Method for making a pultruded panel
Assignee: Owens Corning Fiberglas Technology Inc
•
Filing: 1991-11-18
•
Granted: 1994-02-15
•
Expires: 2011-11-18
Abstract
Abstract A method for continuously manufacturing a composite sandwich structure by pultrusion through a pultrusion die comprises arranging fiber reinforcement materials on the surface of a preformed foam core, applying liquid resin to the reinforcement materials on the surface of the foam core, heating the surface region of the foam core to a temperature of at least 100° C. to convert water in the foam core to steam, thereby causing water vapor pressure expansion of the foam, and using the expansion of the foam core to subject the liquid resin to increased pressure.
Inventors
- 👤 Ralph D. McGrath
- 👤 J. Gordon Murphy
- 👤 Peter R. Mitchell
- 👤 Christian C. Koppernaes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 10:05
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/50; B29C70/52; B29C70/523
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
153 words
A method of continuously manufacturing a composite sandwich structure by pultrusion through a pultrusion die comprising: arranging fiber reinforcement materials on the surface of a preformed closed cell foam core having a bursting pressure greater than about 10 psi (69 kPa); moving the foam core through the pultrusion die; applying liquid resin to the reinforcement materials on the surface of the foam core; heating the surface region of the foam core to a temperature of at least 100° C. to convert water in the foam core to steam, thereby causing water vapor pressure expansion of the foam core and rupture of the foam cells on the surface of the foam core; constraining the liquid resin so that the expansion of the foam core subjects the liquid resin to increased pressure, thereby forcing the liquid resin to penetrate and wet the reinforcement materials and to partially penetrate the foam core; and, curing the resin.
Claim 2
Independent Claim
153 words
A method of continuously manufacturing a composite sandwich structure by pultrusion through a pultrusion die comprising: arranging fiber reinforcement materials on the surface of a preformed closed cell foam core having a bursting pressure greater than about 10 psi (69 kPa); moving the foam core through the pultrusion die; applying liquid resin to the reinforcement materials on the surface of the foam core; heating the surface region of the foam core to a temperature of at least 100° C. to convert water in the foam core to steam, thereby causing water vapor pressure expansion of the foam core and rupture of the foam cells on the surface of the foam core; constraining the liquid resin so that the expansion of the foam core subjects the liquid resin to increased pressure, thereby forcing the liquid resin to penetrate and wet the reinforcement materials and to partially penetrate the foam core; and, curing the resin.
Claim 3
Dependent Claim
32 words
The method of claim 1 in which the expansion of the foam core causes the liquid resin to be subjected to an apparent laminate pressure of at least 10 psi (69 kPa).
Claim 4
Dependent Claim
37 words
The method of claim 2 in which the expansion of the foam core causes the liquid resin to be subjected to an apparent laminate pressure averaging at least 10 psi (69 kPa) while the resin is curing.
Claim 5
Dependent Claim
14 words
The method of claim 2 in which the foam core is a phenolic foam.
Claim 6
Dependent Claim
27 words
The method of claim 4 in which the foam core has an overall density within the range of from about 28 to about 100 kg/m 3 .
Claim 7
Dependent Claim
14 words
The method of claim 5 in which the liquid resin is a phenolic resin.
Claim 8
Dependent Claim
24 words
The method of claim 6 in which the surface region of the foam core is heated to a temperature of at least 150° C.
Claim 9
Dependent Claim
28 words
The method of claim 1 in which the surface region of the foam core is heated to a temperature at least equal to the saturation temperature for water.
Claim 10
Independent Claim
181 words
A method of continuously manufacturing a composite sandwich structure by pultrusion through a pultrusion die comprising: arranging the fiber reinforcement materials on the surface of a preformed closed cell foam core having a bursting pressure greater than about 10 psi (69 kPa); moving the foam core through the pultrusion die; applying liquid resin to the reinforcement materials on the surface of the foam core; heating the surface region of the foam core to a temperature of at least 100° C. to convert water in the surface region of the foam core to steam, thereby causing water vapor pressure expansion of the foam core and rupture of the foam cells on the surface of the foam core; constraining the liquid resin so that the expansion of the foam core subjects the liquid resin to increased pressure, thereby forcing the liquid resin to penetrate and wet the reinforcement materials and to partially penetrate the foam core; curing the resin; and cooling the surface of the foam core to a temperature below 100° C. while the composite sandwich is still constrained by the die.
