt finish.
Inventors
- 👤 Ursula Murschall
- 👤 Angela Speith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:48
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/32; B32B27/06; B32B27/08; B32B27/18; C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/10; C08L23/12; C08L23/14; C08L23/142; B29; B29K; B29K2995/00; B29K2995/0037; B29K2995/0072; B32B2307/00; B32B2307/70; B32B2307/718; B32B2307/746; B32B2323/00; B32B2323/04; B32B2323/043; C08L2205/00; C08L2205/02; C08L2205/03; C08L23/06; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1355; Y10T428/1359; Y10T428/28; Y10T428/2813; Y10T428/2817; Y10T428/2826; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31855; Y10T428/3188; Y10T428/31895; Y10T428/31909; Y10T428/31913
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
319 words
A multilayer polypropylene film comprising: at least one base layer comprising polypropylene, and at least one outer layer comprising a mixture of components I and II, wherein mixture component I is selected from the group consisting of a propylene homopolymer, a copolymer of ethylene and propylene, a copolymer of ethylene and butylene, a copolymer of propylene or butylene, a copolymer of ethylene and another α-olefin having 5 to 10 carbon atoms, a copolymer of propylene and another α-olefin having 5 to 10 carbon atoms, a terpolymer of ethylene, propylene and butylene, a terpolymer of ethylene, propylene and another α-olefin having 5 to 10 carbon atoms, a mixture of two or more of said homopolymers, copolymers and terpolymers, and a blend of two or more of said homopolymers, copolymers and terpolymers that is optionally mixed with one or more of said homopolymers, copolymers and terpolymers, and wherein mixture component II is selected from the group consisting of (i) an HDPE and (ii) a blend of two blend components A and B, in which blend component A consists essentially of an HDPE and blend component B consists essentially of a propylene homopolymer, a copolymer of ethylene and propylene, a copolymer of ethylene and butylene, a copolymer of propylene and butylene, a copolymer of ethylene and another α-olefin having 5 to 10 carbon atoms, a copolymer of propylene and another α-olefin having 5 to 10 carbon atoms, a terpolymer of ethylene, propylene and butylene, a terpolymer of ethylene, propylene and another α-olefin having 5 to 10 carbon atoms, a mixture of two or more of said homopolymers, copolymers and terpolymers, and a blend of two or more homopolymers, copolymers and terpolymers, and wherein the film has a silk-matt finish having a sheen value of less than about 80 at a measurement angle of 85°, measured in accordance with ASTM-D-523-78 and a haze of greater than about 30, measured in accordance with ASTM-D-1003.
Claim 2
Dependent Claim
319 words
A multilayer polypropylene film comprising: at least one base layer comprising polypropylene, and at least one outer layer comprising a mixture of components I and II, wherein mixture component I is selected from the group consisting of a propylene homopolymer, a copolymer of ethylene and propylene, a copolymer of ethylene and butylene, a copolymer of propylene or butylene, a copolymer of ethylene and another α-olefin having 5 to 10 carbon atoms, a copolymer of propylene and another α-olefin having 5 to 10 carbon atoms, a terpolymer of ethylene, propylene and butylene, a terpolymer of ethylene, propylene and another α-olefin having 5 to 10 carbon atoms, a mixture of two or more of said homopolymers, copolymers and terpolymers, and a blend of two or more of said homopolymers, copolymers and terpolymers that is optionally mixed with one or more of said homopolymers, copolymers and terpolymers, and wherein mixture component II is selected from the group consisting of (i) an HDPE and (ii) a blend of two blend components A and B, in which blend component A consists essentially of an HDPE and blend component B consists essentially of a propylene homopolymer, a copolymer of ethylene and propylene, a copolymer of ethylene and butylene, a copolymer of propylene and butylene, a copolymer of ethylene and another α-olefin having 5 to 10 carbon atoms, a copolymer of propylene and another α-olefin having 5 to 10 carbon atoms, a terpolymer of ethylene, propylene and butylene, a terpolymer of ethylene, propylene and another α-olefin having 5 to 10 carbon atoms, a mixture of two or more of said homopolymers, copolymers and terpolymers, and a blend of two or more homopolymers, copolymers and terpolymers, and wherein the film has a silk-matt finish having a sheen value of less than about 80 at a measurement angle of 85°, measured in accordance with ASTM-D-523-78 and a haze of greater than about 30, measured in accordance with ASTM-D-1003.
Claim 3
Dependent Claim
85 words
A multilayer polypropylene film as claimed in claim 1, wherein mixture component I is selected from the group consisting of a propylene homopolymer, a copolymer of ethylene and propylene, a copolymer of ethylene and 1-butylene, a copolymer of propylene and 1-butylene, a terpolymer of ethylene and propylene and 1-butylene, a mixture of two or more said homopolymers, copolymers and terpolymers, and a blend of two or more said homopolymers, copolymers and terpolymers, if desired mixed with one or more of said homopolymers, copolymers and terpolymers.
Claim 4
Dependent Claim
155 words
A multilayer polypropylene film as claimed in claim 1, wherein mixture component I is selected from the group consisting of a propylene homopolymer, a random ethylene-propylene copolymer having an ethylene content of 2 to 10% by weight, a random propylene-1-butylene copolymer having a butylene content of from 4 to 25% by weight, in each case based on the total weight of the copolymer, a random ethylene-propylene-1-butylene terpolymer having an ethylene content of from 1 to 10% by weight, and a 1-butylene content of from 3 to 20% by weight, in each case based on the total weight of the terpolymer, and a blend of an ethylene-propylene-1-butylene terpolymer and a propylene-1-butylene copolymer having an ethylene content of from 0.1 to 7% by weight, a propylene content of from 50 to 90% by weight and a 1-butylene content of from 10 to 40% by weight, in each case based on the total weight of the polymer blend.
