Process for obtaining multi-layer metallization of the back of a semiconductor substrate
Assignee: STMicroelectronics SRL
•
Filing: 1993-07-09
•
Granted: 1994-08-30
•
Expires: 2013-07-09
Abstract
Abstract The metallization of the back of the semiconductor substrate is obtained by depositing a series of metal layers, after ion implantation of dopant on the interface with the first layer. The step of ion implantation is followed by the deposition of one or more metal layers of the aforesaid series, and then by thermal annealing under vacuum or in an inert atmosphere, at a temperature considerably lower than 500° C. and for a period considerably shorter than 60 minutes.
Inventors
- 👤 Antonello Santangelo
- 👤 Carmelo Margo
- 👤 Paolo Lanza
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 11:31
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
123 words
Process for metallizing the back of a semiconductor substrate, by depositing a series of metal layers, after ion implantation of dopant on the surface of the semiconductor which acts as an interface with the first layer of metal, characterized by the fact that the step of ion implantation of dopant is carried out in such a way as to amorphize the surface of the semiconductor substrate, and is followed by the deposition of one or more layers of metal of the aforesaid series, and then by thermal annealing under vacuum or in an inert atmosphere, at a temperature considerably lower than 500° C. and for a period considerably shorter than 60 minutes; wherein the first of said series of metal layers comprises titanium.
Claim 2
Dependent Claim
123 words
Process for metallizing the back of a semiconductor substrate, by depositing a series of metal layers, after ion implantation of dopant on the surface of the semiconductor which acts as an interface with the first layer of metal, characterized by the fact that the step of ion implantation of dopant is carried out in such a way as to amorphize the surface of the semiconductor substrate, and is followed by the deposition of one or more layers of metal of the aforesaid series, and then by thermal annealing under vacuum or in an inert atmosphere, at a temperature considerably lower than 500° C. and for a period considerably shorter than 60 minutes; wherein the first of said series of metal layers comprises titanium.
Claim 3
Dependent Claim
54 words
Process as claimed in claim 1, characterized by the fact that the deposition of the metal layers and the thermal annealing are carried out in the same equipment suitable for sequential deposition of several layers of metal on a semiconductor substrate and for heating the same substrate under vacuum or in an inert atmosphere.
Claim 4
Dependent Claim
57 words
Process as claimed in claim 1, characterized by the fact that the thermal annealing is carried out in a high-vacuum atmosphere with a pressure which is less than or equal to 10 -6 Torr, at a temperature which is less than or equal 400° C. and for a period which is less than or equal 30 minutes.
Claim 5
Dependent Claim
49 words
Process as claimed in claim 1, characterized by the fact that the thermal annealing is carried out in an atmosphere consisting of inert gas at a pressure which is less than or equal to 30·10 -3 Torr, at a temperature which is less than or equal to 30 minutes.
Claim 6
Dependent Claim
38 words
Process as claimed in claim 1, characterized by the fact that the fact that the substrate consists of N type silicon, the implanted dopant is arsenic, and the implantation energy is less than or equal to 10 KeV.
Claim 7
Dependent Claim
51 words
Process as claimed in claim 5, characterized by the fact that the dose of arsenic implanted is approximately 2·10 14 atoms/cm 2 , the implantation energy is approximately 5 KeV, and the thermal annealing is carried out at a temperature of approximately 375° C. for a period of approximately 30 minutes.
Claim 8
Dependent Claim
142 words
Process for metallizing the back of a semiconductor substrate, by depositing a series of metal layers, after ion implantation of dopant on the surface of the semiconductor which acts as an interface with the first layer of metal, characterized by the fact that the step of ion implantation of dopant is carried out in such a way as to amorphize the surface of the semiconductor substrate, and is followed by the deposition of one or more layers of metal of the aforesaid series, and then by thermal annealing under vacuum or in an inert atmosphere, at a temperature considerably lower than 500° C. and for a period considerably shorter than 60 minutes; wherein the first of said series of metal layers comprises a metal which fails to form an alloy in the liquid state with the semiconductor at temperatures below 500° C.
Claim 9
Dependent Claim
142 words
Process for metallizing the back of a semiconductor substrate, by depositing a series of metal layers, after ion implantation of dopant on the surface of the semiconductor which acts as an interface with the first layer of metal, characterized by the fact that the step of ion implantation of dopant is carried out in such a way as to amorphize the surface of the semiconductor substrate, and is followed by the deposition of one or more layers of metal of the aforesaid series, and then by thermal annealing under vacuum or in an inert atmosphere, at a temperature considerably lower than 500° C. and for a period considerably shorter than 60 minutes; wherein the first of said series of metal layers comprises a metal which fails to form an alloy in the liquid state with the semiconductor at temperatures below 500° C.
Claim 10
Dependent Claim
54 words
Process as claimed in claim 7, characterized by the fact that the deposition of the metal layers and the thermal annealing are carried out in the same equipment suitable for sequential deposition of several layers of metal on a semiconductor substrate and for heating the same substrate under vacuum or in an inert atmosphere.
Claim 11
Dependent Claim
59 words
Process as claimed in claim 7, characterized by the fact that the thermal annealing is carried out in a high-vacuum atmosphere with a pressure which is less than or equal to 10 -6 Torr, at a temperature which is less than or equal to 400° C. and for a period which is less than or equal to 30 minutes.
Claim 12
Dependent Claim
62 words
Process as claimed in claim 7, characterized by the fact that the thermal annealing is carried out in an atmosphere consisting of inert gas at a pressure which is less than or equal to 30·10 -3 Torr, at a temperature which is less than or equal to 400° C. and for a period which is less than or equal to 30 minutes.
Claim 13
Dependent Claim
38 words
Process as claimed in claim 7, characterized by the fact that the fact that the substrate consists of N type silicon, the implanted dopant is arsenic, and the implantation energy is less than or equal to 10 KeV.
Claim 14
Dependent Claim
51 words
Process as claimed in claim 11, characterized by the fact that the dose of arsenic implanted is approximately 2·10 14 atoms/cm 2 , the implantation energy is approximately 5 KeV, and the thermal annealing is carried out at a temperature of approximately 375° C. for a period of approximately 30 minutes.
References Cited (Backward Citations)
US3934331A
Cited
EP0012324A1
Cited
CA1120607A
Cited
JPS5715420A
Cited
JPS58106825A
Cited
FR2531106A1
Cited
US4517226A
Cited
US4914054A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-29 | 1998-02-28 | 1998-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-29 | 2002-02-28 | 2002-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-29 | 2006-02-28 | 2006-08-30 | $7700.00 | Window Closed / Lapsed |