US5468427A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for making ultra-fine ceramic particles
Assignee: Alfred University
•
Filing: 1993-09-27
•
Granted: 1995-11-21
•
Expires: 2013-09-27
Abstract
Abstract A process for producing ultra-fine ceramic particles in which droplets are formed from a ceramic precursor mixture containing a metal cation, a nitrogen-containing fuel, a solvent, and an anion capable of participating in an anionic oxidation-reduction reaction with the nitrogen containing fuel. The nitrogen-containing fuel contains at least three nitrogen atoms, at least one oxygen atom, and at least one carbon atom. The ceramic precursor mixture is dried to remove at least 85 weight percent of the solvent, and the dried mixture is then ignited to form a combusted powder.
Inventors
- 👤 Gregory C. Stangle
- 👤 Koththavasal R. Venkatachari
- 👤 Steven P. Ostrander
- 👤 Walter A. Schulze
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:42
CPC Classifications
C; C01; C01B; C01B13/00; C01B13/14; C01B13/32; C01B13/322; C01B13/324; B; B82; B82Y; B82Y30/00; C01B13/34; C01G; C01G23/00; C01G23/003; C01G23/006; C01G23/04; C01G23/047; C01G25/00; C01G25/02; C01G3/00; C01G3/006; C01G49/00; C01G49/0018; C01G49/0036; C01G49/0054; C04; C04B; C04B35/00; C04B35/01; C04B35/45; C04B35/4504; C04B35/4508; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; C01P; C01P2004/00; C01P2004/60; C01P2004/64; C01P2006/00; C01P2006/10; C01P2006/12; C01P2006/40
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
67 words
A process for producing ultra-fine ceramic particles, comprising the steps of: (a) forming droplets of a ceramic precursor mixture containing a metal cation, a nitrogen-containing fuel, a solvent, and an anion capable of participating in an anionic oxidation-reduction reaction with the nitrogen containing fuel, wherein said nitrogen-containing fuel is of the formula R.(HA) a , wherein: 1. a is an integer of from 0 to 2, 2.
Claim 2
Dependent Claim
67 words
A process for producing ultra-fine ceramic particles, comprising the steps of: (a) forming droplets of a ceramic precursor mixture containing a metal cation, a nitrogen-containing fuel, a solvent, and an anion capable of participating in an anionic oxidation-reduction reaction with the nitrogen containing fuel, wherein said nitrogen-containing fuel is of the formula R.(HA) a , wherein: 1. a is an integer of from 0 to 2, 2.
Claim 3
Dependent Claim
95 words
HA is selected from the group consisting of HNO 3 , HCl, HBr, HI, H 2 SO 4 , H 2 O, and CH 3 COOH, 3. R is of the formula ##STR2## wherein: (a) R 1 , R 2 , R 3 , and R 4 are independently selected from the group consisting of hydrogen, alkyl of from 1 to about 4 carbon atoms, and phenyl; (b) b is an integer of from 1 to 2, c is an integer of from 0 to 2, and a plus c is at least 1, and
Claim 4
Dependent Claim
95 words
HA is selected from the group consisting of HNO 3 , HCl, HBr, HI, H 2 SO 4 , H 2 O, and CH 3 COOH, 3. R is of the formula ##STR2## wherein: (a) R 1 , R 2 , R 3 , and R 4 are independently selected from the group consisting of hydrogen, alkyl of from 1 to about 4 carbon atoms, and phenyl; (b) b is an integer of from 1 to 2, c is an integer of from 0 to 2, and a plus c is at least 1, and
Claim 5
Dependent Claim
97 words
R contains at least four hydrogen atoms, provided that the ratio of hydrogen atoms to oxygen atoms in R is at least 3; (b) removing at least about 85 weight percent of the solvent from the droplets of the ceramic precursor mixture to form particles comprising the metal cation, the anion, and the nitrogen-containing fuel, thereby forming dried particles; and (c) subjecting said dried particles to a temperature of from about 500 to about 600 degrees centigrade and an atmosphere with a relative humidity of less than about 60 percent, thereby causing said dried particles to react
Claim 6
Dependent Claim
97 words
R contains at least four hydrogen atoms, provided that the ratio of hydrogen atoms to oxygen atoms in R is at least 3; (b) removing at least about 85 weight percent of the solvent from the droplets of the ceramic precursor mixture to form particles comprising the metal cation, the anion, and the nitrogen-containing fuel, thereby forming dried particles; and (c) subjecting said dried particles to a temperature of from about 500 to about 600 degrees centigrade and an atmosphere with a relative humidity of less than about 60 percent, thereby causing said dried particles to react
Claim 7
Dependent Claim
110 words
in an explosive manner. 2. The process as recited in claim 1, further comprising the steps of: (a) milling said combusted powder until substantially all of the particles of such powder are smaller than about 0.5 microns, thereby forming a milled combusted powder; (b) forming said milled combusted powder into a green body; (c) heating said green body from ambient to a temperature of from about 1,200 to about 1,400 degrees centigrade at a rate of from about 250 to about 750 degrees centigrade per minute and, thereafter, maintaining said green body at a temperature of from about 1,200 to about 1,400 degrees centigrade for at least about 0.5 minutes.
