Assignee: Canon Inc
•
Filing: 1994-08-25
•
Granted: 1995-04-18
•
Expires: 2014-08-25
Abstract
Abstract A toner for developing an electrostatic image has toner particles. The toner particles are prepared by suspension polymerization and contain at least two components comprised of a high softening point resin-A and a low softening point material-B. The toner particles each have a structure separated into a phase-A mainly composed of the resin-A and a phase-B mainly composed of the material-B. The phase-B is absent in the vicinity of the toner particle surface, ranging from its surface to a depth 0.15 time a toner particle diameter. The toner particles contain an organic solvent, a polymerizable monomer or a mixture thereof in a quantity of not more than 1,000 ppm.
Inventors
- 👤 Makoto Kanbayashi
- 👤 Takayuki Nagatsuka
- 👤 Takashige Kasuya
- 👤 Tatsuya Nakamura
- 👤 Tatsuhiko Chiba
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:59
CPC Classifications
G; G03; G03G; G03G9/00; G03G9/08; G03G9/0827; G03G9/0802; G03G9/0804; G03G9/0806; G03G9/0819; G03G9/0825; G03G9/087; G03G9/08784; G03G9/08791; G03G9/08795; G03G9/08797; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2989
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
126 words
A toner for developing an electrostatic image comprising toner particles; said toner particles being prepared by polymerization of a monomer component containing at least a polymerizable monomer and a polar resin in an aqueous medium; containing at least two components comprised of a high softening point resin-A and a low softening point material-B; each having a structure separated into a phase-A mainly composed of said resin-A and a phase-B mainly composed of said material-B, said phase-B being absent from the vicinity of the toner particle surface, said vicinity ranging from the toner particle surface to a depth 0.15 time a toner particle diameter; and wherein an organic solvent, said polymerizable monomer or a mixture thereof is present in a quantity of not more than 1,000 ppm.
Claim 2
Dependent Claim
126 words
A toner for developing an electrostatic image comprising toner particles; said toner particles being prepared by polymerization of a monomer component containing at least a polymerizable monomer and a polar resin in an aqueous medium; containing at least two components comprised of a high softening point resin-A and a low softening point material-B; each having a structure separated into a phase-A mainly composed of said resin-A and a phase-B mainly composed of said material-B, said phase-B being absent from the vicinity of the toner particle surface, said vicinity ranging from the toner particle surface to a depth 0.15 time a toner particle diameter; and wherein an organic solvent, said polymerizable monomer or a mixture thereof is present in a quantity of not more than 1,000 ppm.
Claim 3
Dependent Claim
22 words
The toner according to claim 1, wherein said high softening point resin-A has a weight average molecular weight from 5,000 to 200,000.
Claim 4
Dependent Claim
22 words
The toner according to claim 1, wherein said high softening point resin-A has a flow-out point from 65° C. to 100° C.
Claim 5
Dependent Claim
42 words
The toner according to claim 1, wherein said high softening point resin-A comprises a polymer or copolymer obtained from a polymerizable monomer selected from the group consisting of a styrene monomer, an acrylate, a methacrylate, an acrylonitrile, a methacrylonitrile and an acrylamide.
Claim 6
Dependent Claim
22 words
The toner according to claim 1, wherein said low softening point material-B has a weight average molecular weight from 300 to 10,000.
Claim 7
Dependent Claim
22 words
The toner according to claim 1, wherein said low softening point material-B has a melting point from 30° C. to 130° C.
Claim 8
Dependent Claim
22 words
The toner according to claim 1, wherein said low softening point material-B has a melting point from 60° C. to 100° C.
Claim 9
Dependent Claim
31 words
The toner according to claim 1, wherein said high softening point resin-A and said low softening point material-B in said toner are in a component ratio A:B from 50:50 to 95:5.
Claim 10
Dependent Claim
31 words
The toner according to claim 2, wherein said high softening point resin-A and said low softening point material-B in said toner are in a component ratio A:B from 70:30 to 90:10.
Claim 11
Dependent Claim
87 words
The toner according to claim 1, wherein with respect to a projected area of a toner particle of said toner particles, a maximum inscribed circle corresponding to said toner particle radius r and a minimum circumscribed circle corresponding to said toner particle radius R satisfies the following relationship (1): 1.00<R/r≦1.20 (1) and said toner particles each have an uneven surface such that circumferential length L and circumference 1 of the inscribed circle of a projected area of the toner particle satisfies the following relationship (2): 1.01<L/l<2.00 (2)
Claim 12
Dependent Claim
18 words
The toner according to claim 1, wherein said polar resin comprises a cationic polymer or an anionic polymer.
Claim 13
Dependent Claim
28 words
The toner according to claim 1, wherein said polar resin has a ratio of weight average molecular weight to number average molecular weight Mw/Mn from 1.2 to 10.
Claim 14
Dependent Claim
28 words
The toner according to claim 1, wherein said polar resin has a ratio of weight average molecular weight to number average molecular weight Mw/Mn from 1.5 to 5.
Claim 15
Dependent Claim
20 words
The toner according to claim 1, wherein said polar resin has an acid value from 5 to 100 mg KOH/g.
Claim 16
Dependent Claim
20 words
The toner according to claim 1, wherein said polar resin has an acid value from 20 to 80 mg KOH/g.
