Pressure-sensitive crayon adhesive

Claim 2

A solid thermoplastic and pressure-sensitive crayon adhesive consisting essentially of an intimate mixture of: A. from about 40% to 75% by weight of polyisobutylene having a Flory molecule weight of 40,000 to 70,000; B. about 25% to 60% by weight of synthetic wax having a needle penetration value of from about 1 to 6 and a melting point of at least 190° F.; and C. optionally containing up to about 30% by weight of an adhesion promoter resin for the polyisobutylene wherein said resin has a softening point above 150° F. and is a member selected from the group consisting of rosin, modified rosin, a rosin derivative, a terpene resin, a hydrogenated resin, a resin prepared from a C-5 aliphatic hydrocarbon, and a resin prepared from a mixture of a C-5 aliphatic and a C-9 aromatic hydrocarbon; and wherein the total quantity of polyisobutylene, wax, and resin make up at least 90% of the crayon.

Claim 3

The crayon of claim 1 wherein the quantity of polyisobutylene is from about 40% to 65%.

Claim 4

The crayon of claim 2 having dispersed therein from about 0.02% to 2% by weight of a fluorescent color pigment and wherein the molecular weight of the polyisobutylene is from about 45,000 to 65,000.

Claim 5

The crayon of claim 2 which contains from about 0.1% to 5% of filler.

Claim 6

The crayon of claim 2 wherein the adhesion promoter resin has a softening point of from about 175° F. to 250° F.

Claim 7

The crayon of claim 2 wherein the wax is a polyethylene having a needle penetration value of from about 1 to 6.

Claim 8

The crayon of claim 2 containing from 1% to 30% of the resin and wherein the adhesion promoter resin is a member selected from the group consisting of an aliphatic C-5 hydrocarbon resin, a polyterpene, and a rosin ester.

Claim 9

The crayon adhesive of claim 1 wherein the wax is a synthetic wax having a needle penetration value of about 1 to 6 and a melting point of about 200° F. to 250° F.

Claim 10

The crayon adhesive of claim 1 which, in the absence of colorant is white to translucent and which contains a fluorescent pigment in an amount sufficient to provide a vivid color to the crayon while the film which is transferred is clear to translucent.

Claim 11

The crayon adhesive of claim 1 wherein the wax is microcrystalline wax.

Claim 12

The crayon adhesive of claim 1 which contains from about 40% to 55% of a wax having a melting point of 190° F. to 240° F.

Claim 13

A thermoplastic and pressure-sensitive adhesive mass capable of transferring an adhesive film to a paperlike substrate by friction rubbing and consisting essentially of a substantially homogeneous mixture of: A. about 40% to 65% of polyisobutylene having a Flory molecular weight of from about 40,000 to 70,000; B. about 25% to 60% of a wax having a melting point of at least 165° F. and a needle penetration value of from about 1 to 15; and C. about 10% to 25% of an adhesion promoter resin for the polyisobutylene, said resin having a softening point of from about 176° to 248° F. and is a member selected from the group consisting of rosin, modified rosin, a rosin derivative, a terpene resin, a hydrogenated resin, a resin prepared from a C-5 aliphatic hydrocarbon, and a resin prepared from a mixture of a C-5 aliphatic hydrocarbon and a C-9 aromatic hydrocarbon; and wherein the wax has a needle penetration value of not greater than 8 when the mass contains at least 10% of the resin.

Claim 14

A thermoplastic and pressure-sensitive adhesive mass capable of transferring an adhesive film to a paperlike substrate by friction rubbing and consisting essentially of a substantially homogeneous mixture of: A. about 40% to 65% of polyisobutylene having a Flory molecular weight of from about 40,000 to 70,000; B. about 25% to 60% of a wax having a melting point of at least 165° F. and a needle penetration value of from about 1 to 15; and C. about 10% to 25% of an adhesion promoter resin for the polyisobutylene, said resin having a softening point of from about 176° to 248° F. and is a member selected from the group consisting of rosin, modified rosin, a rosin derivative, a terpene resin, a hydrogenated resin, a resin prepared from a C-5 aliphatic hydrocarbon, and a resin prepared from a mixture of a C-5 aliphatic hydrocarbon and a C-9 aromatic hydrocarbon; and wherein the wax has a needle penetration value of not greater than 8 when the mass contains at least 10% of the resin.

Claim 15

The mass of claim 12 which is sized and shaped as a crayon adhesive.

