US5374585A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for forming field isolation
Assignee: Motorola Solutions Inc
•
Filing: 1994-05-09
•
Granted: 1994-12-20
•
Expires: 2014-05-09
Abstract
Abstract A field isolation region is formed by a thermal oxidation followed by a polishing step. In forming the field isolation region, an opening is formed within a nitride layer, but the substrate is not etched. The field isolation region is formed and extends above the opening in the nitride layer. After forming the field isolation region, the substrate is polished, such that the surfaces of the field isolation region and silicon nitride layer are co-planar. The process may be easily integrated into an existing process flow and still provides an integrated circuit having an acceptable field threshold voltage.
Inventors
- 👤 Bradley P. Smith
- 👤 Thomas S. Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:57
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/10; H10W10/13; Y; Y10; Y10S; Y10S148/00; Y10S148/135; Y10S438/00; Y10S438/959
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
163 words
A process for forming a field isolation region comprising the steps of: forming a nitride layer over a primary surface of a semiconductor substrate, wherein the primary surface has a first topography; patterning the nitride layer to form a patterned nitride layer having a nitride layer opening, wherein this step does not etch the semiconductor substrate; growing a field isolation region to a first thickness within the nitride layer opening, wherein: immediately prior to the step of growing the field isolation region, the primary surface has the first topography; and after growing the field isolation region, the primary surface has a second topography that is different from the first topography; and polishing a portion of the field isolation region and the patterned nitride layer, wherein after this step: an exposed surface of the field isolation region is co-planar with an exposed surface of the patterned nitride layer; and the field isolation region has a second thickness that is thinner than the first thickness.
Claim 2
Dependent Claim
163 words
A process for forming a field isolation region comprising the steps of: forming a nitride layer over a primary surface of a semiconductor substrate, wherein the primary surface has a first topography; patterning the nitride layer to form a patterned nitride layer having a nitride layer opening, wherein this step does not etch the semiconductor substrate; growing a field isolation region to a first thickness within the nitride layer opening, wherein: immediately prior to the step of growing the field isolation region, the primary surface has the first topography; and after growing the field isolation region, the primary surface has a second topography that is different from the first topography; and polishing a portion of the field isolation region and the patterned nitride layer, wherein after this step: an exposed surface of the field isolation region is co-planar with an exposed surface of the patterned nitride layer; and the field isolation region has a second thickness that is thinner than the first thickness.
Claim 3
Dependent Claim
39 words
The process of claim 1, further comprising steps of: forming a pad oxide layer over the primary surface of the a semiconductor substrate; and forming a silicon layer over the pad oxide layer prior to forming a nitride layer.
Claim 4
Dependent Claim
26 words
The process of claim 2, further comprising a step of: patterning the silicon layer to form a silicon layer opening that underlies the nitride layer opening.
Claim 5
Dependent Claim
30 words
The process of claim 2, further comprising a step of removing all portions of the silicon and patterned nitride layers that still overlie the substrate after the step of polishing.
Claim 6
Dependent Claim
16 words
The process of claim 1, wherein the first thickness is in a range of 1000-8000 angstroms.
Claim 7
Dependent Claim
21 words
The process of claim 1, wherein the second thickness is in a range of 100-3000 angstroms thinner than the first thickness.
Claim 8
Dependent Claim
39 words
The process of claim 1, wherein the step of polishing is performed at a substrate holder pressure in a range of 3-5 pounds per square inch and a platen rotational velocity in a range of 55-100 rotations per minute.
Claim 9
Dependent Claim
34 words
The process of claim 7, wherein the step of polishing is performed with a polishing solution including a hydroxide and silica particles, and the polishing solution has a pH in a range of 9.5-10.0.
Claim 10
Dependent Claim
39 words
The process of claim 1, wherein the step of polishing is performed at a substrate holder pressure in a range of 3.5-4.5 pounds per square inch and a platen rotational velocity in a range of 70-90 rotations per minute.
Claim 11
Dependent Claim
189 words
A process for forming a field isolation region comprising the steps of: forming a pad oxide layer over a primary surface of a semiconductor substrate, wherein the primary surface has a first topography; forming a silicon layer over the pad oxide layer; forming a nitride layer over the silicon layer; patterning the nitride layer to form a patterned nitride layer having a nitride layer opening, wherein this step does not etch the semiconductor substrate and the primary surface has the first topography; growing a field isolation region to a first thickness within the nitride layer opening, wherein: immediately prior to the step of growing the field isolation region, the primary surface has the first topography; and after growing the field isolation region, the primary surface has a second topography that is different from the first topography; and polishing a portion of the field isolation region and the patterned nitride layer, wherein after this step: an exposed surface of the field isolation region is co-planar with an exposed surface of the patterned nitride layer; and the field isolation region has a second thickness that is thinner than the first thickness.
Claim 12
Dependent Claim
189 words
A process for forming a field isolation region comprising the steps of: forming a pad oxide layer over a primary surface of a semiconductor substrate, wherein the primary surface has a first topography; forming a silicon layer over the pad oxide layer; forming a nitride layer over the silicon layer; patterning the nitride layer to form a patterned nitride layer having a nitride layer opening, wherein this step does not etch the semiconductor substrate and the primary surface has the first topography; growing a field isolation region to a first thickness within the nitride layer opening, wherein: immediately prior to the step of growing the field isolation region, the primary surface has the first topography; and after growing the field isolation region, the primary surface has a second topography that is different from the first topography; and polishing a portion of the field isolation region and the patterned nitride layer, wherein after this step: an exposed surface of the field isolation region is co-planar with an exposed surface of the patterned nitride layer; and the field isolation region has a second thickness that is thinner than the first thickness.
Claim 13
Dependent Claim
26 words
The process of claim 10, further comprising a step of: patterning the silicon layer to form a silicon layer opening that underlies the nitride layer opening.
Claim 14
Dependent Claim
16 words
The process of claim 10, wherein the first thickness is in a range of 1000-8000 angstroms.
Claim 15
Dependent Claim
21 words
The process of claim 10, wherein the second thickness is in a range of 100-3000 angstroms thinner than the first thickness.
Claim 16
Dependent Claim
39 words
The process of claim 10, wherein the step of polishing is performed at a substrate holder pressure in a range of 3-5 pounds per square inch and a platen rotational velocity in a range of 55-100 rotations per minute.
Claim 17
Dependent Claim
34 words
The process of claim 14, wherein the step of polishing is performed with a polishing solution including a hydroxide and silica particles, and the polishing solution has a pH in a range of 9.5-10.0.
Claim 18
Dependent Claim
39 words
The process of claim 10, wherein the step of polishing is performed at a substrate holder pressure in a range of 3.5-4.5 pounds per square inch and a platen rotational velocity in a range of 70-90 rotations per minute.
Claim 19
Dependent Claim
30 words
The process of claim 10, further comprising a step of removing all portions of the silicon and patterned nitride layers that still overlie the substrate after the step of polishing.
References Cited (Backward Citations)
JPS5630738A
Cited
JPS5731164A
Cited
US4691222A
Cited
US4743566A
Cited
JPS6338241A
Cited
US4927780A
Cited
US5151381A
Cited
US5173444A
Cited
US5064683A
Cited
JPH04209534A
Cited
US5196367A
Cited
US5252503A
Cited
US5246537A
Cited
US5310692A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-12-19 | 1998-06-20 | 1998-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-12-19 | 2002-06-20 | 2002-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-12-19 | 2006-06-20 | 2006-12-20 | $7700.00 | Window Closed / Lapsed |