Claim 17
Dependent Claim
22 words
The toner according to claim 1 wherein said toner particles have a weight average particle diameter from 2 μm to 20 μm.
Claim 18
Dependent Claim
22 words
The toner according to claim 1, wherein said toner particles have a weight average particle diameter from 3 μm to 12 μm.
Claim 19
Dependent Claim
29 words
The toner according to claim 1, wherein said toner contains an additive selected from the group consisting of a fluidity-providing agent, an abrasive, a lubricant and charge controlling particles.
Claim 20
Dependent Claim
30 words
The toner according to claim 18, wherein said additive has a weight average particle diameter of not more than 1/10 of the weight average particle diameter of the toner particles.
Claim 21
Dependent Claim
52 words
The toner according to claim 1, wherein said toner particles are obtained by subjecting a monomer composition containing (i) a polymerizable monomer that forms said high softening point resin-A; (ii) said low softening point material and (iii) said polar resin to suspension polymerization in an aqueous dispersion medium containing a dispersion stabilizer.
Claim 22
Dependent Claim
35 words
The toner according to claim 1, wherein said dispersion stabilizer contains an inorganic dispersant selected from the group consisting of a phosphoric acid polyvalent metal salt, a carbonate, an inorganic salt and an inorganic oxide.
Claim 23
Dependent Claim
38 words
The toner according to claim 20, wherein said dispersion stabilizer contains a surface active agent selected from the group consisting of sodium dodecylbenzenesulfate, sodium tetradecylsulfate, sodium pentadecylsulfate, sodium octylsulfate, sodium oleate, sodium laurate, sodium stearate and potassium stearate.
Claim 24
Dependent Claim
69 words
The toner according to claim 1, wherein said toner particles are obtained by polymerization comprising granulating and polymerizing a monomer composition containing (i) a polymerizable monomer that forms said high softening point resin-A and (ii) said low softening point material, in an aqueous dispersion medium and continuing the polymerization reaction until said organic solvent, polymerizable monomer or a mixture thereof is present in amounts not more than 1,000 ppm.
Claim 25
Dependent Claim
63 words
The toner according to claim 1, wherein said toner particles are obtained by polymerization comprising granulating and polymerizing a monomer composition containing (i) a polymerizable monomer that forms said high softening point resin-A and (ii) said low softening point material, in an aqueous dispersion medium and accelerating the consumption of polymerizable monomers at the moment the polymerization conversion has reached 95% or more.
Claim 26
Dependent Claim
42 words
The toner according to claim 24, wherein said toner particles are obtained by polymerization comprising accelerating the consumption of polymerizable monomers by raising polymerization temperature by 5° C. to 60° C. at the moment the polymerization conversion has reached 95% or more.
Claim 27
Dependent Claim
63 words
The toner according to claim 25, wherein said toner particles are obtained by polymerization using in combination a polymerization initiator capable of being decomposed at a first polymerization temperature by which the polymerization conversion has reached 95% or more and a polymerization initiator capable of being decomposed at a second polymerization temperature 5° C. to 60° C. higher than the first polymerization temperature.
Claim 28
Dependent Claim
53 words
The toner according to claim 24, wherein said toner particles are obtained by polymerization comprising accelerating the consumption of polymerizable monomers by using in combination a polymerization initiator having a long half-life period and a polymerizable initiator having a short half-life period at the moment the polymerization conversion has reached 95% or more.
Claim 29
Dependent Claim
45 words
The toner according to claim 24, wherein said toner particles are obtained by polymerization comprising accelerating the consumption of polymerizable monomers by using a polyfunctional polymerization initiator having a plurality of polymerization initiating points at the moment the polymerization conversion has reach 95% or more.
Claim 30
Dependent Claim
83 words
The toner according to claim 1, wherein said toner particles are obtained by subjecting toner particles obtained by polymerization comprising granulating and polymerizing a monomer composition containing (i) a polymerizable monomer that forms said high softening point resin and (ii) said low softening point material, in an aqueous dispersion medium to a treatment to remove from said toner particles the organic solvent, polymerizable monomers or a mixture thereof without transporting the phase-B low softening point material-B to the surfaces of the toner particles,
Claim 31
Dependent Claim
57 words
The toner according to claim 29, wherein said toner particles are obtained by carrying out a treatment to remove from the toner particles the organic solvent, polymerizable monomers or a mixture thereof after completion of the polymerization reaction or at the latter-half stage of the polymerization reaction in an aqueous medium under normal pressure or reduced pressure.
Claim 32
Dependent Claim
31 words
The toner according to claim 29, wherein said toner particles are obtained by subjecting the toner particles obtained by said polymerization, to deaeration at a low temperature and under reduced pressure.
References Cited (Backward Citations)
US2297691A
Cited
US3634251A
Cited
US3959153A
Cited
JPS5114895A
Cited
JPS5317737A
Cited
JPS5317736A
Cited
JPS5317735A
Cited
US4971879A
Cited
JPS6453786A
Cited
US5130220A
Cited
US5130219A
Cited
US5143812A
Cited
US5135833A
Cited
US5153092A
Cited
US5300386A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-04-17 | 1998-10-17 | 1999-04-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-04-17 | 2002-10-17 | 2003-04-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-04-17 | 2006-10-17 | 2007-04-18 | $7700.00 | Window Closed / Lapsed |