Claim 16

The crayon adhesive of claim 12 wherein the wax has a needle penetration value of from about 1 to 6 and the adhesion promoter resin is a member selected from the group consisting of an aliphatic C-5 hydrocarbon resin, a rosin ester, and a polymerized terpene.

Claim 17

The crayon adhesive of claim 14 wherein the wax is a synthetic polyolefin wax.

Claim 18

The crayon adhesive of claim 15 which includes from about 0.1% to 5% of a finely divided inert filler.

Claim 19

The crayon adhesive of claim 15 wherein, in the absence of a coloring agent, the adhesive film which is frictionally transferred from said crayon is clear.

Claim 20

The crayon adhesive of claim 17 which includes from about 0.05% to 0.3% of a fluorescent pigment wherein the pigment provides a vivid color to the crayon while the transferred adhesive film is not visible through a sheet of 16 pound yellow ruled paper.

Claim 21

The crayon adhesive of claim 17 wherein the adhesion promoter resin is an aliphatic C-5 hydrocarbon resin having a softening point of from about 194° F. to 230° F.

Claim 22

The crayon adhesive of claim 17 wherein the resin is a rosin ester having a softening point of from about 194° F. to 230° F.

Claim 23

A solid, thermoplastic, pressure-sensitive crayon adhesive having the characteristics of becoming softer and less cohesive at the area of contact and under the influence of frictional heat generated when an exposed area of the crayon is drawn rapidly in frictional contact with a smooth, dry, paperlike, surface and then being capable of transferring a thin, continuous layer of the softening adhesive to the said day surface, said crayon: A. when stored at a temperature of 140° F. for one week being (a) free from melting or deforming, and (b) free from ingredient separation and bleeding; B. having a milky white to translucent color in the absence of a coloring agent; C. being capable of transferring a clear adhesive film on said paperlike substrate and forming a fiber tearing bond after another piece of paperlike substrate is placed in contact with the transferred adhesive film and a pressure of at least 15 pounds per square inch is applied over the area of said substrates in contact with the film at room temperature for 10 seconds; and D. wherein the crayon adhesive consists essentially f a substantially homogeneous mixture of: (a) about 40% to 65% of polyisobutylene having a Flory molecular weight of about 40,000 to 70,000; (b) from about 25% to 40% of a synthetic wax having a needle penetration value of from about 1 to 6 and a melting point of at least 190° F.; and (c) from about 10% to 20% of an adhesion promoter resin for the polyisobutylene, said resin having a softening point of about 176° F. to 248° F. and is a member selected from the group consisting of rosin, modified rosin, a rosin derivative, a terpene resin, a hydrogenated resin, a resin prepared from a C-5 aliphatic hydrocarbon, and a resin prepared from a mixture of a C-5 aliphatic and C-9 aromatic hydrocarbon.

Claim 24

A solid, thermoplastic, pressure-sensitive crayon adhesive having the characteristics of becoming softer and less cohesive at the area of contact and under the influence of frictional heat generated when an exposed area of the crayon is drawn rapidly in frictional contact with a smooth, dry, paperlike, surface and then being capable of transferring a thin, continuous layer of the softening adhesive to the said day surface, said crayon: A. when stored at a temperature of 140° F. for one week being (a) free from melting or deforming, and (b) free from ingredient separation and bleeding; B. having a milky white to translucent color in the absence of a coloring agent; C. being capable of transferring a clear adhesive film on said paperlike substrate and forming a fiber tearing bond after another piece of paperlike substrate is placed in contact with the transferred adhesive film and a pressure of at least 15 pounds per square inch is applied over the area of said substrates in contact with the film at room temperature for 10 seconds; and D. wherein the crayon adhesive consists essentially f a substantially homogeneous mixture of: (a) about 40% to 65% of polyisobutylene having a Flory molecular weight of about 40,000 to 70,000; (b) from about 25% to 40% of a synthetic wax having a needle penetration value of from about 1 to 6 and a melting point of at least 190° F.; and (c) from about 10% to 20% of an adhesion promoter resin for the polyisobutylene, said resin having a softening point of about 176° F. to 248° F. and is a member selected from the group consisting of rosin, modified rosin, a rosin derivative, a terpene resin, a hydrogenated resin, a resin prepared from a C-5 aliphatic hydrocarbon, and a resin prepared from a mixture of a C-5 aliphatic and C-9 aromatic hydrocarbon.

