Method for manufacturing inorganic membranes by organometallic chemical vapor infiltration
Assignee: Air Products and Chemicals Inc
•
Filing: 1992-11-09
•
Granted: 1994-07-26
•
Expires: 2012-11-09
Abstract
Abstract The present invention is a method for manufacturing inorganic membranes which are capable of separating oxygen from oxygen-containing gaseous mixtures. The membranes comprise a porous composite of a thin layer of a multicomponent metallic oxide which has been deposited onto a porous support wherein the pores of the multicomponent metallic oxide layer are subsequently filled or plugged with a metallic-based species. The inorganic membranes are formed by depositing a porous multicomponent metallic oxide layer onto the porous support to form a porous composite having a network of pores capable of transporting gases. The network of pores are plugged or filled by organometallic vapor infiltration to form an inorganic membrane having essentially no through porosity.
Inventors
- 👤 Michael F. Carolan
- 👤 Paul N. Dyer
- 👤 Stephen M. Fine
- 👤 Alexander Makitka, III
- 👤 Robin E. Richards
- 👤 Leslie E. Schaffer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:50
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0039; B01D67/0072; B01D67/0044; B01D71/00; B01D71/02; B01D71/022; B01D71/0223; B01D71/02232; B01D71/024; C; C04; C04B; C04B41/00; C04B41/45; C04B41/52; C23; C23C; C23C16/00; C23C16/04; C23C16/045; C23C16/44; C23C16/46; B01D2323/00; B01D2323/08; B01D2323/081; B01D2323/12; B01D2325/00; B01D2325/02; B01D2325/0283; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12042; Y10T428/12479; Y10T428/249921; Y10T428/249953; Y10T428/249955; Y10T428/249956; Y10T428/249957; Y10T428/249967; Y10T428/24997; Y10T428/249981; Y10T428/249994; Y10T428/249999
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
127 words
A method for manufacturing an inorganic membrane capable of separating oxygen from an oxygen-containing gaseous mixture, the method comprising the steps of: (a) depositing a porous multicomponent metallic oxide layer onto a porous support to form a porous composite having a network of pores capable of transporting gases; (b) contacting a first surface of the porous composite with a vaporized organometallic complex and a second surface of the porous composite with a gaseous reactive agent comprising an oxidizing or reducing agent at a temperature ranging from 300° to 600° C. and a pressure sufficient to react the organometallic complex and the gaseous reactive agent to form plugs in the pores of the porous multicomponent metallic oxide layer to form an inorganic membrane having essentially no through porosity.
Claim 2
Independent Claim
127 words
A method for manufacturing an inorganic membrane capable of separating oxygen from an oxygen-containing gaseous mixture, the method comprising the steps of: (a) depositing a porous multicomponent metallic oxide layer onto a porous support to form a porous composite having a network of pores capable of transporting gases; (b) contacting a first surface of the porous composite with a vaporized organometallic complex and a second surface of the porous composite with a gaseous reactive agent comprising an oxidizing or reducing agent at a temperature ranging from 300° to 600° C. and a pressure sufficient to react the organometallic complex and the gaseous reactive agent to form plugs in the pores of the porous multicomponent metallic oxide layer to form an inorganic membrane having essentially no through porosity.
Claim 3
Dependent Claim
35 words
The method of claim 1 wherein the porous support has an average pore diameter of greater than 1 μm and the multicomponent metallic oxide layer has an average pore diameter of less than 1 μm.
Claim 4
Dependent Claim
34 words
The method of claim 2 wherein the depositing of the porous multicomponent metallic oxide layer onto the porous support according to step (a) is accomplished by chemical vapor deposition, dip coating or vacuum filtration.
Claim 5
Dependent Claim
32 words
The method of claim 2 wherein the depositing of the porous multicomponent metallic oxide layer onto the porous support according to step (a) is accomplished by tape casting, coextrusion, spraying or electrophoresis.
Claim 6
Dependent Claim
20 words
The method of claim 4 wherein the depositing is accomplished by plasma spraying, arc spraying, flame spraying or aerosol spraying.
Claim 7
Dependent Claim
41 words
The method of claim 3 which further comprises sintering the porous composite formed in step (a) at a temperature ranging from 500° C. to 1500° C. for a period ranging from 10 minutes to twenty-four hours prior to conducting step (b).
Claim 8
Dependent Claim
32 words
The method of claim 1 wherein the contacting of the organometallic complex and the gaseous reactive agent according to step (b) occurs at a pressure ranging from 1 to about 100 Torr.
Claim 9
Dependent Claim
36 words
The method of claim 7 wherein the organometallic complex is selected from the group consisting of Fe(thd) 3 , La(thd) 3 , Co(thd) 2 , (Ba) 4 (thd) 8 , Mg(thd) 2 and Sr(thd) 2 .
Claim 10
Dependent Claim
29 words
The method of claim 8 wherein the gaseous reactive agent is an oxidizing agent and the plugs comprise a metallic oxide, a metallic carbonate or a multicomponent metallic oxide.
Claim 11
Dependent Claim
24 words
The method of claim 9 wherein the oxidizing agent is selected from the group consisting of oxygen, air, ozone, N 2 O and water.
Claim 12
Dependent Claim
24 words
The method of claim 1 wherein the gaseous reactive agent is a reducing agent and the plugs comprise a metal or mixture of metals.