Claim 11
Independent Claim
181 words
A method of continuously manufacturing a composite sandwich structure by pultrusion through a pultrusion die comprising: arranging the fiber reinforcement materials on the surface of a preformed closed cell foam core having a bursting pressure greater than about 10 psi (69 kPa); moving the foam core through the pultrusion die; applying liquid resin to the reinforcement materials on the surface of the foam core; heating the surface region of the foam core to a temperature of at least 100° C. to convert water in the surface region of the foam core to steam, thereby causing water vapor pressure expansion of the foam core and rupture of the foam cells on the surface of the foam core; constraining the liquid resin so that the expansion of the foam core subjects the liquid resin to increased pressure, thereby forcing the liquid resin to penetrate and wet the reinforcement materials and to partially penetrate the foam core; curing the resin; and cooling the surface of the foam core to a temperature below 100° C. while the composite sandwich is still constrained by the die.
Claim 12
Dependent Claim
32 words
The method of claim 9 in which the expansion of the foam core causes the liquid resin to be subjected to an apparent laminate pressure of at least 10 psi (69 kPa).
Claim 13
Dependent Claim
37 words
The method of claim 10 in which the expansion of the foam core causes the liquid resin to be subjected to an apparent laminate pressure averaging at least 10 psi (69 kPa) while the resin is curing.
Claim 14
Dependent Claim
14 words
The method of claim 9 in which the foam core is a phenolic foam.
Claim 15
Dependent Claim
28 words
The method of claim 12 in which the foam core has an overall aged density within the range of from about 28 to about 100 kg/m 3 .
Claim 16
Dependent Claim
21 words
The method of claim 13 in which the foam core has a compressive strength greater than about 10 psi (69 kPa).
Claim 17
Dependent Claim
14 words
The method of claim 14 in which the liquid resin is a phenolic resin.
Claim 18
Dependent Claim
52 words
The method of claim 15 in which the surface region of the foam core is heated to a temperature of at least 150° C., and the cooling step cools the surface region of the foam core to a temperature below 100° C. while the composite sandwich is still constrained by the die.
Claim 19
Dependent Claim
54 words
The method of claim 9 in which the surface region of the foam core is heated to a temperature equal to the saturation temperature of water in the foam core, and the cooling step cools the foam core to a temperature below 100° C. while the composite sandwich is still constrained by the die.
Claim 20
Independent Claim
183 words
A method of continuously manufacturing a composite sandwich structure by pultrusion through a pultrusion die comprising: arranging fiber reinforcement materials on the surface of a preformed closed cell foam core having a bursting pressure greater than about 10 psi (69 kPa); moving the foam core through the pultrusion die; applying liquid resin to the reinforcement materials on the surface of the foam core; heating the surface region of the foam core to a temperature of at least the saturation temperature of water to convert water in the foam core to steam, thereby causing water vapor pressure expansion of the foam core and rupture of the foam cells on the surface of the foam core; constraining the liquid resin so that the expansion of the foam core subjects the liquid resin to increased pressure, thereby forcing the liquid resin to penetrate and wet the reinforcement materials and to partially penetrate the foam core; curing the resin; and, cooling the surface region of the foam core to a temperature below the saturation temperature of water while the composite sandwich is still constrained by the die.
Claim 21
Independent Claim
183 words
A method of continuously manufacturing a composite sandwich structure by pultrusion through a pultrusion die comprising: arranging fiber reinforcement materials on the surface of a preformed closed cell foam core having a bursting pressure greater than about 10 psi (69 kPa); moving the foam core through the pultrusion die; applying liquid resin to the reinforcement materials on the surface of the foam core; heating the surface region of the foam core to a temperature of at least the saturation temperature of water to convert water in the foam core to steam, thereby causing water vapor pressure expansion of the foam core and rupture of the foam cells on the surface of the foam core; constraining the liquid resin so that the expansion of the foam core subjects the liquid resin to increased pressure, thereby forcing the liquid resin to penetrate and wet the reinforcement materials and to partially penetrate the foam core; curing the resin; and, cooling the surface region of the foam core to a temperature below the saturation temperature of water while the composite sandwich is still constrained by the die.
References Cited (Backward Citations)
US3157204A
Cited
US3736210A
Cited
US3915783A
Cited
US4042746A
Cited
CA1113673A
Cited
CA1141640A
Cited
CA1262858A
Cited
US4585683A
Cited
US5120380A
Cited
US4880893A
Cited
US5112663A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-02-14 | 1997-08-16 | 1998-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-02-14 | 2001-08-16 | 2002-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-02-14 | 2005-08-16 | 2006-02-15 | $7700.00 | Window Closed / Lapsed |