Claim 5
Dependent Claim
76 words
A multilayer polypropylene film as claimed in claim 2, wherein blend component B is selected from the group consisting of a propylene homopolymer, a copolymer of ethylene and propylene, a copolymer of ethylene and 1-butylene, a copolymer of propylene and 1-butylene, a terpolymer of ethylene and propylene and 1-butylene, a mixture of two or more of said homopolymers, copolymers and terpolymers, and a blend of two or more of said particularly preferred homopolymers, copolymers and terpolymers.
Claim 6
Dependent Claim
157 words
A multilayer polypropylene film as claimed in claim 3, wherein blend component B is selected from the group consisting of a propylene homopolymer, or a random ethylene-propylene copolymer having an ethylene content of 2 to 10% by weight and a random propylene-1-butylene copolymer having a butylene content of from 4 to 25% by weight, in each case based on the total weight of the copolymer, a random ethylene-propylene-1-butylene terpolymer having an ethylene content of from 1 to 10% by weight and a 1-butylene content of from 3 to 20% by weight, in each case based on the total weight of the terpolymer, and a blend of an ethylene-propylene-1-butylene terpolymer and a propylene-1-butylene copolymer having an ethylene content of from 0.1 to 7% by weight, a propylene content of from 50 to 90% by weight and a 1-butylene content of from 10 to 40% by weight, in each case based on the total weight of the polymer blend.
Claim 7
Dependent Claim
101 words
A multilayer polypropylene film as claimed in claim 1, wherein the HDPE has a melt flow index measured in accordance with DIN 53 735 with a load of 50N at 190° C., of from 0.2 to 50 g/10 min, a viscosity index, measured in accordance with DIN 53 728, Part 4, of from 100 to 450 cm 3 /g, a density, measured in accordance with DIN 53 479, Method A, of from 0.93 to 0.97 g/cm 3 , a degree of crystallization of from 35° to 80°, and a melting point of from 120° to 150° C. according to DSC measurement.
Claim 8
Dependent Claim
26 words
A multilayer polypropylene film as claimed in claim 1, wherein the ratio between blend components A and B is in the range from A:B=20:80 to A:B=80:20.
Claim 9
Dependent Claim
26 words
A multilayer polypropylene film as claimed in claim 1, wherein the ratio between blend components A and B is in the range from A:B=40:60 to A:B=60:40.
Claim 10
Dependent Claim
34 words
A multilayer polypropylene film as claimed in claim 1, wherein the blend has a melt flow index of from 1.5 to 12 g/10 min, measured at 230° C. with a load of 21.6 N.
Claim 11
Dependent Claim
34 words
A multilayer polypropylene film as claimed in claim 1, wherein the blend has a melt flow index of from 2.5 to 6 g/10 min, measured at 230° C. with a load of 21.6 N.
Claim 12
Dependent Claim
26 words
A multilayer polypropylene film as claimed in claim 1, wherein the ratio between mixture components I and II is in the range from I:II=90:10 to I:II=10:90.
Claim 13
Dependent Claim
41 words
A multilayer polypropylene film as claimed in claim 1, wherein the polypropylene polymer of the base layer has a melting point of at least 140° C. and the melt flow index is in the range from 0.5 to 15 g/10 min.
Claim 14
Dependent Claim
44 words
A multilayer polypropylene film as claimed in claim 1, wherein the outer layer and the base layer contains as an additive, one or more members selected from the group consisting of an antistatic agent, an antiblocking agent, a lubricant, a stabilizer and a neutralizer.
Claim 15
Dependent Claim
38 words
A multilayer polypropylene film as claimed in claim 1, wherein said surface having a silk-matt finish has a sheen of from about 25 to about 45, measured in accordance with ASTM-D 523-78 at a measurement angle of 85°.
Claim 16
Dependent Claim
28 words
A multilayer polypropylene film as claimed in claim 14, wherein said film has a haze of from about 40 to about 80, measured in accordance with ASTM-D 1003.
Claim 17
Dependent Claim
11 words
A packaging comprising a multilayer film as claimed in claim 1.
Claim 18
Dependent Claim
29 words
An aqueous barrier coated film, comprising: a base film of a multilayer polypropylene film as claimed in claim 1; and an aqueous barrier coating layer on said base film.
Claim 19
Dependent Claim
37 words
A laminate, comprising: a base film of a multilayer polypropylene film as claimed in claim 1; and a layer selected from the group consisting of paper, cardboard, metal, metallized plastic and plastic laminated to said base film.
Claim 20
Dependent Claim
44 words
A multilayer polypropylene film as claimed in claim 1, wherein the outer layer or the base layer contains as an additive, one or more members selected from the group consisting of an antistatic agent, an antiblocking agent, a lubricant, a stabilizer and a neutralizer.
References Cited (Backward Citations)
GB1145199A
Cited
US4297415A
Cited
US4283453A
Cited
US4419411A
Cited
US4522887A
Cited
US4622237A
Cited
US4666778A
Cited
US4578316A
Cited
EP0236945A2
Cited
GB2201407A
Cited
US4855187A
Cited
EP0365463A2
Cited
EP0394550A1
Cited
EP0538746A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-12-11 | 1999-06-12 | 1999-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-12-11 | 2003-06-12 | 2003-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-12-11 | 2007-06-12 | 2007-12-12 | $7700.00 | Window Closed / Lapsed |