US5346719A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Tungsten metallization of CVD diamond
Assignee: Diamond Innovations Inc
•
Filing: 1993-08-02
•
Granted: 1994-09-13
•
Expires: 2013-08-02
Abstract
Abstract A process for significantly improving the adhesion of a refractory metal deposited on diamond is disclosed. The process involves depositing an initial thin metal coating by low pressure chemical vapor deposition on diamond, heat treating in a non-oxidizing environment, and continuing the deposition of the initial metal coating until a desired thickness is achieved. Diamond sheets that have undergone the inventive process where 15 micrometers of tungsten are deposited, exhibit tungsten adhesive values in excess of 10,000 pounds per square inch.
Inventors
- 👤 Kenneth P. Zarnoch
- 👤 Charles D. Iacovangelo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:13
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/14; C09K3/1436; C09K3/1445; C23; C23C; C23C16/00; C23C16/02; C23C16/0272; C23C16/0281; C23C16/06; C23C16/08; C23C16/14; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/38; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155; Y10T29/49165
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
61 words
A process for improving adhesion of metal coatings on diamond surfaces comprising: depositing an initial uniform thin coating of a refractory metal on a diamond surface, wherein the initial coating of the refractory metal is about 10-10,000 angstroms; heat treating said initial coating to form a refractory metal-carbon bonding layer with said diamond; and then continuing deposition of said refractory metal.
Claim 2
Dependent Claim
61 words
A process for improving adhesion of metal coatings on diamond surfaces comprising: depositing an initial uniform thin coating of a refractory metal on a diamond surface, wherein the initial coating of the refractory metal is about 10-10,000 angstroms; heat treating said initial coating to form a refractory metal-carbon bonding layer with said diamond; and then continuing deposition of said refractory metal.
Claim 3
Dependent Claim
32 words
A process according to claim 1 wherein said refractory metal is selected from the group consisting of tungsten, niobium, molybdenum, chromium, titanium, vanadium, tantalum, zirconium, hafnium, aluminum, and mixtures of said metals.
Claim 4
Dependent Claim
23 words
A process according to claim 1 wherein the heat treatment is conducted at a temperature of about 700°-1200° C. in a non-oxidizing environment.
Claim 5
Dependent Claim
15 words
A process according to claim 3 wherein the heat treatment time is about 5-60 minutes.
Claim 6
Dependent Claim
25 words
A process according to claim 1 wherein said deposition of said refractory metal takes place by low pressure chemical vapor deposition in a non-oxidizing environment.
Claim 7
Dependent Claim
23 words
A process according to claim 5 wherein said initial coating of refractory metal is deposited at about 300°-700° C. at about 0.1-3.0 torr.
Claim 8
Dependent Claim
26 words
A process according to claim 5 wherein after heat treatment, deposition of said refractory metal is continued at about 400°-800° C. and at about 0.1-3.0 torr.
Claim 9
Dependent Claim
75 words
A process for improving adhesion of tungsten on diamond comprising depositing by low pressure chemical vapor deposition at about 450° C. and at about 0.5 torr an initial tungsten coating of about 200 Å on a diamond surface substantially free of contaminants; heating said diamond to about 900°-1000° C. in a non-oxidizing atmosphere until a tungsten-carbon bonding layer forms with said diamond; and depositing additional tungsten at about 650° C. and at about 0.5 torr.
Claim 10
Dependent Claim
75 words
A process for improving adhesion of tungsten on diamond comprising depositing by low pressure chemical vapor deposition at about 450° C. and at about 0.5 torr an initial tungsten coating of about 200 Å on a diamond surface substantially free of contaminants; heating said diamond to about 900°-1000° C. in a non-oxidizing atmosphere until a tungsten-carbon bonding layer forms with said diamond; and depositing additional tungsten at about 650° C. and at about 0.5 torr.
Claim 11
Dependent Claim
19 words
A process according to claim 8 wherein the tungsten coating is formed by the hydrogen reduction of tungsten hexafluoride.
Claim 12
Dependent Claim
97 words
A process for improving adhesion of metal to apertures in diamond comprising depositing by low pressure chemical vapor deposition in a non-oxidizing atmosphere about a 10-10,000 Å thick layer of a refractory metal at about 300°-700° C. and at about 0.1-3.0 torr on diamond surfaces and within said apertures; heat treating the deposit thus formed in a non-oxidizing atmosphere at a temperature of about 700°-1200° C. to form a refractory metal-carbon bonding layer with said diamond; then continuing deposition of said refractory metal at about 400°-800° C. and at about 0.1-3.0 torr to substantially fill said apertures.
Claim 13
Dependent Claim
97 words
A process for improving adhesion of metal to apertures in diamond comprising depositing by low pressure chemical vapor deposition in a non-oxidizing atmosphere about a 10-10,000 Å thick layer of a refractory metal at about 300°-700° C. and at about 0.1-3.0 torr on diamond surfaces and within said apertures; heat treating the deposit thus formed in a non-oxidizing atmosphere at a temperature of about 700°-1200° C. to form a refractory metal-carbon bonding layer with said diamond; then continuing deposition of said refractory metal at about 400°-800° C. and at about 0.1-3.0 torr to substantially fill said apertures.
Claim 14
Dependent Claim
19 words
A process according to claim 10 wherein said apertures are vias extending between two surfaces of said diamond substrate.
Claim 15
Dependent Claim
21 words
A process according to claim 10 wherein said vias have an aspect ratio in the range of about 0.1 to 100.
Claim 16
Dependent Claim
32 words
A process according to claim 10 wherein said refractory metals are selected from the group consisting of tungsten, niobium, molybdenum, chromium, titanium, vanadium, tantalum, zirconium, hafnium, aluminum, and mixtures of said metals.
Claim 17
Dependent Claim
11 words
A process according to claim 13 wherein said metal is tungsten.
Claim 18
Dependent Claim
52 words
A process according to claim 14 wherein said tungsten is initially deposited at about 450° C. and at about 0.5 torr to a thickness of about 200 Å, then heat treated at about 900°-1000° C. for about 30-60 minutes, followed by further deposition at about 650° C. and at about 0.5 torr.
Claim 19
Dependent Claim
18 words
A process according to claim 14 wherein the tungsten is formed by the hydrogen reduction of tungsten hexafluoride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-09-12 | 1998-03-14 | 1998-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-09-12 | 2002-03-14 | 2002-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-09-12 | 2006-03-14 | 2006-09-13 | $7700.00 | Window Closed / Lapsed |