Reduction of hydrogen generation by silicone-coated optical fibers

Claim 2

A process of reducing hydrogen generation by a silicone-coated optical fiber, said process comprising: coating an optical fiber with a silicone composition; curing the silicone composition; and treating said cured, silicone-coated, optical fiber with one or more olefinic hydrocarbons under conditions effective to convert --Si--H groups in the silicone coating to --Si--R groups, wherein R is an alkyl group having the same number of carbon atoms as the one or more olefinic hydrocarbons.

Claim 3

A process according to claim 1, wherein said treating groups converts --Si--H groups to --Si--R groups to a level at which the cured silicone coating generates no more than 200 microliters of hydrogen per gram of silicone coating substantially to remove --Si--H groups completely from the silicone coating.

Claim 4

A process according to claim 1, wherein said treating is carried out int he presence of a hydrosilylation catalyst.

Claim 5

A process according to claim 3, wherein the catalyst is selected from the group consisting of platinum, rhodium, ruthenium, palladium, osmium, Lewis bases, and irridium catalysts, and mixtures thereof.

Claim 6

A process according to claim 3, wherein the catalyst is incorporated int he silicone coating of said optical fiber.

Claim 7

A process according to claim 1, wherein the one or more type of olefinic hydrocarbon has 2 to 10 carbon atoms.

Claim 8

A process according to claim 6, wherein the one or more type of olefinic hydrocarbon is ethylene.

Claim 9

A process according to claim 1, wherein said treating is carried out at a temperature of 60° to 200° C. and a pressure of 1 to 12 atmospheres.

Claim 10

A process according to claim 1, wherein said treating is under conditions effective to achieve a Shore A surface hardness of 10 to 50 in the treated, cured silicone-coated, optical fiber.

Claim 11

A process according to claim 1, wherein said cured, silicone-coated, optical fiber comprises: a core formed from a light transmissive material; an inner cladding surrounding and having a refractive index below that of said glass core; and a cured, silicone coating around said inner cladding.

Claim 12

A process according to claim 10, wherein said cured, silicone coated, optical fiber further comprises: a glass cladding between said inner glass cladding and said cured, silicone coating, wherein said outer cladding has a refractive index above that of said core and said inner cladding.

Claim 13

The product by the process of claim 7.

Claim 14

The product by the process of claim 1.

Claim 15

A process of forming a cured, silicone-coated, optical fiber with reduced hydrogen generation capability, said process comprising providing an optical fiber comprising: a core formed from a light transmissive material; an inner cladding surrounding and having a refractive index below that of said glass core; and a cured, silicone coating around said inner cladding, and treating said cured, silicone-coated, optical fiber with ethylene at a temperature of 85° to 125° C. and at a pressure of 2 to 12 atmospheres in the presence of a platinum catalyst to convert --Si--H groups in the silicone coating to --Si--CH 2 CH 3 groups, whereby said silicone coating generates no more than 200 microliters of hydrogen per gram of silicone coating substantially to remove --Si--H groups completely from the silicone coating.

Claim 16

A process of forming a cured, silicone-coated, optical fiber with reduced hydrogen generation capability, said process comprising providing an optical fiber comprising: a core formed from a light transmissive material; an inner cladding surrounding and having a refractive index below that of said glass core; and a cured, silicone coating around said inner cladding, and treating said cured, silicone-coated, optical fiber with ethylene at a temperature of 85° to 125° C. and at a pressure of 2 to 12 atmospheres in the presence of a platinum catalyst to convert --Si--H groups in the silicone coating to --Si--CH 2 CH 3 groups, whereby said silicone coating generates no more than 200 microliters of hydrogen per gram of silicone coating substantially to remove --Si--H groups completely from the silicone coating.

Claim 17

A process according to claim 14, wherein said optical fiber further comprises: an outer cladding between said inner cladding and said cured silicone coating, wherein said outer cladding has a refractive index above that of said core and said inner cladding.