Assignee: Individual
•
Filing: 1980-12-19
•
Granted: 1982-07-13
•
Expires: 2000-12-19
Abstract
Abstract Polarized ophthalmic glass lenses are made from conventional ophthalmic glass. This is accomplished by heating a sheet of ophthalmic glass, which includes a reducible metal oxide as part of its composition, to its softening point in a reducing atmosphere for a time interval sufficient to reduce the metal oxide to metal to a predetermined depth on at least one surface of the sheet. Following this reduction of the metal oxide, the sheet is held at an elevated temperature to permit the reduced oxides to nucleate. Then, the sheet is stretched in one direction to elongate the nucleated metal particles in parallel lines. The glass then is shaped, cut into lenses, permitted to cool, and the outer surface of the lens blanks are ground and polished in a conventional manner, leaving the stretched elongated metal particles on the inner surface thereof to create polarized ophthalmic lenses.
Inventors
- 👤 Robert A. Simms
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:43
CPC Classifications
C; C03; C03C; C03C4/00; C03C4/04; C03C4/06; C03C23/00
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
97 words
A method of making polarized ophthalmic glass, comprising the steps of: heating a sheet of ophthalmic glass, including a reducible metal oxide as a part of its composition, to its softening point in a reducing atmosphere for a predetermined period of time sufficient to reduce said metal oxide to metal particles to a predetermined depth less than the thickness of said sheet on at least one surface of said sheet; stretching said sheet in one direction to elongate said metal particles in parallel lines; and cooling the glass to set the elongated metal particles in the glass.
Claim 2
Independent Claim
97 words
A method of making polarized ophthalmic glass, comprising the steps of: heating a sheet of ophthalmic glass, including a reducible metal oxide as a part of its composition, to its softening point in a reducing atmosphere for a predetermined period of time sufficient to reduce said metal oxide to metal particles to a predetermined depth less than the thickness of said sheet on at least one surface of said sheet; stretching said sheet in one direction to elongate said metal particles in parallel lines; and cooling the glass to set the elongated metal particles in the glass.
Claim 3
Dependent Claim
15 words
The method according to claim 1 wherein the reducing atmosphere consists of a hydrogen/nitrogen atmosphere.
Claim 4
Dependent Claim
42 words
The method according to claim 2 wherein the temperature to which the glass sheet is heated is three hundred degrees Centigrade (300° C.) to six hundred degrees Centigrade (600° C.) and the predetermined period of time is at least ten (10) minutes.
Claim 5
Dependent Claim
56 words
The method according to claim 1 further including the steps of removing the reducing atmosphere following the heating of said sheet of glass therein for said predetermined period of time and holding said sheet of glass in a nonreducing atmosphere at its softening temperature for a second predetermined period of time prior to stretching said sheet.
Claim 6
Dependent Claim
18 words
The method according to claim 4 wherein said second predetermined period of time is substantially two (2) hours.
Claim 7
Dependent Claim
29 words
The method according to claim 1 further including the step of shaping the glass to a predetermined curvature following stretching of said sheet and prior to cooling the glass.
Claim 8
Dependent Claim
24 words
The method according to claim 6 wherein said sheet is stretched to elongate it from ten (10) to thirty (30) times its original length.
Claim 9
Dependent Claim
24 words
The method according to claim 1 wherein said sheet is stretched to elongate it from ten (10) to thirty (30) times its original length.
Claim 10
Independent Claim
139 words
A method of making polarized ophthalmic lenses, comprising the steps of: heating a sheet of ophthalmic glass, including a reducible metal oxide as a part of its composition, to its softening point in a reducing atmosphere for a predetermined period of time sufficient to reduce said metal oxide to metal particles to a predetermined depth on at least one surface of said sheet; stretching said sheet in one direction to elongate said metal particles in parallel lines; placing the stretched glass sheet over a shaping fixture while said glass sheet is at the softening temperature and permitting said sheet to conform to the curvature of said shaping fixture; cutting individual lenses from the glass after shaping on said shaping fixture; and cooling the glass to set the elongated metal particles in the glass of the individual lenses thus formed.
Claim 11
Independent Claim
139 words
A method of making polarized ophthalmic lenses, comprising the steps of: heating a sheet of ophthalmic glass, including a reducible metal oxide as a part of its composition, to its softening point in a reducing atmosphere for a predetermined period of time sufficient to reduce said metal oxide to metal particles to a predetermined depth on at least one surface of said sheet; stretching said sheet in one direction to elongate said metal particles in parallel lines; placing the stretched glass sheet over a shaping fixture while said glass sheet is at the softening temperature and permitting said sheet to conform to the curvature of said shaping fixture; cutting individual lenses from the glass after shaping on said shaping fixture; and cooling the glass to set the elongated metal particles in the glass of the individual lenses thus formed.
Claim 12
Dependent Claim
47 words
The method according to claim 9 wherein said at least one surface comprises the inner surface of each of the lenses thus formed and further including the step of grinding and polishing the outer surfaces of such lenses to particular prescriptions following the cooling of the glass.
Claim 13
Dependent Claim
28 words
The method according to claim 9 wherein the reducing atmosphere comprises a hydrogen/nitrogen reducing atmosphere, and wherein said predetermined period of time is at least ten (10) minutes.
Claim 14
Dependent Claim
40 words
The method according to claim 9 wherein the step of stretching said sheet takes place after said predetermined period of time and said sheet is stretched from ten (10) to thirty (30) times its original dimension in said one direction.
Claim 15
Dependent Claim
51 words
The method according to claim 9 further including the step of removing the reducing atmosphere after said predetermined period of time and holding said sheet of glass at said softening temperature for a second predetermined period of time to nucleate the reduced metal oxides prior to stretching said sheet of glass.
Claim 16
Dependent Claim
61 words
The method according to claim 9 wherein the glass is heated to a temperature ranging from three hundred degrees Centigrade (300° C.) to six hundred degrees Centigrade (600° C.) to soften the glass, and wherein said predetermined time is sufficient further to allow the reduced metal oxide to nucleate and wherein said stretching of said sheet takes place following such nucleation.
Claim 17
Dependent Claim
28 words
The method according to claim 14 wherein the reducing atmosphere comprises a hydrogen/nitrogen reducing temperature, and wherein said predetermined period of time is at least ten (10) minutes.
Claim 18
Dependent Claim
40 words
The method according to claim 15 wherein the step of stretching said sheet takes place after said predetermined period of time and said sheet is stretched from ten (10) to thirty (30) times its original dimension in said one direction.
Claim 19
Dependent Claim
47 words
The method according to claim 16 wherein said at least one surface comprises the inner surface of each of the lenses thus formed and further including the step of grinding and polishing the outer surfaces of such lenses to particular prescriptions following the cooling of the glass.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-12 | 1986-01-11 | 1986-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-12 | 1990-01-11 | 1990-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-12 | 1994-01-11 | 1994-07-13 | $7700.00 | Window Closed / Lapsed |