Crystallizing method of ferroelectric film
Assignee: Sharp Corp
•
Filing: 1994-10-11
•
Granted: 1995-08-22
•
Expires: 2014-10-11
Abstract
Abstract A lower capacitor electrode is formed on the basic plate 1, and thereafter a ferroelectric film, for example, a PZT film having the Pb is formed. ITO, RuO2, SnO2 which are Pt or oxide conductive material are formed as a cap layer into 200 Å or more in film thickness by a sputtering method or silicone oxide film or the like are formed with 200A or more in film thickness by a thermal CVD method. Thereafter, a thermal operating operation is effected. By the prevention of the Pb from being evaporated at the thermal processing time, the elaborate ferroelectric film of stoichiometrical perovskite construction can be formed.
Inventors
- 👤 Kazuya Ishihara
- 👤 Shigeo Onishi
- 👤 Masaya Komai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:21
CPC Classifications
H; H01; H01G; H01G7/00; H01G7/06; H10; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/682
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
115 words
A method of forming a ferroelectric film in a semiconductor device, the method comprising: forming a lower electrode on a semiconductor substrate; depositing a ferroelectric substance film on the lower electrode, the ferroelectric substance film including lead and having a crystalline construction; forming a cap layer on an entire surface of the ferroelectric substance film, the cap layer being selected from a group consisting of platinum, a conductive oxide, and a silicon oxide film; conducting a thermal heat treatment to convert the crystalline construction of the ferroelectric substance film to a perovskite construction; and wherein during the thermal heat treatment the cap layer tends to prevent lead from being evaporated from the ferroelectric substance film.
Claim 2
Independent Claim
115 words
A method of forming a ferroelectric film in a semiconductor device, the method comprising: forming a lower electrode on a semiconductor substrate; depositing a ferroelectric substance film on the lower electrode, the ferroelectric substance film including lead and having a crystalline construction; forming a cap layer on an entire surface of the ferroelectric substance film, the cap layer being selected from a group consisting of platinum, a conductive oxide, and a silicon oxide film; conducting a thermal heat treatment to convert the crystalline construction of the ferroelectric substance film to a perovskite construction; and wherein during the thermal heat treatment the cap layer tends to prevent lead from being evaporated from the ferroelectric substance film.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein the thermal heat treatment is effected by a lamp heating operation.
Claim 4
Dependent Claim
15 words
The method of claim 1, wherein the thermal heat treatment is conducted under high pressure.
Claim 5
Dependent Claim
16 words
The method of claim 1, wherein the cap layer comprises platinum having an orientation of (1,1,1).
Claim 6
Dependent Claim
17 words
The method of claim 1, wherein the cap layer has a thickness of at least 200 Angstroms.
Claim 7
Dependent Claim
43 words
The method of claim 1, wherein oxide conductors comprising the cap layer are selected from a group consisting of ITO, RuO 2 , SnO 2 , ReO 3 , LaCoO 3 , La 1-x Sr x CoO 3 , and LaCaMnO 3 .
Claim 8
Independent Claim
91 words
A method of forming a ferroelectric film in a semiconductor device, the method comprising: depositing a ferroelectric substance film on a substrate, the ferroelectric substance film including Pb and having a crystalline construction; conducting a thermal heat treatment of the ferroelectric substance film in an atmosphere having Pb or PbO gas to change the ferroelectric substance film into a perovskite crystalline construction; and wherein the presence of Pb or PbO gas in the atmosphere tends to prevent Pb from being evaporated from the ferroelectric substance film during the thermal heat treatment.
Claim 9
Independent Claim
91 words
A method of forming a ferroelectric film in a semiconductor device, the method comprising: depositing a ferroelectric substance film on a substrate, the ferroelectric substance film including Pb and having a crystalline construction; conducting a thermal heat treatment of the ferroelectric substance film in an atmosphere having Pb or PbO gas to change the ferroelectric substance film into a perovskite crystalline construction; and wherein the presence of Pb or PbO gas in the atmosphere tends to prevent Pb from being evaporated from the ferroelectric substance film during the thermal heat treatment.
Claim 10
Dependent Claim
15 words
The method of claim 7, wherein the thermal heat treatment is conducted under high pressure.
Claim 11
Independent Claim
67 words
A method for forming a ferroelectric film having a perovskite crystalline structure, the method comprising: accumulating on a base pate a ferroelectric film which includes Pb; conducting a thermal heat treatment whereby the ferroelectric film is changed to have a perovskite type crystal structure, the thermal heat treatment being conducted in an oxygen atomic atmosphere, the oxygen atomic atmosphere being formed by irradiating ozone with ultraviolet rays.
Claim 12
Independent Claim
67 words
A method for forming a ferroelectric film having a perovskite crystalline structure, the method comprising: accumulating on a base pate a ferroelectric film which includes Pb; conducting a thermal heat treatment whereby the ferroelectric film is changed to have a perovskite type crystal structure, the thermal heat treatment being conducted in an oxygen atomic atmosphere, the oxygen atomic atmosphere being formed by irradiating ozone with ultraviolet rays.
Claim 13
Dependent Claim
19 words
The method of claim 9, wherein the oxygen atomic atmosphere has a pressure of from 10 to 50 Torr.
Claim 14
Dependent Claim
16 words
The method of claim 9, wherein the thermal heat treatment is conducted at 650 degrees Centigrade.
Claim 15
Dependent Claim
17 words
The method of claim 9, wherein the ultraviolet rays have a wavelength not greater than 185 nm.
Claim 16
Independent Claim
93 words
A method for forming a ferroelectric film having a perovskite crystalline structure, the method comprising: accumulating on a base plate a ferroelectric film which includes Pb; conducting a thermal heat treatment whereby the ferroelectric film is changed to have a perovskite type crystal structure, the thermal heat treatment being conducted in an oxygen atomic atmosphere, the oxygen atomic atmosphere being formed by irradiating ozone with ultraviolet rays having a wavelength not greater than 185 nm in order to form many crystal nuclei and to confine growth of crystal grain to a small diameter.
Claim 17
Independent Claim
93 words
A method for forming a ferroelectric film having a perovskite crystalline structure, the method comprising: accumulating on a base plate a ferroelectric film which includes Pb; conducting a thermal heat treatment whereby the ferroelectric film is changed to have a perovskite type crystal structure, the thermal heat treatment being conducted in an oxygen atomic atmosphere, the oxygen atomic atmosphere being formed by irradiating ozone with ultraviolet rays having a wavelength not greater than 185 nm in order to form many crystal nuclei and to confine growth of crystal grain to a small diameter.
Claim 18
Dependent Claim
35 words
The method of claim 13, wherein ozone (O 3 ) is decomposed into O.sub.(1D) and oxygen O 2 , and whereby oxidation is promoted with the O.sub.(1D) to prevent oxygen deficit defects in the film.
Claim 19
Dependent Claim
29 words
The method of claim 13, wherein the oxygen atomic atmosphere is formed by irradiating ozone with ultraviolet rays having a wavelength not greater than 185 nm for one minute.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-08-21 | 1999-02-20 | 1999-08-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-08-21 | 2003-02-20 | 2003-08-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-08-21 | 2007-02-20 | 2007-08-22 | $7700.00 | Window Closed / Lapsed |