Low temperature method for synthesizing diamond with high quality by vapor phase deposition
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1992-04-01
•
Granted: 1995-02-21
•
Expires: 2012-04-01
Abstract
Abstract A diamond film deposited on a substrate heated at less than 400 DEG C. in vapor phase from material gas including hydrogen gas and hydrocarbon gas often incurs low strength, low abrasion resistance, and opacity owing to high concentration of non-diamond ingredients. The inventors have discovered that inclusion of nitrogen gas in material gas is likely to raise the concentration of non-diamond ingredients. Good diamond film of good quality shall be obtained by synthesizing from the material gas in which the nitrogen concentration is less than 1000 ppm. The smaller the nitrogen concentration is suppressed, the higher the quality of diamond rises.
Inventors
- 👤 Takayuki Shibata
- 👤 Nobuhiro Ota
- 👤 Naoji Fujimori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:51
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/26; C23C16/27; C23C16/274; C23C16/278; C30; C30B; C30B25/00; C30B25/02; C30B25/10; C30B25/105; C30B29/00; C30B29/02; C30B29/04; Y; Y10; Y10S; Y10S427/00; Y10S427/103; Y10S427/106
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
103 words
A method for low temperature synthesis of diamond from vapor phase comprising the steps of: preparing a material gas consisting of hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof; introducing the material gas into a vacuum chamber, decomposing the material gas by heat, microwave, light or electric discharge and depositing a diamond film on a substrate body heated at 250° C. to 700° C. such that the concentration of nitrogen in the material gas is less than 1000 ppm.
Claim 2
Independent Claim
103 words
A method for low temperature synthesis of diamond from vapor phase comprising the steps of: preparing a material gas consisting of hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof; introducing the material gas into a vacuum chamber, decomposing the material gas by heat, microwave, light or electric discharge and depositing a diamond film on a substrate body heated at 250° C. to 700° C. such that the concentration of nitrogen in the material gas is less than 1000 ppm.
Claim 3
Independent Claim
115 words
A method for low temperature synthesis of diamond from vapor phase comprising the steps of: preparing a material gas by mixing i) hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof, with, ii) dopant gas of hydrogen gas or rare gas, eliminating nitrogen gas from the material gas so that the nitrogen concentration decreases below 1000 ppm, introducing the material gas into a vacuum chamber, decomposing the material gas by heat, microwave, light or electric discharge, and depositing a diamond film on a substrate body heated at 250° C. to 700° C.
Claim 4
Independent Claim
115 words
A method for low temperature synthesis of diamond from vapor phase comprising the steps of: preparing a material gas by mixing i) hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof, with, ii) dopant gas of hydrogen gas or rare gas, eliminating nitrogen gas from the material gas so that the nitrogen concentration decreases below 1000 ppm, introducing the material gas into a vacuum chamber, decomposing the material gas by heat, microwave, light or electric discharge, and depositing a diamond film on a substrate body heated at 250° C. to 700° C.
Claim 5
Independent Claim
58 words
The method for low temperature synthesis of diamond as claimed in claim (1) or (2), wherein the hydrocarbon gas is paraffine hydrocarbon denoted by a molecular formula C n H 2n+2 , olefin hydrocarbon denoted by a molecular formula C n H 2n , acetylene hydrocarbon denoted by a molecular formula C n H 2n-2 or aromatic hydrocarbon.
Claim 6
Independent Claim
33 words
The method for low temperature synthesis of diamond as claimed in claim (3), wherein halogen gas is fluorine gas (F 2 ), bromine gas (Br 2 ) or chlorine gas (Cl 2 ).
Claim 7
Independent Claim
50 words
The method for low temperature synthesis of diamond as claimed in claim (1) or (2), wherein halogenized hydrocarbon is one of halogenized alkyls denoted by molecular formulas C n H 2n+1 X, C n H 2n XY and C 2 H 2n-1 XYZ, where X, Y and Z are halogen.
