Method for forming inter-metal dielectrics in a semiconductor device
Assignee: Samsung Electronics Co Ltd
•
Filing: 1992-10-02
•
Granted: 1994-10-04
•
Expires: 2012-10-02
Abstract
Abstract A method for forming an inter-metal dielectrics in a semiconductor device includes the steps of sequentially forming a first and second insulating layers over a semiconductor substrate with a patterned metal layers, etching-back the second insulating layer so as to form second insulating spacers over the side walls of the first insulating layer, and growing a third insulating layer over the first and second insulating layers, the growing speed of the third insulating layer being different from the region over the first insulating layer to the region over the second insulating layer.
Inventors
- 👤 Chang-Gyu Kim
- 👤 Ji-Hyun Choi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:42
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/65; H10P14/6502; H10P14/6506; H10P95/00; H10P95/06; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/074; H10W20/075; H10W20/077; H10W20/092
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
187 words
A method for forming a planarized dielectric layer on a structure comprised of a semiconductor substrate and a patterned conductive layer formed thereon, whereby the topology of the structure consists of raised surface features defining recesses therebetween, the method comprising the steps of: forming a first insulating layer on said structure; forming a second insulating layer on said first insulating layer; etching back said second insulating layer to remove portions of said second insulating layer disposed on said first insulating layer and above said raised surface features, but without removing any of said first insulating layer, to thereby expose portions of said first insulating layer disposed on said raised surface features and to leave remaining portions of said second insulating layer in said recesses; and, depositing a third insulating layer on said exposed portions of said first insulating layer at a first deposition rate, and depositing said third insulating layer within said recesses at a second deposition rate, wherein the difference between said first and second deposition rates is such as to result in the upper surface of said third insulating layer having a substantially flat profile.
Claim 2
Independent Claim
187 words
A method for forming a planarized dielectric layer on a structure comprised of a semiconductor substrate and a patterned conductive layer formed thereon, whereby the topology of the structure consists of raised surface features defining recesses therebetween, the method comprising the steps of: forming a first insulating layer on said structure; forming a second insulating layer on said first insulating layer; etching back said second insulating layer to remove portions of said second insulating layer disposed on said first insulating layer and above said raised surface features, but without removing any of said first insulating layer, to thereby expose portions of said first insulating layer disposed on said raised surface features and to leave remaining portions of said second insulating layer in said recesses; and, depositing a third insulating layer on said exposed portions of said first insulating layer at a first deposition rate, and depositing said third insulating layer within said recesses at a second deposition rate, wherein the difference between said first and second deposition rates is such as to result in the upper surface of said third insulating layer having a substantially flat profile.
Claim 3
Dependent Claim
36 words
The method as set forth in claim 1, wherein said first insulating layer is a material selected from a group consisting of PSG, O 3 --TEOS PSG, O 3 --TEOS BPSG, and P--TEOS undoped silicated glass.
Claim 4
Dependent Claim
34 words
The method as set forth in claim 2, wherein said second insulating layer is a material selected from a group consisting of plasma-enhanced silane undoped silicate glass and O 3 --TEOS undoped silicate glass.
Claim 5
Dependent Claim
22 words
The method as set forth in claim 3, wherein said third insulating layer is comprised of O 3 --TEOS undoped silicate glass.
Claim 6
Independent Claim
208 words
A method for forming a planarized dielectric layer on a structure comprised of a semiconductor substrate and a patterned conductive layer formed thereon, whereby the topology of the structure consists of a raised surface features defining recesses therebetween, the method comprising the steps of: forming a first insulating layer on said structure; forming a second insulating layer on said first insulating layer; applying a sacrificial layer on said second insulating layer; etching back said sacrificial layer to expose portions of said second insulating layer disposed above said raised surface features, thereby leaving remaining portions of said sacrificial layer in said recesses; removing said exposed portions of said second insulating layer by using said remaining portions of said sacrificial layer as a mask, to thereby expose portions of said first insulating layer disposed on said raised surface features; removing said remaining portions of said sacrificial layer; and, depositing a third insulating layer on said exposed portions of said first insulating layer at a first deposition rate, and depositing said third insulating layer within said recesses at a second deposition rate, wherein the difference between said first and second deposition rates is such as to result int he upper surface of said third insulating layer having a substantially flat profile.
Claim 7
Independent Claim
208 words
A method for forming a planarized dielectric layer on a structure comprised of a semiconductor substrate and a patterned conductive layer formed thereon, whereby the topology of the structure consists of a raised surface features defining recesses therebetween, the method comprising the steps of: forming a first insulating layer on said structure; forming a second insulating layer on said first insulating layer; applying a sacrificial layer on said second insulating layer; etching back said sacrificial layer to expose portions of said second insulating layer disposed above said raised surface features, thereby leaving remaining portions of said sacrificial layer in said recesses; removing said exposed portions of said second insulating layer by using said remaining portions of said sacrificial layer as a mask, to thereby expose portions of said first insulating layer disposed on said raised surface features; removing said remaining portions of said sacrificial layer; and, depositing a third insulating layer on said exposed portions of said first insulating layer at a first deposition rate, and depositing said third insulating layer within said recesses at a second deposition rate, wherein the difference between said first and second deposition rates is such as to result int he upper surface of said third insulating layer having a substantially flat profile.
Claim 8
Dependent Claim
18 words
The method ass et forth in claim 5, wherein said sacrificial layer is comprised of a photoresist material.
Claim 9
Dependent Claim
16 words
The method as set forth in claim 5, wherein said sacrificial layer is comprised of spin-on-glass.
Claim 10
Dependent Claim
36 words
The method as set forth in claim 5, wherein said first insulating layer is a material selected from a group consisting of PSG, O 3 --TEOS PSG, O 3 --TEOS BPSG, and P-TEOS undoped silicated glass.
Claim 11
Dependent Claim
34 words
The method as set forth in claim 8, wherein said second insulating layer is a material selected from a group consisting of plasma-enhanced silane undoped silicate glass and O 3 --TEOS undoped silicate glass.
Claim 12
Dependent Claim
22 words
The method as set forth in claim 9, wherein said third insulating layer is comprised of O 3 --TEOS undoped silicate glass.
Claim 13
Dependent Claim
40 words
The method as set forth in claim 1, wherein said etching back step is carried out by using an anisotropic etching process, to thereby leave remaining portions of said second insulating layer on only sidewalls of said raised surface features.
References Cited (Backward Citations)
US4474831A
Cited
US4535528A
Cited
US4839311A
Cited
US4986878A
Cited
US5160986A
Cited
US5051380A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-10-03 | 1998-04-04 | 1998-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-10-03 | 2002-04-04 | 2002-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-10-03 | 2006-04-04 | 2006-10-04 | $7700.00 | Window Closed / Lapsed |