Hot melt adhesive
Assignee: Henkel Corp
•
Filing: 1993-02-23
•
Granted: 1994-07-19
•
Expires: 2013-02-23
Abstract
Abstract Hot melt packaging adhesive compositions consisting essentially of 20 to 50% by weight of an ethylene n-butyl acrylate copolymer containing 25-45% by weight, preferably 30 to 40% n-butyl acrylate and having a melt index of at least 10; 30 to 60% of an aliphatic or cycloaliphatic hydrocarbon resin or hydrogenated derivative thereof or a hydrogenated aromatic hydrocarbon resin; and 10 to 30% by weight of a high melting synthetic wax provide adhesives characterized by an excellent balance of high and low temperature performance without sacrifice to machinability or thermal stability. Further, the adhesive is characterized by a low density and consequently is readily filterable in recycling systems.
Inventors
- 👤 Daniel Stauffer
- 👤 Paul P. Puletti
- 👤 Thomas F. Kauffman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:45
CPC Classifications
C; C08; C08L; C08L91/00; C08L91/06; C09; C09J; C09J123/00; C09J123/02; C09J123/04; C09J123/08; C09J157/00; C09J157/02; C09J165/00; C08L2666/00; C08L2666/02; C08L2666/04
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
112 words
A carton, case or tray formed utilizing a hot melt adhesive composition having a specific gravity less than 0.98 and a viscosity less than 8000 cps at 175° C., said adhesive consisting essentially of: a) 20 to 50% by weight of at least one ethylene n-butyl acrylate copolymer containing 25-45% by weight n-butyl acrylate and having a melt index of at least 10; b) 30 to 60% of a tackifying resin selected from the group consisting of aliphatic and cycloaliphatic hydrocarbon resins or hydrogenated derivatives thereof and hydrogenated aromatic hydrocarbon resins; c) 10 to 30% by weight of a synthetic wax having a melting point above 100° C.; and d) 0-1.5% stabilizer.
Claim 2
Dependent Claim
112 words
A carton, case or tray formed utilizing a hot melt adhesive composition having a specific gravity less than 0.98 and a viscosity less than 8000 cps at 175° C., said adhesive consisting essentially of: a) 20 to 50% by weight of at least one ethylene n-butyl acrylate copolymer containing 25-45% by weight n-butyl acrylate and having a melt index of at least 10; b) 30 to 60% of a tackifying resin selected from the group consisting of aliphatic and cycloaliphatic hydrocarbon resins or hydrogenated derivatives thereof and hydrogenated aromatic hydrocarbon resins; c) 10 to 30% by weight of a synthetic wax having a melting point above 100° C.; and d) 0-1.5% stabilizer.
Claim 3
Dependent Claim
22 words
The carton, case or tray of claim 1 wherein the ethylene/n-butyl acrylate copolymer in the adhesive contains 30 to 35% n-butyl acrylate.
Claim 4
Dependent Claim
24 words
The carton, case or tray of claim 1 wherein the ethylene/n-butyl acrylate copolymer in the adhesive has a melt index between 100 and 800.
Claim 5
Dependent Claim
27 words
The carton, case or tray of claim 1 wherein the tackifying resin in the adhesive has a Ring and Ball softening point of 70° to 150° C.
Claim 6
Dependent Claim
27 words
The carton, case or tray of claim 1 wherein the tackifying resin in the adhesive is an aliphatic or cycloaliphatic petroleum hydrocarbon resin or hydrogenated derivative thereof.
Claim 7
Dependent Claim
32 words
The carton, case or tray of claim 1 wherein the wax in the adhesive is selected from the group consisting of synthetic, high density, low molecular weight polyethylene waxes and Fischer-Tropsch waxes.
Claim 8
Dependent Claim
18 words
The carton, case or tray of claim 6 wherein the wax in the adhesive is a Fischer-Tropsch wax.
Claim 9
Dependent Claim
36 words
The carton, case or tray of claim 1 wherein the adhesive contains a blend of an ethylene/n-butyl acrylate copolymer having a melt index of 45 and an ethylene/n-butyl acrylate copolymer having a melt index of 400.
Claim 10
Dependent Claim
56 words
The carton, case or tray of claim 1 wherein the adhesive consists essentially of a blend of an ethylene/n-butyl acrylate copolymer having a melt index of 45 and an ethylene/n-butyl acrylate copolymer having a melt index of 400; tackifying resin having a Ring and Ball softening point of 70° to 150° C. and a Fischer-Tropsch wax.
