Method for manufacturing porous semiconductor light emitting device
Assignee: Fujitsu Semiconductor Ltd
•
Filing: 1994-01-06
•
Granted: 1995-06-27
•
Expires: 2014-01-06
Abstract
Abstract An Si or SiC semiconductor layer is subjected to anodic oxidation in an HF solution to form a porous semiconductor layer. Without drying, the porous semiconductor layer is then immersed in pure water. Ultrasonic waves applied to the pure water shorten the reaction time and help bubbles separate from the surface of the porous region. The porous semiconductor layer is used for forming a pn junction, and carriers are injected into the pn junction.
Inventors
- 👤 Masao Yamada
- 👤 Motoo Nakano
- 👤 George J. Collins
- 👤 Tetsuro Tamura
- 👤 Akira Takazawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:36
CPC Classifications
H; H10; H10H; H10H20/00; H10H20/80; H10H20/81; H10H20/822; H10H20/826; H10H20/8264; B; B82; B82Y; B82Y10/00; H10D; H10D62/00; H10D62/80; H10D62/83; H10D62/832; H10D62/8325; H10P; H10P50/00; Y; Y10; Y10S; Y10S438/00; Y10S438/911; Y10S438/96; Y10S438/962
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
128 words
A method of manufacturing an Si light emitting device comprising the steps of: providing an Si layer having a first conductivity type; forming a metal electrode on a surface of said Si layer; performing an anodic oxidation by immersing said Si layer in an aqueous solution of hydrofluoric acid and forming a porous region containing a cluster of Si quantum wires on said surface of said Si layer; forming an oxidized layer by oxidizing an exposed surface of said Si layer in an oxidizing atmosphere; depositing a highly doped Si or SiC layer having a second conductivity type opposite to the first conductivity type of said Si layer on the oxidized layer above said porous region; and depositing a transparent conductive film on said Si or SiC layer.
Claim 2
Independent Claim
128 words
A method of manufacturing an Si light emitting device comprising the steps of: providing an Si layer having a first conductivity type; forming a metal electrode on a surface of said Si layer; performing an anodic oxidation by immersing said Si layer in an aqueous solution of hydrofluoric acid and forming a porous region containing a cluster of Si quantum wires on said surface of said Si layer; forming an oxidized layer by oxidizing an exposed surface of said Si layer in an oxidizing atmosphere; depositing a highly doped Si or SiC layer having a second conductivity type opposite to the first conductivity type of said Si layer on the oxidized layer above said porous region; and depositing a transparent conductive film on said Si or SiC layer.
Claim 3
Independent Claim
93 words
A method of manufacturing an Si light emitting device comprising the steps of: providing an Si layer; forming a metal electrode on a surface of said Si layer; performing an anodic oxidation by immersing said Si layer in an aqueous solution of hydrofluoric acid and forming a porous region containing a cluster of Si quantum wires on said surface of said Si layer; rinsing said porous layer with pure water to increase the transition energy of said porous region for recombination light emission; and forming a carrier supply layer on said porous region.
Claim 4
Independent Claim
93 words
A method of manufacturing an Si light emitting device comprising the steps of: providing an Si layer; forming a metal electrode on a surface of said Si layer; performing an anodic oxidation by immersing said Si layer in an aqueous solution of hydrofluoric acid and forming a porous region containing a cluster of Si quantum wires on said surface of said Si layer; rinsing said porous layer with pure water to increase the transition energy of said porous region for recombination light emission; and forming a carrier supply layer on said porous region.
Claim 5
Dependent Claim
47 words
A method according to claim 2, wherein said carrier supply layer is a highly doped Si or SiC layer having a conductivity type opposite to the conductivity type of said Si layer, and said method includes depositing a transparent conductive film on said Si or SiC layer.
Claim 6
Dependent Claim
25 words
A method according to claim 2, wherein said carrier supply layer includes a transparent conductive film, said film being formed directly on said porous region.