Claim 8
Independent Claim
104 words
A method for low temperature synthesis of diamond from vapor phase comprising the steps of: preparing a material gas by mixing hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof, eliminating nitrogen gas from the material gas so that the nitrogen concentration decreases below 1000 ppm, introducing the material gas into a vacuum chamber, decomposing the material gas by heat, microwave, light or electric discharge, and depositing a diamond film on a substrate body heated at 250° C. to 700° C.
Claim 9
Independent Claim
104 words
A method for low temperature synthesis of diamond from vapor phase comprising the steps of: preparing a material gas by mixing hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof, eliminating nitrogen gas from the material gas so that the nitrogen concentration decreases below 1000 ppm, introducing the material gas into a vacuum chamber, decomposing the material gas by heat, microwave, light or electric discharge, and depositing a diamond film on a substrate body heated at 250° C. to 700° C.
Claim 10
Independent Claim
109 words
A method for low temperature synthesis of diamond from vapor phase comprising the steps of: preparing a material gas consisting essentially of hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof, introducing the material gas into a vacuum chamber, and depositing a diamond film on a substrate body, by the chemical vapor deposition method, on a substrate body heated at 250° C. to 700° C.; such that the concentration of nitrogen in the material gas prior to depositing the diamond film is less than 1000 ppm.
Claim 11
Independent Claim
109 words
A method for low temperature synthesis of diamond from vapor phase comprising the steps of: preparing a material gas consisting essentially of hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof, introducing the material gas into a vacuum chamber, and depositing a diamond film on a substrate body, by the chemical vapor deposition method, on a substrate body heated at 250° C. to 700° C.; such that the concentration of nitrogen in the material gas prior to depositing the diamond film is less than 1000 ppm.
Claim 12
Independent Claim
99 words
A method for low temperature synthesis of diamond from a vapor phase comprising the steps of: preparing a material gas consisting essentially of hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof; introducing said material gas into a vacuum chamber; and depositing a diamond film on a substrate body, by chemical vapor deposition, on a substrate body; such that said material gas, prior to depositing said film, has a nitrogen concentration of less than 1000 ppm.
Claim 13
Independent Claim
99 words
A method for low temperature synthesis of diamond from a vapor phase comprising the steps of: preparing a material gas consisting essentially of hydrogen gas, carbon and halogen, said carbon being hydrocarbon gas or halogenized hydrocarbon gas or a mixture thereof, and said halogen being halogen gas or halogenized hydrocarbon gas or a mixture thereof; introducing said material gas into a vacuum chamber; and depositing a diamond film on a substrate body, by chemical vapor deposition, on a substrate body; such that said material gas, prior to depositing said film, has a nitrogen concentration of less than 1000 ppm.
Claim 14
Dependent Claim
23 words
The method of claim 8, wherein said substrate body is heated to a temperature in the range of 250° C. to 700° C.
Claim 15
Dependent Claim
26 words
The method according to claim 8, wherein said hydrocarbon gas is selected from the group consisting of paraffin gas, olefin gas, acetylene gas, and aromatic hydrocarbon.
Claim 16
Dependent Claim
24 words
The method according to claim 8, wherein said halogen gas is selected from the group consisting of fluorine gas, bromine gas, and chlorine gas.
Claim 17
Dependent Claim
50 words
The method according to claim 8, wherein said halogenized hydrocarbon gas is a halogenized alkyl gas selected from the group consisting of gases with the molecular formulae C n H 2n+1 X, C n H 2n XY and C 2 H 2n-1 XYZ, where X, Y and Z are halogen.
Claim 18
Dependent Claim
23 words
The method according to claim 8, wherein said material gas is further mixed with a dopant gas of hydrogen gas or rare gas.
References Cited (Backward Citations)
JPS5930709A
Cited
US4957061A
Cited
US5009923A
Cited
EP0284190B1
Cited
EP0348026A1
Cited
JPH0333641A
Cited
US5094878A
Cited
US5071677A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-02-20 | 1998-08-22 | 1999-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-02-20 | 2002-08-22 | 2003-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-02-20 | 2006-08-22 | 2007-02-21 | $7700.00 | Window Closed / Lapsed |