Claim 8
Dependent Claim
13 words
The process as recited in claim 1, wherein said anion is nitrate ion.
Claim 9
Dependent Claim
18 words
The process as recited in claim 3, wherein said ceramic precursor mixture is comprised of a barium compound.
Claim 10
Dependent Claim
18 words
The process as recited in claim 4, wherein said ceramic precursor mixture is comprised of a titanium compound.
Claim 11
Dependent Claim
22 words
The process as recited in claim 3, wherein said ceramic precursor mixture is comprised of yttrium nitrate, barium nitrate, and copper nitrate.
Claim 12
Dependent Claim
13 words
The process as recited in claim 1, wherein said metal cation is zirconium.
Claim 13
Dependent Claim
26 words
The process as recited in claim 7, wherein said ceramic precursor mixture is comprised of from about 80 to about 98 weight percent of zirconyl nitrate.
Claim 14
Dependent Claim
26 words
The process as recited in claim 8, wherein said ceramic precursor mixture is comprised of from about 2 to about 20 weight percent of yttrium nitrate.
Claim 15
Dependent Claim
14 words
The process as recited in claim 1, wherein said solvent consists essentially of water.
Claim 16
Dependent Claim
25 words
The process as recited in claim 1, wherein at least about 80 weight percent of said droplets have a maximum dimension of about 6 microns.
Claim 17
Dependent Claim
40 words
The process as recited in claim 1, wherein said particles comprising the metal cation, the anion, and the nitrogen-containing fuel are formed into a pellet and, thereafter, heated to a temperature of from about 275 to about 750 degrees centigrade.
Claim 18
Dependent Claim
29 words
The process as recited in claim 1, wherein said combusted powder is coated with a material capable of being converted into a transition metal oxide by precipitation and heat.
Claim 19
Dependent Claim
42 words
The process as recited in claim 13, wherein said material is comprised of a transition metal compound selected from the group consisting of the nitrate, the sulfate, the carbonate, the chloride, the oxalate, the acetate, and the hydroxide of a transition metal.
Claim 20
Dependent Claim
25 words
The process as recited in claim 13, wherein said combusted powder is dispersed in a slurry containing water, carbonate ion, and a transition metal compound.
Claim 21
Dependent Claim
18 words
The process as recited in claim 1, wherein said combusted powder is milled in a sol-gel forming solution.
Claim 22
Dependent Claim
17 words
The process as recited in claim 16, wherein said sol-gel forming solution is comprised of tetraethyl orthosilicate.
References Cited (Backward Citations)
US4065544A
Cited
US4343909A
Cited
US4626451A
Cited
US4810415A
Cited
US4778671A
Cited
US4988646A
Cited
US5061682A
Cited
US5102592A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-11-20 | 1999-05-22 | 1999-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-11-20 | 2003-05-22 | 2003-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-11-20 | 2007-05-22 | 2007-11-21 | $7700.00 | Window Closed / Lapsed |