Dimensionally graded conductive foam
Assignee: Lockheed Martin Corp
•
Filing: 1993-05-14
•
Granted: 1995-07-11
•
Expires: 2013-05-14
Abstract
Abstract A dimensionally graded electroconductive and electromagnetically responsive composite material is produced by contacting a polyurethane open cell foam substrate with a solution of an oxidatively polymerizable compound, such as pyrrole, that is polymerized to form a thin electroconductive polymer coating on the foam's surfaces. The reaction, wherein the compound is oxidized and polymerized to form a conductive polymer occurs over time. By varying the amount of time the porous foam substrate is in contact with the reacting solution a graded amount of electroconductive polymer is deposited on the foam substrate. The electrical activity of the resultant electrically conducting polyurethane/polypyrrole composite foam is measured as a Free Field Transmission loss at the microwave frequency of 10 GHz and expressed in "-dB". The polyurethane/polypyrrole composite foam with dimensionally graded electrical conductivity/activity constitutes a new bulk absorber.
Inventors
- 👤 Urszula G. Wettermark
- 👤 Gregory H. Worrell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 07:27
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/36; C08J9/40; C08J9/405; H; H01; H01B; H01B1/00; H01B1/06; H01B1/12; H01B1/124; H01B1/127; C08J2375/00; C08J2375/04; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249961; Y10T428/249987
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
100 words
A three-dimensional electroconducting composite material that can be used as an electromagnetically responsive bulk absorber, the composite material comprising in combination: a porous polyurethane open cell foam substrate having opposite ends and a length, at least a portion of the substrate having a thickness of at least one inch; and a coating of electroconductive polymer formed by chemical polymerization throughout the substrate, the amount of polymer coated on the substrate increasing along the length of the substrate from one end of the substrate to the other so that a dimensional conductivity gradient is formed along the length of the substrate.
Claim 2
Dependent Claim
100 words
A three-dimensional electroconducting composite material that can be used as an electromagnetically responsive bulk absorber, the composite material comprising in combination: a porous polyurethane open cell foam substrate having opposite ends and a length, at least a portion of the substrate having a thickness of at least one inch; and a coating of electroconductive polymer formed by chemical polymerization throughout the substrate, the amount of polymer coated on the substrate increasing along the length of the substrate from one end of the substrate to the other so that a dimensional conductivity gradient is formed along the length of the substrate.
Claim 3
Dependent Claim
25 words
The composite material of claim 1, wherein: the polyurethane foam substrate has a pore size in the range of 30 to 60 pores per inch.
Claim 4
Dependent Claim
12 words
The composite material of claim 1, wherein: the electroconductive polymer is polypyrrole.
Claim 5
Dependent Claim
84 words
The composite material of claim 1, wherein: the coating of electroconductive polymer is formed in a chemical reaction by preparing a solution of a polymerizable monomer that can be polymerized to form the electroconductive polymer, contacting at least a portion of the substrate in the solution of polymerizable monomer, initiating the polymerization reaction of the polymerizable monomer so that the electroconductive polymer is deposited on the substrate over time, and then varying the contact time of the substrate with the solution of polymerizable monomer.
Claim 6
Dependent Claim
12 words
The composite material of claim 4, wherein: the polymerizable monomer is pyrrole.
Claim 7
Dependent Claim
20 words
The composite material of claim 4, wherein: the polymerizable monomer is oxidatively polymerized by adding an oxidant to the solution.
Claim 8
Dependent Claim
16 words
The composite material of claim 6, wherein: the oxidant is provided by a ferric chloride salt.
Claim 9
Dependent Claim
13 words
The composite material of claim 4, wherein: the solution is an aqueous solution.
Claim 10
Dependent Claim
19 words
The composite material of claim 4, wherein: a stabilizing dopant is added to the solution for stabilizing the polymer.
Claim 11
Dependent Claim
18 words
The composite material of claim 9, wherein: the stabilizing dopant is supplied by a p-toluene sulfonate sodium salt.
Claim 12
Dependent Claim
163 words
A three-dimensional electroconductive composite material that can be used as an electromagnetically responsive bulk absorber, the composite material comprising in combination: a porous polyurethane open cell foam substrate having opposite ends and a length, at least a portion of the substrate having a thickness of at least one inch; a coating of electroconductive polypyrrole throughout the substrate, the amount of polypyrrole coated on the substrate increasing along the length of the substrate from one end to the other so that a dimensional conductivity gradient is formed along the length of the substrate, the coating being formed in a chemical reaction by preparing a solution of pyrrole that can be oxidatively polymerized to form the electroconductive polypyrrole, contacting at least a portion of the substrate in the solution of pyrrole monomer, initiating the polymerization reaction of the pyrrole so that the electroconductive polypyrrole is deposited on the substrate over time, and then varying the contact time of the substrate with the solution of pyrrole.