Claim 25

The crayon adhesive of claim 21 wherein the wax is a polyethylene wax having a needle penetration value of about 1 to 2.5.

Claim 26

The crayon adhesive of claim 22 containing a from about 0.05 to 0.3% of a fluorescent pigment.

Claim 27

The crayon adhesive of claim 22 wherein the adhesion promoter resin is a member selected from the group consisting of an aliphatic C-5 hydrocarbon resin, a polyterpene, and a rosin ester, and wherein the softening point of the resin is from about 194° F. to 230° F.

Claim 28

The crayon adhesive of claim 24 wherein the resin is an aliphatic C-5 hydrocarbon resin.

Claim 29

A solid, thermoplastic, pressure-sensitive crayon adhesive, said adhesive: A. being normally tacky; B. capable of transferring a thin, smooth, and continuous layer of adhesive film to a paperlike substrate by friction rubbing on said substrate; C. forming a permanent bond after another paperlike substrate is pressed against the transferred adhesive film; and D. having a composition consisting essentially of (1) from about 40% to 75% by weight of polyisobutylene having a Flory molecular weight of 40,000 to 70,000 (2) about 25% to 60% by weight of wax having a needle penetration value of from about 1 to 15 and a melting point of at least 165° F. and (3) optionally containing up to about 30% by weight of an adhesion promoter resin for the polyisobutylene wherein said resin has a softening point above 150° F. and is a member selected from the group consisting of rosin, modified rosin, a rosin derivative, a terpene resin, a hydrogenated resin, a resin prepared from a C-5 aliphatic hydrocarbon, and a resin prepared from a mixture of a C-5 aliphatic and a C-9 aromatic hydrocarbon; and provided that the was has a needle penetration value of not greater than 8 when at least 10% of adhesion promoter resin is in the composition and wherein at least 90% of the adhesive consists of polyisobutylene, wax, and adhesion promoter resin.

Claim 30

A solid, thermoplastic, pressure-sensitive crayon adhesive, said adhesive: A. being normally tacky; B. capable of transferring a thin, smooth, and continuous layer of adhesive film to a paperlike substrate by friction rubbing on said substrate; C. forming a permanent bond after another paperlike substrate is pressed against the transferred adhesive film; and D. having a composition consisting essentially of (1) from about 40% to 75% by weight of polyisobutylene having a Flory molecular weight of 40,000 to 70,000 (2) about 25% to 60% by weight of wax having a needle penetration value of from about 1 to 15 and a melting point of at least 165° F. and (3) optionally containing up to about 30% by weight of an adhesion promoter resin for the polyisobutylene wherein said resin has a softening point above 150° F. and is a member selected from the group consisting of rosin, modified rosin, a rosin derivative, a terpene resin, a hydrogenated resin, a resin prepared from a C-5 aliphatic hydrocarbon, and a resin prepared from a mixture of a C-5 aliphatic and a C-9 aromatic hydrocarbon; and provided that the was has a needle penetration value of not greater than 8 when at least 10% of adhesion promoter resin is in the composition and wherein at least 90% of the adhesive consists of polyisobutylene, wax, and adhesion promoter resin.

Claim 31

The crayon adhesive of claim 26 which is sized and shaped to be held in the hand wherein said crayon adhesive is from about 0.25 to 0.75 inch thick, 0.25 to 1 inch wide and about 1.5 to 4 inches in length and wherein said crayon when stored at 140° F. for one week does not melt, or deform and there is no separation or bleeding of the ingredients thereof on such storage.

Claim 32

The crayon adhesive of claim 27 wherein: A. the quantity of wax varies from about 25% to 45% and has a melting point of 190° F. to 240° F.; and B. the quantity of adhesion promoter is from about 10% to 25% and wherein the adhesion promoter is a member selected from the group consisting of an aliphatic C-5 hydrocarbon resin, a polyterpene, and a rosin ester.

Claim 33

The crayon adhesive of claim 28 wherein: the adhesion promoter resin has a softening point of from about 175° F. to 250° F.; and the wax is a synthetic wax having a needle penetration value of from about 1 to 6.

Claim 34

The crayon adhesive of claim 29 wherein the wax is a polyethylene wax having a needle penetration value of about 1 to 2.5.

Claim 35

The composition of claim 1 wherein at least 95% of the composition consists of polyisobutylene, wax, and resin.