Claim 13
Dependent Claim
20 words
The method of claim 11 wherein the reducing agent is selected from the group consisting of H 2 and CO.
Claim 14
Independent Claim
205 words
A method for manufacturing an inorganic membrane capable of separating oxygen from an oxygen-containing gaseous mixture, the method comprising the steps of: (a) depositing a porous multicomponent metallic oxide layer represented by the formula A x A' x' A" x" B y B' y' B" y" O 3-z , where A,A',A" are chosen from the group comprising Groups 1, 2, 3 and 15 and the F block lanthanides; and B,B',B" are chosen from the D block transition metals according to the Periodic Table of the Elements adopted by the IUPAC wherein 0<x≦1 , 0≦x'≦1, 0≦x"≦1, 0<y≦1, 0≦y'≦1, 0≦y"≦1, X+x'+x"=1, y+Y'+y"=1 and z is a number which renders the compound charge neutral, onto a porous support to form a porous composite having a network of pores capable of transporting gases; (b) contacting a first surface of the porous composite with a vaporized organometallic complex and a second surface of the porous composite with a gaseous reactive agent comprising an oxidizing or reducing agent at a temperature ranging from 300° to 600° C. and a pressure sufficient to react the organometallic complex and the gaseous reactive agent to form plugs in the pores of the porous composite to form an inorganic membrane having essentially no through porosity.
Claim 15
Independent Claim
205 words
A method for manufacturing an inorganic membrane capable of separating oxygen from an oxygen-containing gaseous mixture, the method comprising the steps of: (a) depositing a porous multicomponent metallic oxide layer represented by the formula A x A' x' A" x" B y B' y' B" y" O 3-z , where A,A',A" are chosen from the group comprising Groups 1, 2, 3 and 15 and the F block lanthanides; and B,B',B" are chosen from the D block transition metals according to the Periodic Table of the Elements adopted by the IUPAC wherein 0<x≦1 , 0≦x'≦1, 0≦x"≦1, 0<y≦1, 0≦y'≦1, 0≦y"≦1, X+x'+x"=1, y+Y'+y"=1 and z is a number which renders the compound charge neutral, onto a porous support to form a porous composite having a network of pores capable of transporting gases; (b) contacting a first surface of the porous composite with a vaporized organometallic complex and a second surface of the porous composite with a gaseous reactive agent comprising an oxidizing or reducing agent at a temperature ranging from 300° to 600° C. and a pressure sufficient to react the organometallic complex and the gaseous reactive agent to form plugs in the pores of the porous composite to form an inorganic membrane having essentially no through porosity.
Claim 16
Dependent Claim
35 words
The method of claim 13 wherein the porous support has an average pore diameter of greater than 1 μm and the multicomponent metallic oxide layer has an average pore diameter of less than 1 μm.
Claim 17
Dependent Claim
30 words
The method of claim 14 wherein the depositing of the porous multicomponent metallic oxide layer onto the porous support of step (a) is accomplished by dip coating or vacuum filtration.
Claim 18
Dependent Claim
31 words
The method of claim 14 wherein the depositing of the porous multicomponent metallic oxide layer onto the porous support of step (a) is accomplished by tape casting, coextrusion, spraying or electrophoresis.
Claim 19
Dependent Claim
20 words
The method of claim 16 wherein the depositing is accomplished by plasma spraying, arc spraying, flame spraying or aerosol spraying.
Claim 20
Dependent Claim
41 words
The method of claim 15 which further comprises sintering the porous composite formed in step (a) at a temperature ranging from 500° C. to 1500° C. for a period ranging from 10 minutes to twenty-four hours prior to conducting step (b).
Claim 21
Dependent Claim
32 words
The method of claim 13 wherein the contacting of the organometallic complex and the gaseous reactive agent according to step (b) occurs at a pressure ranging from 1 to about 100 Torr.
Claim 22
Dependent Claim
36 words
The method of claim 19 wherein the organometallic complex is selected from the group consisting of Fe(thd) 3 , La(thd) 3 , Co(thd) 2 , (Ba) 4 (thd) 8 , Mg(thd) 2 and Sr(thd) 2 .
Claim 23
Dependent Claim
29 words
The method of claim 20 wherein the gaseous reactive agent is an oxidizing agent and the plugs comprise a metallic oxide, a metallic carbonate or a multicomponent metallic oxide.
Claim 24
Dependent Claim
24 words
The method of claim 21 wherein the oxidizing agent is selected from the group consisting of oxygen, air, ozone, N 2 O and water.
Claim 25
Dependent Claim
24 words
The method of claim 13 wherein the gaseous reactive agent is a reducing agent and the plugs comprise a metal or mixture of metals.
Claim 26
Dependent Claim
20 words
The method of claim 23 wherein the reducing agent is selected from the group consisting of H 2 and CO.
References Cited (Backward Citations)
US4330663A
Cited
JPS6121717A
Cited
US4609562A
Cited
US4992305A
Cited
US5140003A
Cited
US5106654A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-07-25 | 1998-01-24 | 1998-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-07-25 | 2002-01-24 | 2002-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-07-25 | 2006-01-24 | 2006-07-26 | $7700.00 | Window Closed / Lapsed |