Method of forming a ferroelectric film
Assignee: Sharp Corp
•
Filing: 1993-07-01
•
Granted: 1995-03-14
•
Expires: 2013-07-01
Abstract
Abstract A method of forming a ferroelectric film on a heated support is provided which includes the steps of forming a first layer on the heated support by sputtering a material including lead at a first pressure; and forming a second layer on the first layer by sputtering the material at a second pressure, the second pressure being lower than the first pressure.
Inventors
- 👤 Kazuya Ishihara
- 👤 Shigeo Onishi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 12:56
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/0021; C23C14/0036; C23C14/06; C23C14/08; H; H10; H10P; H10P14/00; H10P14/40
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
82 words
A method of forming a ferroelectric film on a heated support comprising the steps of: forming a first layer on said heated support by sputtering a target of ferroelectric material including lead, the sputtering for forming the first layer being conducted at a first pressure; and forming a second layer on said first layer by sputtering said target of ferroelectric material, the sputtering for forming the second layer conducted at a second pressure, said second pressure being lower than said first pressure.
Claim 2
Independent Claim
82 words
A method of forming a ferroelectric film on a heated support comprising the steps of: forming a first layer on said heated support by sputtering a target of ferroelectric material including lead, the sputtering for forming the first layer being conducted at a first pressure; and forming a second layer on said first layer by sputtering said target of ferroelectric material, the sputtering for forming the second layer conducted at a second pressure, said second pressure being lower than said first pressure.
Claim 3
Dependent Claim
14 words
The method of claim 1, wherein said support is an electrode for a capacitor.
Claim 4
Dependent Claim
20 words
The method of claim 1, wherein said first layer and said second layer are substantially polycrystalline with a perovskite structure.
Claim 5
Dependent Claim
31 words
The method of claim 1, wherein said first pressure is in the range of 50 to 100 mTorr and said second pressure is in the range of 5 to 10 mTorr.
Claim 6
Dependent Claim
21 words
The method of claim 1, wherein said support is heated at a temperature in the range of 550° to 700° C.
Claim 7
Dependent Claim
14 words
The method of claim 1, wherein said ferroelectric material further includes zirconium and titanium.
Claim 8
Independent Claim
127 words
A method of forming a ferroelectric film on a heated support comprising the steps of: forming a first layer having a perovskite structure on said heated support by sputtering a ferroelectric material including lead, said sputtering for forming said first layer being conducted at a first pressure, said heated support being maintained at a temperature which is sufficiently high in order that said first layer has a perovskite structure; and forming a second layer on said first layer by sputtering said ferroelectric material, said sputtering for forming said second layer being conducted at a second pressure, said second pressure being lower than said first pressure, said heated support being maintained at a temperature which is sufficiently high in order that said second layer has a polycrystalline structure.
Claim 9
Independent Claim
127 words
A method of forming a ferroelectric film on a heated support comprising the steps of: forming a first layer having a perovskite structure on said heated support by sputtering a ferroelectric material including lead, said sputtering for forming said first layer being conducted at a first pressure, said heated support being maintained at a temperature which is sufficiently high in order that said first layer has a perovskite structure; and forming a second layer on said first layer by sputtering said ferroelectric material, said sputtering for forming said second layer being conducted at a second pressure, said second pressure being lower than said first pressure, said heated support being maintained at a temperature which is sufficiently high in order that said second layer has a polycrystalline structure.
Claim 10
Dependent Claim
31 words
The method of claim 7, wherein said first pressure is in the range of 50 to 100 mTorr and said second pressure is in the range of 5 to 10 mTorr.
Claim 11
Dependent Claim
33 words
The method of claim 8, wherein said support is maintained at a temperature in the range of 550° to 700° C. during the formation of both said first layer and said second layer.
Claim 12
Dependent Claim
54 words
The method of claim 7, wherein said sputtering for forming both said first layer and said second layer is conducted using an inert gas and an oxygen gas, and a flow ratio of said inert gas to said oxygen gas for forming said first layer is greater than that for forming said second layer.
Claim 13
Dependent Claim
25 words
The method of claim 10, wherein said flow ratio of said inert gas to said oxygen gas for forming said first layer is approximately 8:2.
Claim 14
Independent Claim
91 words
A method of forming a ferroelectric film on a heated support comprising the step of forming a ferroelectric film having a perovskite structure on said heated support by sputtering a ferroelectric material containing lead, said heated support being maintained at a temperature which is sufficiently high in order that said ferroelectric film has a perovskite structure, wherein said sputtering is initially conducted at a first pressure and subsequently conducted at a second pressure to increase a deposition rate of said ferroelectric film, the first pressure being greater than the second pressure.
Claim 15
Independent Claim
91 words
A method of forming a ferroelectric film on a heated support comprising the step of forming a ferroelectric film having a perovskite structure on said heated support by sputtering a ferroelectric material containing lead, said heated support being maintained at a temperature which is sufficiently high in order that said ferroelectric film has a perovskite structure, wherein said sputtering is initially conducted at a first pressure and subsequently conducted at a second pressure to increase a deposition rate of said ferroelectric film, the first pressure being greater than the second pressure.
Claim 16
Dependent Claim
31 words
The method of claim 12, wherein said first pressure is in the range of 50 to 100 mTorr and said second pressure is in the range of 5 to 10 mTorr.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-03-13 | 1998-09-12 | 1999-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-03-13 | 2002-09-12 | 2003-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-03-13 | 2006-09-12 | 2007-03-14 | $7700.00 | Window Closed / Lapsed |