Golf ball and process for producing the same

Claim 2

A golf ball comprising a core and a cover for covering the core, said cover containing an ionomer resin as a main material, said ionomer resin having the first peak at 85° to 95° C. and the second peak at 70° to 80° C. in its crystal melting behavior attended with the measurement by a differential scanning calorimeter when the resin is heated from -30° C. to 150° C. at a heating rate of 10° C./minute, the ionomer resin being obtained by subjecting an ionic ethylene copolymer composed of three components of α-olefin, α, β-ethylenic unsaturated carboxylic acid, and α, β-ethylenic unsaturated carboxylic acid metal salt, or four components of α-olefin, α, β-ethylenic unsaturated carboxylic acid, α, β-ethylenic unsaturated carboxylic acid metal salt, and α, β-ethylenic unsaturated carboxylic acid ester to partial metal crosslinking, and wherein the ionomer resin is one of monovalent metal ions or divalent metal ions as metal ions for partially neutralizing α, β-ethylenic unsaturated carboxylic acid and a degree of neutralization by the metal ions being 30 to 70% of the carboxyl group of the carboxylic acid, the acid content being 10 to 20% by weight.

Claim 3

A process for producing a golf ball, comprising the steps of providing a core and a cover for the core, the cover containing an ionomer resin as a main material, subjecting the ionomer resin for the cover which has been covered on the core to annealing treatment at 45° to 63° C. for 3 to 240 hours so that the ionomer resin has a first peak at 85° to 95° C. and a second peak at 70° to 80° C. in its crystal melting behavior attended with the measurement by a differential scanning calorimeter when the resin is heated from -30° C. to 150° C. at a heating rate of 10° C./minute, subjecting an ionic ethylene copolymer composed of three components of α-olefin, α, β-ethylenic unsaturated carboxylic acid, and α, β-ethylenic unsaturated carboxylic acid metal salt, or four components of α-olefin, α, β-ethylenic unsaturated carboxylic acid, α, β-ethylenic unsaturated carboxylic acid metal salt, and α, β-ethylenic unsaturated carboxylic acid ester to partial metal crosslinking to thereby obtain the ionomer resin, wherein the ionomer resin is one of monovalent metal ions or divalent metal ions as metal ions for partially neutralizing α, β-ethylenic unsaturated carboxylic acid and a degree of neutralization by the metal ions being 30 to 70% of the carboxyl group of the carboxylic acid, the acid content being 10 to 20% by weight.

Claim 4

A process for producing a golf ball, comprising the steps of providing a core and a cover for the core, the cover containing an ionomer resin as a main material, subjecting the ionomer resin for the cover which has been covered on the core to annealing treatment at 45° to 63° C. for 3 to 240 hours so that the ionomer resin has a first peak at 85° to 95° C. and a second peak at 70° to 80° C. in its crystal melting behavior attended with the measurement by a differential scanning calorimeter when the resin is heated from -30° C. to 150° C. at a heating rate of 10° C./minute, subjecting an ionic ethylene copolymer composed of three components of α-olefin, α, β-ethylenic unsaturated carboxylic acid, and α, β-ethylenic unsaturated carboxylic acid metal salt, or four components of α-olefin, α, β-ethylenic unsaturated carboxylic acid, α, β-ethylenic unsaturated carboxylic acid metal salt, and α, β-ethylenic unsaturated carboxylic acid ester to partial metal crosslinking to thereby obtain the ionomer resin, wherein the ionomer resin is one of monovalent metal ions or divalent metal ions as metal ions for partially neutralizing α, β-ethylenic unsaturated carboxylic acid and a degree of neutralization by the metal ions being 30 to 70% of the carboxyl group of the carboxylic acid, the acid content being 10 to 20% by weight.

Claim 5

A golf ball produced in accordance with the method of claim 2.