Claim 11
Dependent Claim
31 words
The carton, case or tray of claim 1 used for packaging products at temperatures greater than about 40° C., which products will be stored at temperatures less than about -18° C.
Claim 12
Dependent Claim
164 words
Hot melt adhesive compositions having a specific gravity less than 0.98, said adhesive consisting essentially of: a) 20 to 50% by weight of at least one ethylene n-butyl acrylate copolymer containing 25-45% by weight n-butyl acrylate and having a melt index of at least 10; b) 30 to 60% of a tackifying resin selected from the group consisting of aliphatic and cycloaliphatic hydrocarbon resins or hydrogenated derivatives thereof and hydrogenated aromatic hydrocarbon resins; c) 10 to 30% by weight of a synthetic wax having a melting point above 100° C.; and d) 0-1.5% stabilizer; said adhesive characterized by a viscosity of less than 8000 cps at 175° C., fiber tearing bonds from Kraft paper within the range of 0° to 160° F., a Ring and Ball softening point of 100°-130° C., a cloud point less than 140° C., clarity at 170° C. and being capable of surviving a 144 hour covered thermal stability test for 144 hours with no char, skinning or gel formation.
Claim 13
Dependent Claim
164 words
Hot melt adhesive compositions having a specific gravity less than 0.98, said adhesive consisting essentially of: a) 20 to 50% by weight of at least one ethylene n-butyl acrylate copolymer containing 25-45% by weight n-butyl acrylate and having a melt index of at least 10; b) 30 to 60% of a tackifying resin selected from the group consisting of aliphatic and cycloaliphatic hydrocarbon resins or hydrogenated derivatives thereof and hydrogenated aromatic hydrocarbon resins; c) 10 to 30% by weight of a synthetic wax having a melting point above 100° C.; and d) 0-1.5% stabilizer; said adhesive characterized by a viscosity of less than 8000 cps at 175° C., fiber tearing bonds from Kraft paper within the range of 0° to 160° F., a Ring and Ball softening point of 100°-130° C., a cloud point less than 140° C., clarity at 170° C. and being capable of surviving a 144 hour covered thermal stability test for 144 hours with no char, skinning or gel formation.
Claim 14
Dependent Claim
19 words
The adhesive of claim 11 wherein the ethylene/n-butyl acrylate copolymer in the adhesive contains 30 to 35% n-butyl acrylate.
Claim 15
Dependent Claim
18 words
The adhesive of claim 11 wherein the ethylene/n-butyl acrylate copolymer has a melt index between 100 and 800.
Claim 16
Dependent Claim
21 words
The adhesive of claim 11 wherein the tackifying resin has a Ring and Ball softening point of 70° to 150° C.
Claim 17
Dependent Claim
21 words
The adhesive of claim 11 wherein the tackifying resin is an aliphatic or cycloaliphatic petroleum hydrocarbon resin or hydrogenated derivative thereof.
Claim 18
Dependent Claim
26 words
The adhesive of claim 11 wherein the wax is selected from the group consisting of synthetic, high density, low molecular weight polyethylene waxes and Fischer-Tropsch waxes.
Claim 19
Dependent Claim
30 words
The adhesive of claim 11 containing a blend of an ethylene/n-butyl acrylate copolymer having a melt index of 45 and an ethylene/n-butyl acrylate copolymer having a melt index of 400.
Claim 20
Dependent Claim
51 words
The adhesive of claim 11 consisting essentially of a blend of an ethylene/n-butyl acrylate copolymer having a melt index of 45 and an ethylene/n-butyl acrylate copolymer having a melt index of 400; a tackifying resin having a Ring and Ball softening point of 70° to 150° C. and a Fischer-Tropsch wax.
References Cited (Backward Citations)
US3884786A
Cited
US4146521A
Cited
US4500661A
Cited
US4167433A
Cited
US4404299A
Cited
US4434261A
Cited
US4460728A
Cited
US4631308A
Cited
US4471086A
Cited
US4567223A
Cited
US4752634A
Cited
US4816306A
Cited
US4874804A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-07-18 | 1998-01-17 | 1998-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-07-18 | 2002-01-17 | 2002-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-07-18 | 2006-01-17 | 2006-07-19 | $7700.00 | Window Closed / Lapsed |