Process for making an interconnect bump for flip-chip integrated circuit including integral standoff and hourglass shaped solder coating
Assignee: Adeia Semiconductor Technologies LLC
•
Filing: 1994-06-02
•
Granted: 1995-11-14
•
Expires: 2014-06-02
Abstract
Abstract An interconnect bump is formed on a substrate structure of a flip-chip microelectronic integrated circuit by sputtering a metal base layer on the substrate, and then forming a copper standoff on the base layer. A solder cap is formed on the standoff having a peripheral portion that extends laterally external of the standoff. The peripheral portion of the cap is used as a self-aligned mask for a photolithographic step that results in removing the metal base layer except under the standoff and the cap. The cap has a lower melting point than the standoff. Heat is applied that is sufficient to cause the cap to melt over and coat the standoff and insufficient to cause the standoff to melt. The peripheral portions of the cap and the base layer that extend laterally external of the standoff cause the melted solder to form into a generally hourglass shape over the standoff due to surface tension.
Inventors
- 👤 Brian Lynch
- 👤 Patrick O'Brien
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:58
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/341; H05K3/3431; H05K3/3436; H10; H10W; H10W70/00; H10W70/099; H10W72/00; H10W72/20; H10W90/00; H10W90/701; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0364; H05K2201/0367; H10W72/01; H10W72/012; H10W72/01251; H10W72/01255; H10W72/251; H10W72/252; H10W72/255; H10W72/281; H10W72/283; H10W72/90; H10W72/941; H10W72/9415; Y; Y02; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
176 words
A method of fabricating an interconnect bump on a substrate structure, comprising the steps of: (a) forming a standoff on the substrate structure; forming a cap on the standoff having a peripheral portion that extends laterally external of the standoff, the cap having a lower melting point than the standoff: (c) applying heat that is sufficient to cause the cad to melt over and coat the standoff and insufficient to cause the standoff to melt; and (d) prior to step (c), forming a base under the standoff having a peripheral portion that extends laterally external of the standoff, the base being wetted by the cap in step (c); in which step (d) comprises the substeps of: (e) forming a base layer on the substrate structure; (f) forming a photoresist section on a portion of said base layer corresponding to said peripheral portion of the base using said peripheral portion of the cap as a self-aligned mask; (g) removing said base layer except under said photoresist section to form the base; and (h) removing said photoresist section.
Claim 2
Independent Claim
176 words
A method of fabricating an interconnect bump on a substrate structure, comprising the steps of: (a) forming a standoff on the substrate structure; forming a cap on the standoff having a peripheral portion that extends laterally external of the standoff, the cap having a lower melting point than the standoff: (c) applying heat that is sufficient to cause the cad to melt over and coat the standoff and insufficient to cause the standoff to melt; and (d) prior to step (c), forming a base under the standoff having a peripheral portion that extends laterally external of the standoff, the base being wetted by the cap in step (c); in which step (d) comprises the substeps of: (e) forming a base layer on the substrate structure; (f) forming a photoresist section on a portion of said base layer corresponding to said peripheral portion of the base using said peripheral portion of the cap as a self-aligned mask; (g) removing said base layer except under said photoresist section to form the base; and (h) removing said photoresist section.
Claim 3
Dependent Claim
34 words
A method as in claim 1, in which steps (a) and (b) comprise forming the standoff and the cap respectively of materials such that the standoff is wetted by the cap in step (c).
Claim 4
Dependent Claim
31 words
A method as in claim 1, in which step (b) comprises forming said peripheral portion such that the cap melts over the standoff into a generally hourglass shape in step (c).
Claim 5
Dependent Claim
130 words
A method as in claim 1, in which: step (f) comprises the substeps, performed prior to step (a), of: (i) forming a photoresist layer on said base layer; and (j) forming a hole through said photoresist layer; step (a) comprises forming the standoff in said hole; step (b) comprises forming the cap on the standoff such that said peripheral portion of the cap extends over said photoresist layer; step (f) comprises the substeps, performed between steps (b) and (g), of: (m) exposing said photoresist layer using said peripheral portion of the cap as a self-aligned mask; and (n) developing said photoresist layer to form said photoresist section; and step (g) comprises etching away said base layer using an etchant that does not etch said photoresist section to form the base.
Claim 6
Dependent Claim
66 words
A method as in claim 4, in which: step (a) comprises forming the standoff to a thickness that is smaller than a thickness of said photoresist layer such that a recess is formed in said hole above the standoff; and step (b) comprises forming the cap to a thickness that is larger than a depth of said recess such that the cap extends above said hole.
