US5430573A
Expired / Lapsed
US
⏱️ 0.0 years remaining
UV-absorbing, polarizing glass article
Assignee: Corning Inc
•
Filing: 1993-12-15
•
Granted: 1995-07-04
•
Expires: 2013-12-15
Abstract
Abstract A UV-absorbing, polarizing glass article and method of making, the glass having an R 2 O-B 2 O 3 -SiO 2 base glass composition, a sharp spectral cut-off at about 400 nm, a precipitated crystal phase consisting of a halide selected from the group composed of cuprous, cadmium and mixed cuprous-cadmium halides, the crystallites in the crystal phase being elongated, and a portion of the crystallites near the surface of the article being at least partially reduced to colloidal copper, whereby the article exhibits permanent dichroic behavior.
Inventors
- 👤 Roger J. Araujo
- 👤 Nicholas F. Borrelli
- 👤 Josef C. Lapp
- 👤 David W. Morgan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:28
CPC Classifications
C; C03; C03B; C03B23/00; C03B23/02; C03B23/023; C03B23/03; C03B23/025; C03B23/0256; C03C; C03C14/00; C03C14/006; C03C23/00; C03C23/007; C03C3/00; C03C3/04; C03C3/076; C03C3/089; C03C3/091; C03C3/11; C03C4/00; C03C4/04; C03C4/06; C03C4/065; C03C4/08; C03C4/085; G; G02; G02B; G02B5/00; G02B5/20; G02B5/22; G02B5/23; G02B5/30; G02B5/3025; Y; Y10; Y10S; Y10S501/00; Y10S501/90; Y10S501/905
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
84 words
A UV-absorbing, polarizing glass article, the glass having an R 2 O-B 2 O 3 -SiO 2 base glass composition, a sharp spectral cut-off at about 400 nm, a precipitated crystal phase consisting of halide crystallites selected from the group composed of cuprous, cadmium and mixed cuprous-cadmium halide crystallites, the crystallites in the crystal phase being elongated, and a portion of the crystallites near the surface of the article being at least partially reduced to colloidal copper, whereby the article exhibits permanent dichroic behavior.
Claim 2
Dependent Claim
84 words
A UV-absorbing, polarizing glass article, the glass having an R 2 O-B 2 O 3 -SiO 2 base glass composition, a sharp spectral cut-off at about 400 nm, a precipitated crystal phase consisting of halide crystallites selected from the group composed of cuprous, cadmium and mixed cuprous-cadmium halide crystallites, the crystallites in the crystal phase being elongated, and a portion of the crystallites near the surface of the article being at least partially reduced to colloidal copper, whereby the article exhibits permanent dichroic behavior.
Claim 3
Dependent Claim
32 words
An article in accordance with claim 1 wherein the glass composition includes 0.2-2.0 weight percent copper calculated as Cu 2 O and 0.25-2.0% of a halogen selected from bromine, chlorine and mixtures.
Claim 4
Dependent Claim
110 words
An article in accordance with claim 1 wherein the glass composition consists essentially of, as calculated from the glass batch in weight percent on an oxide and halogen basis; 40-80% SiO 2 , 4-35% B 2 O 3 , 0-26% Al 2 O 3 , 0-8% Li 2 O, 0-15% Na 2 O, 0-20% K 2 O the total Li 2 O+Na 2 O+K 2 O being 2-20%, 0-10% Cao+BaO+SrO, 0.2-2% Cu 2 O, 0-2% CdO, 0-12% ZrO 2 , 0-2.5% SnO 2 , 0-2% As 2 O 3 +Sb 2 O 3 , 0-2 Cl, 0-2% Br, 0.25-2.0% Cl+Br, 0-2% F, with an R-value in the range of 0.15-0.45.
Claim 5
Dependent Claim
14 words
An article in accordance with claim 1 wherein the glass is a non-photochromic glass.