Claim 7
Dependent Claim
38 words
A method accordingly to claim 2, wherein said hydrofluoric acid aqueous solution contains 10 to 50 weight % hydrofluoric acid, and said anodic oxidation step is performed at a current density of 10 to 100 mA/cm 2 .
Claim 8
Dependent Claim
22 words
A method according to claim 2, wherein said Si layer is formed by depositing a polycrystalline Si layer on a support substrate.
Claim 9
Dependent Claim
27 words
A method according to claim 2, wherein said rinsing step is performed by immersing the porous layer in pure water while applying ultrasonic waves to said water.
Claim 10
Independent Claim
69 words
A method of manufacturing a porous semiconductor device comprising the steps of: performing an anodic oxidation of an Si or SiC semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer; performing an anodic oxidation of an Si or SiC semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer; and immersing said porous semiconductor layer in pure water.
Claim 11
Independent Claim
69 words
A method of manufacturing a porous semiconductor device comprising the steps of: performing an anodic oxidation of an Si or SiC semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer; performing an anodic oxidation of an Si or SiC semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer; and immersing said porous semiconductor layer in pure water.
Claim 12
Dependent Claim
21 words
A method according to claim 8, wherein said pure water immersion step is performed while applying ultrasonic waves to the water.
Claim 13
Dependent Claim
25 words
A method according to claim 8, wherein said pure water immersion step includes a step of immersing said porous semiconductor layer in heated pure water.
Claim 14
Independent Claim
48 words
A method of manufacturing a porous semiconductor light emitting device comprising the steps of: performing an anodic oxidation of an Si or SiC semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer; and annealing said porous semiconductor in a vapor containing atmosphere.
Claim 15
Independent Claim
48 words
A method of manufacturing a porous semiconductor light emitting device comprising the steps of: performing an anodic oxidation of an Si or SiC semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer; and annealing said porous semiconductor in a vapor containing atmosphere.
Claim 16
Independent Claim
49 words
A method of manufacturing a porous semiconductor light emitting device comprising the steps of: performing an anodic oxidation of an Si or SiC semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer; and exposing said porous semiconductor layer to a fluorine gas atmosphere.
Claim 17
Independent Claim
49 words
A method of manufacturing a porous semiconductor light emitting device comprising the steps of: performing an anodic oxidation of an Si or SiC semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer; and exposing said porous semiconductor layer to a fluorine gas atmosphere.
Claim 18
Independent Claim
50 words
A method of manufacturing a porous semiconductor light emitting device comprising the steps of: irradiating reactive ions on the surface of an Si or SiC semiconductor layer; and performing an anodic oxidation of said semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer thereon.
Claim 19
Independent Claim
50 words
A method of manufacturing a porous semiconductor light emitting device comprising the steps of: irradiating reactive ions on the surface of an Si or SiC semiconductor layer; and performing an anodic oxidation of said semiconductor layer in an aqueous solution of hydrofluoric acid to form a porous semiconductor layer thereon.
Claim 20
Dependent Claim
22 words
A method according to claim 13, wherein said reactive ions are ions generated from a CF 4 or Cl 3 plasma gas.
Claim 21
Dependent Claim
25 words
A method according to claim 14, further comprising a step of injecting p-type impurity ions into said semiconductor layer prior to said anodic oxidation step.
Claim 22
Dependent Claim
24 words
A method according to claim 15, further comprising a step of injecting p-type impurity ions into said semiconductor layer after said anodic oxidation step.
Claim 23
Independent Claim
99 words
A method of manufacturing an Si light emitting device comprising the steps of: preparing an SOI substrate having a laminated structure comprising an Si layer, an insulating layer, and a support substrate; forming an opening in said support substrate and said insulating layer; forming a back contact electrode on a bottom surface of said support substrate covering said opening; performing an anodic oxidation of said Si layer in an aqueous solution of hydrofluoric acid to form a porous Si region thereon; and forming an n-type region and a p-type region in said Si layer sandwiching said porous Si region.