Claim 7
Independent Claim
227 words
A method of fabricating an interconnect bump on a substrate structure, comprising the steps of: (a) forming a standoff on the substrate structure; (b) forming a cap on the standoff having a peripheral portion that extends laterally external of the standoff, the cap having a lower melting point than the standoff; and (c) applying heat that is sufficient to cause the cap to melt over and coat the standoff and insufficient to cause the standoff to melt; and (d) prior to step (c), forming a base under the standoff having a peripheral portion that extends laterally external of the standoff, the base being wetted by the cap in step (c); in which: step (d) comprises the substeps of: (e) forming a base layer on the substrate structure; (f) forming a photoresist section on a portion of said base layer corresponding to said peripheral portion of the base using said peripheral portion of the cap as a self-aligned mask; (g) removing said base layer except under said photoresist section to form the base; and (h) removing said photoresist section; and steps (a) and (b) comprise forming the standoff and the cap of electrically conductive metals respectively that are selected such that the cap wets the standoff in step (c); and step (a) comprises forming the standoff of a material selected from the group consisting of copper and gold.
Claim 8
Independent Claim
227 words
A method of fabricating an interconnect bump on a substrate structure, comprising the steps of: (a) forming a standoff on the substrate structure; (b) forming a cap on the standoff having a peripheral portion that extends laterally external of the standoff, the cap having a lower melting point than the standoff; and (c) applying heat that is sufficient to cause the cap to melt over and coat the standoff and insufficient to cause the standoff to melt; and (d) prior to step (c), forming a base under the standoff having a peripheral portion that extends laterally external of the standoff, the base being wetted by the cap in step (c); in which: step (d) comprises the substeps of: (e) forming a base layer on the substrate structure; (f) forming a photoresist section on a portion of said base layer corresponding to said peripheral portion of the base using said peripheral portion of the cap as a self-aligned mask; (g) removing said base layer except under said photoresist section to form the base; and (h) removing said photoresist section; and steps (a) and (b) comprise forming the standoff and the cap of electrically conductive metals respectively that are selected such that the cap wets the standoff in step (c); and step (a) comprises forming the standoff of a material selected from the group consisting of copper and gold.
Claim 9
Independent Claim
227 words
A method of fabricating an interconnect bump on a substrate structure, comprising the steps of: (a) forming a standoff on the substrate structure; (b) forming a cap on the standoff having a peripheral portion that extends laterally external of the standoff, the cap having a lower melting point than the standoff; and (c) applying heat that is sufficient to cause the cap to melt over and coat the standoff and insufficient to cause the standoff to melt; and (d) prior to step (c), forming a base under the standoff having a peripheral portion that extends laterally external of the standoff, the base being wetted by the cap in step (c); in which: step (d) comprises the substeps of: (e) forming a base layer on the substrate structure; (f) forming a photoresist section on a portion of said base layer corresponding to said peripheral portion of the base using said peripheral portion of the cap as a self-aligned mask; (g) removing said base layer except under said photoresist section to form the base; and (h) removing said photoresist section; and steps (a) and (b) comprise forming the standoff and the cap of electrically conductive metals respectively that are selected such that the cap wets the standoff in step (c); and step (a) comprises forming the cap of a material selected from the group consisting of solder and indium.
Claim 10
Independent Claim
227 words
A method of fabricating an interconnect bump on a substrate structure, comprising the steps of: (a) forming a standoff on the substrate structure; (b) forming a cap on the standoff having a peripheral portion that extends laterally external of the standoff, the cap having a lower melting point than the standoff; and (c) applying heat that is sufficient to cause the cap to melt over and coat the standoff and insufficient to cause the standoff to melt; and (d) prior to step (c), forming a base under the standoff having a peripheral portion that extends laterally external of the standoff, the base being wetted by the cap in step (c); in which: step (d) comprises the substeps of: (e) forming a base layer on the substrate structure; (f) forming a photoresist section on a portion of said base layer corresponding to said peripheral portion of the base using said peripheral portion of the cap as a self-aligned mask; (g) removing said base layer except under said photoresist section to form the base; and (h) removing said photoresist section; and steps (a) and (b) comprise forming the standoff and the cap of electrically conductive metals respectively that are selected such that the cap wets the standoff in step (c); and step (a) comprises forming the cap of a material selected from the group consisting of solder and indium.
References Cited (Backward Citations)
US4427715A
Cited
US4545610A
Cited
US5134460A
Cited
US4818728A
Cited
JPS63174337A
Cited
JPS6477948A
Cited
US5014111A
Cited
JPH025540A
Cited
JPH02177540A
Cited
US5272376A
Cited
US5147084A
Cited
US5075965A
Cited
US5233504A
Cited
US5154341A
Cited
JPH0562979A
Cited
JPH05129303A
Cited
JPH05206139A
Cited
US5349500A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-11-13 | 1999-05-15 | 1999-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-11-13 | 2003-05-15 | 2003-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-11-13 | 2007-05-15 | 2007-11-14 | $7700.00 | Window Closed / Lapsed |