Claim 6
Dependent Claim
108 words
A non-photochromic glass article in accordance with claim 4 wherein the glass composition consists essentially of, as calculated from the glass batch in weight percent on an oxide and halogen basis, 48-80% SiO 2 , 10-35% B 2 O 3 , 0-12% Al 2 O 3 , 0-4% Li 2 O, 0-14% Na 2 O, 0-12% K 2 O, 4-15% Li 2 O+Na 2 O+K 2 O, 0-10% CaO+BaO+SrO, 0.2-1.6% Cu 2 O, 0-2% CdO, 0-12% ZrO 2 , 0-2.5% SnO 2 , 0-2% As 2 O 3 +Sb 2 O 3 , 0-1.75 Cl, 0-1% Br, 0.25-2.0% Cl+Br, 0-2% F, with an R-value in the range 0.15-0.45.
Claim 7
Dependent Claim
14 words
An article in accordance with claim 1 wherein the glass is a photochromic glass.
Claim 8
Dependent Claim
67 words
A photochromic glass article in accordance with claim 6 wherein the glass composition consists essentially of, as calculated from the glass batch in weight percent on an oxide and halogen basis, 40-75% SiO 2 , 4-26% B 2 O 3 , 4-26% Al 2 O 3 , 2-8% Li 2 O, 4-15% Na 2 O, 6-20% K 2 O, 0.3-2% Cu 2 O, 0-2% Cl+Br, 0-2% F.
Claim 9
Independent Claim
116 words
A method of producing a UV-absorbing, polarizing glass article which comprises the steps of melting a batch for a R 2 O-B 2 O 3 -SiO 2 base glass containing at least 0.2% by weight Cu 2 O together with a sufficient amount of at least one halogen selected from chlorine and bromine to react with at least 0.2% copper, precipitating cuprous halide crystallites in the glass, subjecting the glass to a stress in one direction to elongate the glass and the cuprous halide crystallites therein, and then exposing the glass to a reducing atmosphere to reduce at least a portion of the copper halide crystallites in a thin layer near the surface of the glass.
Claim 10
Independent Claim
116 words
A method of producing a UV-absorbing, polarizing glass article which comprises the steps of melting a batch for a R 2 O-B 2 O 3 -SiO 2 base glass containing at least 0.2% by weight Cu 2 O together with a sufficient amount of at least one halogen selected from chlorine and bromine to react with at least 0.2% copper, precipitating cuprous halide crystallites in the glass, subjecting the glass to a stress in one direction to elongate the glass and the cuprous halide crystallites therein, and then exposing the glass to a reducing atmosphere to reduce at least a portion of the copper halide crystallites in a thin layer near the surface of the glass.
Claim 11
Dependent Claim
29 words
A method in accordance with claim 8 which further comprises cooling the molten glass while avoiding crystallite formation, and thereafter reheating the glass to thermally precipitate cuprous halide crystallites.
Claim 12
Dependent Claim
21 words
A method in accordance with claim 9 wherein the glass is reheated to a temperature in the range of 500°-900° C.
Claim 13
Dependent Claim
25 words
A method in accordance with claim 8 wherein the glass is exposed to a reducing atmosphere at a temperature of at least about 400° C.
Claim 14
Dependent Claim
13 words
A method in accordance with claim 8 wherein the reducing atmosphere is hydrogen.
References Cited (Backward Citations)
US3325299A
Cited
US3540793A
Cited
US3653863A
Cited
US3954485A
Cited
US4304584A
Cited
US4339256A
Cited
US4479819A
Cited
US4792535A
Cited
US5045509A
Cited
JPH04279337A
Cited
US5281562A
Cited
US5322819A
Cited
US5275979A
Cited
US5300465A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-07-03 | 1999-01-02 | 1999-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-07-03 | 2003-01-02 | 2003-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-07-03 | 2007-01-02 | 2007-07-04 | $7700.00 | Window Closed / Lapsed |