Claim 24
Independent Claim
99 words
A method of manufacturing an Si light emitting device comprising the steps of: preparing an SOI substrate having a laminated structure comprising an Si layer, an insulating layer, and a support substrate; forming an opening in said support substrate and said insulating layer; forming a back contact electrode on a bottom surface of said support substrate covering said opening; performing an anodic oxidation of said Si layer in an aqueous solution of hydrofluoric acid to form a porous Si region thereon; and forming an n-type region and a p-type region in said Si layer sandwiching said porous Si region.
Claim 25
Dependent Claim
47 words
A method according to claim 17, further comprising the steps of: forming an Si oxidized film on said Si layer by thermally oxidizing the surface of said Si layer after said anodic oxidation step; and depositing Si on said Si oxidized film by low pressure vapor deposition.
Claim 26
Dependent Claim
64 words
A method according to claim 18, wherein said back contact electrode is formed of a metal which is resistant to said hydrofluoric acid aqueous solution, said anodic oxidation step being performed by immersing said SOI substrate in said hydrofluoric acid aqueous solution, said method further comprising a step of removing said back contact electrode after said Si depositing step through low pressure vapor deposition.
Claim 27
Dependent Claim
53 words
A method according to claim 18, wherein said back contact electrode is formed of an oxidizable metal, said anodic oxidation step being performed without immersing said back contact electrode in said hydrofluoric acid aqueous solution, said method further comprising a step of oxidizing and changing said back contact electrode to an insulating layer.
Claim 28
Independent Claim
50 words
A method of manufacturing an Si light emitting device comprising the steps of: forming a porous Si region of quantum wires in a p-type Si layer; and depositing an n-type conductive polymer layer on said porous Si region using an electrochemical film forming method or a vapor film forming method.
Claim 29
Independent Claim
50 words
A method of manufacturing an Si light emitting device comprising the steps of: forming a porous Si region of quantum wires in a p-type Si layer; and depositing an n-type conductive polymer layer on said porous Si region using an electrochemical film forming method or a vapor film forming method.
Claim 30
Dependent Claim
76 words
A method according to claim 21, wherein said p-type Si layer is a polycrystalline Si layer, and said porous Si region forming step includes a step of forming a quantum wire Si region by anodic oxidation of said polycrystalline Si layer in an aqueous solution of hydrofluoric acid, said quantum wire Si region being formed so as to present a number of pores contiguous to each other on the surface layer of said polycrystalline Si layer.
Claim 31
Independent Claim
79 words
A method of manufacturing a semiconductor light emitting device comprising the steps of: growing a p-type SiC layer on a p-type Si single crystal substrate; forming a quantum wire cluster in a surface region of said p-type SiC layer by anodic oxidation of said p-type SiC layer in an aqueous solution of hydrofluoric acid or alcohol diluted hydrofluoric acid; and depositing an n-type SiC layer of a transparent conductive layer on said quantum wire cluster in a vapor phase.
Claim 32
Independent Claim
79 words
A method of manufacturing a semiconductor light emitting device comprising the steps of: growing a p-type SiC layer on a p-type Si single crystal substrate; forming a quantum wire cluster in a surface region of said p-type SiC layer by anodic oxidation of said p-type SiC layer in an aqueous solution of hydrofluoric acid or alcohol diluted hydrofluoric acid; and depositing an n-type SiC layer of a transparent conductive layer on said quantum wire cluster in a vapor phase.
Claim 33
Dependent Claim
25 words
A method according to claim 23, wherein ultraviolet rays are applied to the surface region of said p-type SiC layer during said anodic oxidation step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-06-26 | 1998-12-26 | 1999-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-06-26 | 2002-12-26 | 2003-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-06-26 | 2006-12-26 | 2007-06-27 | $7700.00 | Window Closed / Lapsed |