Dual etching of ceramic materials
Assignee: Texas Instruments Inc
•
Filing: 1994-04-04
•
Granted: 1995-11-14
•
Expires: 2014-04-04
Abstract
Abstract A novel method etching through a substrate (e.g. BST 22) comprises removi A n5 Vthick substrate material from the backside of the substrate to form vias (e.g. cavity 24) all the way to the back surface of a frontside thin film (e.g. optical coating 20). To prevent damage to the frontside thin film while etching from the backside of the supporting substrate, the periphery of each frontside pixel is surrounded by a trench (e.g. etch stop trench 30) much deeper than the thickness of the thin film but also significantly shallower than the thickness of the substrate. This trench is then filled with an etch stop material (e.g. photoresist 32). This etch stop may be partially removed by the backside etching method but provides a tolerant means of recognizing when to stop etching before frontside film damage occurs. After etching the substrate down to and partially through the etch stop, the assembly is removed from the substrate etching medium. The remaining etch stop material may be removed with a specific agent which does not damage the frontside film. For example, if the etch stop is an organic material, such as photoresist, it may be removed from the back with a suitable solvent or dry etch without damaging either the substrate or the frontside thin film.
Inventors
- 👤 Robert A. Owen
- 👤 James F. Belcher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:23
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B41/53; C04B41/5338; C04B41/80; C04B41/91; H; H10; H10N; H10N15/00; H10N15/10; C04B2111/00; C04B2111/00474; C04B2111/00844
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
167 words
A method of forming a microelectronic structure, said method comprising steps: (a) providing a ceramic substrate having a front side and a back side; (b) etching a first pattern partially into said front side of said substrate, thereby forming etch stop trenches having said first pattern; (c) filling said etch stop trenches with an etch stop material; (d) depositing a thin front layer on said front side of said substrate; (e) etching a second pattern into said back side of said substrate, said second pattern substantially the same as said first pattern, and substantially aligned with said etch stop trenches on said front side, thereby forming cavities extending down to and partially into said etch stop material, but not extending to said thin front layer; and (f) removing said etch stop material, thereby forming isolated islands of said ceramic substrate connected by said thin front layer, whereby the thin front layer remains substantially undamaged, having not been exposed to the etching processes of steps (b) and (e).
Claim 2
Independent Claim
167 words
A method of forming a microelectronic structure, said method comprising steps: (a) providing a ceramic substrate having a front side and a back side; (b) etching a first pattern partially into said front side of said substrate, thereby forming etch stop trenches having said first pattern; (c) filling said etch stop trenches with an etch stop material; (d) depositing a thin front layer on said front side of said substrate; (e) etching a second pattern into said back side of said substrate, said second pattern substantially the same as said first pattern, and substantially aligned with said etch stop trenches on said front side, thereby forming cavities extending down to and partially into said etch stop material, but not extending to said thin front layer; and (f) removing said etch stop material, thereby forming isolated islands of said ceramic substrate connected by said thin front layer, whereby the thin front layer remains substantially undamaged, having not been exposed to the etching processes of steps (b) and (e).
Claim 3
Dependent Claim
14 words
The method according to claim 1, wherein said ceramic substrate is barium strontium titanate.
Claim 4
Dependent Claim
43 words
The method according to claim 1, said step (b) further comprising: forming a first mask layer on said front side of said substrate before said etching of said first pattern; and removing said first mask layer after said etching of said first pattern.
Claim 5
Dependent Claim
13 words
The method according to claim 3, wherein said first mask layer is photoresist.
Claim 6
Dependent Claim
30 words
The method according to claim 1, wherein said etch stop material is selected from the group consisting of: photoresist, silicon dioxide, polyimide, parylene, epoxy, silicon nitride, and spin on glass.
Claim 7
Dependent Claim
31 words
The method according to claim 1, said step (c) further comprising: planarizing said etch stop material and said front side of said substrate after said filling of said etch stop trenches.
Claim 8
Dependent Claim
59 words
The method according to claim 1, wherein said thin front layer comprises multiple layers, and said step of depositing said thin front layer further comprises: depositing a conductive metallic layer on said front side of said substrate; depositing a transparent organic layer on said conductive metallic layer; and depositing a thin transparent metal layer on said transparent organic layer.
Claim 9
Dependent Claim
27 words
The method according to claim 7, wherein said conductive metallic layer is NiCr, said transparent organic layer is parylene, and said thin transparent metal layer is NiCr.
Claim 10
Dependent Claim
44 words
The method according to claim 1, wherein a top surface of said thin front layer opposite said ceramic substrate is mounted to a removable carrier after said step of depositing said thin front layer, wherein said carrier provides mechanical support for subsequent process steps.
Claim 11
Dependent Claim
32 words
The method according to claim 1, said method further comprising thinning said ceramic substrate by mechanically polishing said back side of said ceramic substrate before said step of etching said second pattern.
Claim 12
Dependent Claim
45 words
The method according to claim 10, said method further comprising depositing a thin electrical contact on said back side of said ceramic substrate after said step of thinning said ceramic substrate, and etching said thin electrical contact during said step of etching said second pattern.
Claim 13
Dependent Claim
13 words
The method according to claim 11, wherein said islands form infrared sensitive capacitors.
Claim 14
Dependent Claim
19 words
The method according to claim 11, wherein said thin electrical contact comprises two or more layers, and comprises indium.
Claim 15
Dependent Claim
43 words
The method according to claim 1, said step (e) further comprising: forming a second mask layer on said back side of said substrate before said etching of said second pattern; and removing said second mask layer after said etching of said second pattern.
Claim 16
Dependent Claim
13 words
The method according to claim 14, wherein said second mask layer is photoresist.
Claim 17
Dependent Claim
19 words
The method according to claim 1, wherein said steps of etching said first and second patterns comprise ion milling.
Claim 18
Dependent Claim
21 words
The method according to claim 1, wherein said etch stop material is removed with a wet solvent or a dry etch.
Claim 19
Dependent Claim
17 words
The method according to claim 1, wherein said islands of said ceramic substrate form a reticulated array.
Claim 20
Dependent Claim
15 words
The method according to claim 18, wherein said microelectronic structure is an infrared radiation detector.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-11-13 | 1999-05-15 | 1999-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-11-13 | 2003-05-15 | 2003-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-11-13 | 2007-05-15 | 2007-11-14 | $7700.00 | Window Closed / Lapsed |