Copper foil for the manufacture of printed circuit boards and method of producing the same
Assignee: Circuit Foil USA Inc
•
Filing: 1993-11-24
•
Granted: 1995-09-05
•
Expires: 2013-11-24
Abstract
Abstract A surface of copper foil is protected from oxidation and tarnishing by electrodepositing on the surface a protective layer containing metallic zinc and one or more compound of tri-valent chromium, which protection layer is easily removable by dissolution in a dilute aqueous alkaline solution and which preferably has a zinc to chromium weight ratio of 1:1 or greater. An electrodeposited copper foil especially suited for multilayer printed circuit boards has such a protective layer electrodeposited on the matte side thereof and an electrodeposited copper bonding treatment on the shiny side thereof.
Inventors
- 👤 Adam M. Wolski
- 👤 Paul Dufresne
- 👤 Kurt Ac
- 👤 Michel Mathieu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:49
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/38; H05K3/382; H05K3/384; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K2203/00; H05K2203/03; H05K2203/0307; H05K2203/07; H05K2203/0703; H05K2203/0723; H05K3/02; H05K3/022; H05K3/46; H05K3/4611; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12431; Y10T428/12438; Y10T428/12472; Y10T428/12493; Y10T428/12771; Y10T428/12785; Y10T428/12792; Y10T428/12861; Y10T428/12903; Y10T428/12993
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
83 words
Copper foil useful for the manufacture of printed circuit boards, which foil comprises: a. an electrodeposited copper base foil having a matte surface and an opposing shiny surface, b. an oxidation-and-tarnish resistant protective layer on said matte surface, which comprises metallic zinc and one or more compounds of tri-valent chromium and has a zinc to chromium weight ratio of at least about 1:1 and which is soluble in a dilute alkaline solution, and c. an electrodeposited plural-layer bonding treatment on said shiny surface.
Claim 2
Dependent Claim
83 words
Copper foil useful for the manufacture of printed circuit boards, which foil comprises: a. an electrodeposited copper base foil having a matte surface and an opposing shiny surface, b. an oxidation-and-tarnish resistant protective layer on said matte surface, which comprises metallic zinc and one or more compounds of tri-valent chromium and has a zinc to chromium weight ratio of at least about 1:1 and which is soluble in a dilute alkaline solution, and c. an electrodeposited plural-layer bonding treatment on said shiny surface.
Claim 3
Dependent Claim
20 words
The copper foil of claim 1, wherein said alkaline solution is a dilute aqueous alkaline solution at substantially ambient temperature.
Claim 4
Dependent Claim
23 words
The copper foil of claim 1, wherein the weight ratio of zinc to chromium in said protective layer is at least about 2:1.
Claim 5
Dependent Claim
30 words
The copper foil of claim 1, wherein said protective layer comprises from about 20 to about 40 wt. % zinc and from about 10 to about 20 wt. % chromium.
Claim 6
Dependent Claim
31 words
The copper foil of claim 1, wherein said bonding treatment comprises an electrodeposited dendritic copper layer on said shiny surface and an electrodeposited gilding copper layer on said dendritic copper layer.
Claim 7
Dependent Claim
31 words
The copper foil of claim 5, wherein said protective layer is electrodeposited, said zinc is metallic zinc, and the weight ratio of zinc to chromium therein is at least about 2:1.
Claim 8
Dependent Claim
44 words
Electrolytic copper foil having a matte surface and a shiny surface and the matte surface thereof being covered by an anti-corrosive, heat resistant layer, said layer comprising metallic zinc and the salts of tri-valent chromium and being soluble in a dilute aqueous alkaline solution.
Claim 9
Dependent Claim
44 words
Electrolytic copper foil having a matte surface and a shiny surface and the matte surface thereof being covered by an anti-corrosive, heat resistant layer, said layer comprising metallic zinc and the salts of tri-valent chromium and being soluble in a dilute aqueous alkaline solution.
Claim 10
Dependent Claim
20 words
The copper foil of claims 7, wherein the zinc to chromium weight ratio in said layer is greater than 1:1.
Claim 11
Dependent Claim
29 words
The copper foil of claim 7, wherein said layer contains from about 20 to about 40 wt. % zinc and from about 10 to about 20 wt. % chromium.
References Cited (Backward Citations)
US2769774A
Cited
US3625844A
Cited
US3674656A
Cited
US3857681A
Cited
USRE30180E
Cited
US3853716A
Cited
US3998601A
Cited
JPS57152490A
Cited
US4572768A
Cited
US5207889A
Cited
US5215646A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-09-04 | 1999-03-06 | 1999-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-09-04 | 2003-03-06 | 2003-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-09-04 | 2007-03-06 | 2007-09-05 | $7700.00 | Window Closed / Lapsed |