Claim 13
Dependent Claim
163 words
A three-dimensional electroconductive composite material that can be used as an electromagnetically responsive bulk absorber, the composite material comprising in combination: a porous polyurethane open cell foam substrate having opposite ends and a length, at least a portion of the substrate having a thickness of at least one inch; a coating of electroconductive polypyrrole throughout the substrate, the amount of polypyrrole coated on the substrate increasing along the length of the substrate from one end to the other so that a dimensional conductivity gradient is formed along the length of the substrate, the coating being formed in a chemical reaction by preparing a solution of pyrrole that can be oxidatively polymerized to form the electroconductive polypyrrole, contacting at least a portion of the substrate in the solution of pyrrole monomer, initiating the polymerization reaction of the pyrrole so that the electroconductive polypyrrole is deposited on the substrate over time, and then varying the contact time of the substrate with the solution of pyrrole.
Claim 14
Dependent Claim
25 words
The composite material of claim 11, wherein: the polyurethane foam substrate has a pore size in the range of 30 to 60 pores per inch.
Claim 15
Dependent Claim
22 words
The composite material of claim 11, wherein: the pyrrole is oxidatively polymerized by adding an oxidant provided by a ferric chloride salt.
Claim 16
Dependent Claim
28 words
The composite material of claim 11, wherein: the contact time is varied by immersing the substrate into the solution; and then gradually removing the substrate from the solution.
Claim 17
Dependent Claim
28 words
The composite material of claim 11, wherein: the contact time is varied by immersing the substrate into the solution; and then incrementally removing the substrate from the solution.
Claim 18
Dependent Claim
19 words
The composite material of claim 11, wherein: a stabilizing dopant is added to the solution to stabilize the polypyrrole.
Claim 19
Dependent Claim
18 words
The composite material of claim 16, wherein: the stabilizing dopant is supplied by a p-toluene sulfonate sodium salt.
Claim 20
Dependent Claim
106 words
A composite cone used as an electromagnetically responsive bulk absorber in an anechoic chamber, the composite cone comprising in combination: a porous polyurethane open cell foam substrate having a pyramidical shape, the top of the substrate forming a peak and the bottom forming a base, the substrate having a longitudinal axis that extends from the top to the bottom; and a coating of electroconductive polymer formed by chemical polymerization throughout the substrate, the amount of polymer coated on the substrate increasing along the longitudinal axis of the substrate so that a dimensional conductivity gradient is formed by the coating along the longitudinal axis of the substrate.
Claim 21
Dependent Claim
106 words
A composite cone used as an electromagnetically responsive bulk absorber in an anechoic chamber, the composite cone comprising in combination: a porous polyurethane open cell foam substrate having a pyramidical shape, the top of the substrate forming a peak and the bottom forming a base, the substrate having a longitudinal axis that extends from the top to the bottom; and a coating of electroconductive polymer formed by chemical polymerization throughout the substrate, the amount of polymer coated on the substrate increasing along the longitudinal axis of the substrate so that a dimensional conductivity gradient is formed by the coating along the longitudinal axis of the substrate.
Claim 22
Dependent Claim
43 words
The composite cone of claim 18, wherein: the amount of polymer coated on the substrate increases along the longitudinal axis from the top of the substrate to the bottom so that the top of the substrate has a lower conductivity than the bottom.
Claim 23
Dependent Claim
12 words
The composite cone of claim 18, wherein: the electroconductive polymer is polypyrrole.
Claim 24
Dependent Claim
87 words
The composite cone of claim 18, wherein: the coating of electroconductive polymer is formed in a chemical reaction by preparing a solution of a polymerizable monomer that can be polymerized to form the electroconductive polymer, contacting at least a portion of the substrate in the solution of polymerizable monomer, initiating the polymerization reaction of the polymerizable monomer so that the electroconductive polymer is deposited on the surfaces of the substrate over time, and then varying the contact time of the substrate with the solution of polymerizable monomer.
Claim 25
Dependent Claim
12 words
The composite cone of claim 21, wherein: the polymerizable monomer is pyrrole.
Claim 26
Dependent Claim
20 words
The composite cone of claim 21, wherein: the polymerizable monomer is oxidatively polymerized by adding an oxidant to the solution.
Claim 27
Dependent Claim
47 words
The composite cone of claim 21, wherein: the contact time is varied by immersing the substrate into the solution; and then gradually removing the substrate from the solution so that the top of the substrate is removed first and the bottom of the substrate is removed last.
Claim 28
Dependent Claim
46 words
The composite cone of claim 21, wherein: the contact time is varied by immersing the substrate into the solution; and then incrementally removing the substrate from the solution so that the top of the substrate is removed first and bottom of the substrate is removed last.
References Cited (Backward Citations)
US5063384A
Cited
US3574295A
Cited
US4287243A
Cited
US4468291A
Cited
US4547270A
Cited
US4707527A
Cited
US4696835A
Cited
US4710401A
Cited
US4617228A
Cited
US4604427A
Cited
US4557807A
Cited
US4636430A
Cited
US4617353A
Cited
US4764422A
Cited
US4798686A
Cited
US4803096A
Cited
US4877646A
Cited
US5162135A
Cited
US5063125A
Cited
US5066424A
Cited
US5132490A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-07-10 | 1999-01-09 | 1999-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-07-10 | 2003-01-09 | 2003-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-07-10 | 2007-01-09 | 2007-07-11 | $7700.00 | Window Closed / Lapsed |