Method of introducing an integral thermo-bonded layer into the surface of a thermoformed substrate
Assignee: Foster Products Corp
•
Filing: 1992-09-18
•
Granted: 1993-12-07
•
Expires: 2012-09-18
Abstract
Abstract The invention relates to a process of thermoforming thermoplastic substrates. More particularly the method of the invention relates to a method of thermoforming thermoplastic substrates wherein an integral coating is formed on the thermoplastic substrate that is resistant to removal of the coating. The novel coating method of the invention produces coated thermoplastic substrates wherein the coating is intimately bonded to the substrate. The coated substrates are hard, abrasion resistant, mold resistant, chemically resistant, and solvent resistant. The coating composition employs in a solvent base a pigment and a thermoplastic material compatible with the to be coated thermoplastic substrate. The thermoplastic material in cooperation with the pigment, solvent and other components of the coating composition after coating on the thermoplastic substrate, are heated to a thermoforming temperature and the thermoplastic material is intimately fused to the thermoplastic substrate surface.
Inventors
- 👤 Vernon H. Batdorf
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:52
CPC Classifications
B; B05; B05D; B05D3/00; B05D3/02; B05D3/0254; B05D3/12; B05D7/00; B05D7/02; B29; B29C; B29C51/00; B29C51/002; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/046; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/256; Y10T428/31504; Y10T428/31536; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/31917; Y10T428/3192; Y10T428/31931; Y10T428/31935
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
125 words
A method of thermoforming a thermoplastic substrate, with the simultaneous formation of an integral coating on a surface of said thermoplastic substrate, which method comprises the steps of: (a) applying to said surface of said thermoplastic substrate a pigmented thermoplastic polymeric coating composition comprising: (i) a compatible thermoplastic polymer compatible with said thermoplastic substrate; (ii) a pigment; and (ii) a major proportion of a solvent; wherein said coating composition forms a solvent-free discrete coating on said thermoplastic substrate; and (b) heating the coated thermoplastic substrate to the thermoforming temperature of said thermoplastic substrate and said compatible thermoplastic polymer; wherein said thermoplastic substrate and said coating composition become intimately bonded and thermally fused during a thermoforming operation at the interface between said substrate and said coating.
Claim 2
Independent Claim
125 words
A method of thermoforming a thermoplastic substrate, with the simultaneous formation of an integral coating on a surface of said thermoplastic substrate, which method comprises the steps of: (a) applying to said surface of said thermoplastic substrate a pigmented thermoplastic polymeric coating composition comprising: (i) a compatible thermoplastic polymer compatible with said thermoplastic substrate; (ii) a pigment; and (ii) a major proportion of a solvent; wherein said coating composition forms a solvent-free discrete coating on said thermoplastic substrate; and (b) heating the coated thermoplastic substrate to the thermoforming temperature of said thermoplastic substrate and said compatible thermoplastic polymer; wherein said thermoplastic substrate and said coating composition become intimately bonded and thermally fused during a thermoforming operation at the interface between said substrate and said coating.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein said thermoplastic substrate comprises a vinyl polymer having a molecular weight of about 50,000-350,000.
Claim 4
Dependent Claim
22 words
The method of claim 2 wherein said thermoplastic substrate comprises a polyvinyl chloride polymer, a polymethyl methacrylate polymer, or a polystyrene polymer.
Claim 5
Dependent Claim
18 words
The method of claim 1 wherein said thermoplastic substrate comprises a copolymer of acrylonitrile, butadiene, and styrene (ABS).
Claim 6
Dependent Claim
25 words
The method of claim 1 wherein said coating composition comprises about 15-30% of a compatible thermoplastic vinyl polymer having a molecular weight of about 25,000-150,000.
Claim 7
Dependent Claim
18 words
The method of claim 5, wherein said compatible thermoplastic polymer comprises polyvinyl chloride, polymethyl methacrylate, ABS, or polystyrene.
Claim 8
Dependent Claim
23 words
The method of claim 1 wherein said compatible thermoplastic polymer of said coating composition comprises chlorinated rubber, chlorinated polyethylene, or chlorinated polyvinyl chloride.
Claim 9
Dependent Claim
26 words
The method of claim 1 wherein said pigment is present in said coating composition at a concentration of about 3-20% and is heat and light stable.
Claim 10
Dependent Claim
22 words
The method of claim 8 wherein said pigment of said coating composition comprises metal flake, organic pigment, inorganic pigment, or mixtures thereof.
Claim 11
Dependent Claim
29 words
The method of claim 1 wherein said solvent is present in said coating composition at a concentration of about 60-85% forming a true solution with said compatible thermoplastic polymer.
Claim 12
Dependent Claim
33 words
The method of claim 1 wherein said solvent of said coating composition comprises cyclohexanone, methyl ethyl ketone, methyl amyl ketone, methyl isoamyl ketone, methyl isobutyl ketone, xylene, toluene, chlorinated solvents, acetates, or dimethylformamide.
Claim 13
Dependent Claim
23 words
The method of claim 1 wherein said coating composition is curtain coated, sprayed or roll coated onto said surface of said thermoplastic substrate.
Claim 14
Dependent Claim
27 words
The method of claim 1 wherein said discrete coating has a thickness of about 1-15 mils when we and a thickness of about 0.2-4 mils when dry.
Claim 15
Dependent Claim
16 words
The method of claim 1 wherein said coating composition has a viscosity of about 70-1,000 cps.
Claim 16
Dependent Claim
24 words
The method of claim 1 wherein said coated thermoplastic substrate is heated by a process comprising radient heat rods, oven heating or microwave heating.
Claim 17
Dependent Claim
19 words
The method of claim 1 wherein said coated thermoplastic substrate is heated to a temperature of about 200°-720° F.
Claim 18
Dependent Claim
19 words
The method of claim 1 wherein said coated thermoplastic substrate is heated to a temperature of about 260°-30020 F.
Claim 19
Independent Claim
130 words
A method of thermoforming a polyvinyl chloride substrate, with the simultaneous formation of an integral coating on a surface of said polyvinyl chloride substrate, said method comprising the steps of: (a) applying to said surface of said polyvinyl chloride substrate a pigmented thermoplastic polymeric coating composition comprising: (i) a thermoplastic polymer compatible with polyvinyl chloride; (ii) a pigment; and (iii) a major proportion of a solvent; wherein said coating composition forms a solvent-free discrete coating on said polyvinyl chloride substrate; and (b) heating the coated polyvinyl chloride substrate to the thermoforming temperature of said polyvinyl chloride substrate and said solvent-free coating composition; wherein said polyvinyl chloride substrate and said coating composition become intimately bonded and thermally fused during a thermoforming operation at the interface between said substrate and said coating.
Claim 20
Independent Claim
130 words
A method of thermoforming a polyvinyl chloride substrate, with the simultaneous formation of an integral coating on a surface of said polyvinyl chloride substrate, said method comprising the steps of: (a) applying to said surface of said polyvinyl chloride substrate a pigmented thermoplastic polymeric coating composition comprising: (i) a thermoplastic polymer compatible with polyvinyl chloride; (ii) a pigment; and (iii) a major proportion of a solvent; wherein said coating composition forms a solvent-free discrete coating on said polyvinyl chloride substrate; and (b) heating the coated polyvinyl chloride substrate to the thermoforming temperature of said polyvinyl chloride substrate and said solvent-free coating composition; wherein said polyvinyl chloride substrate and said coating composition become intimately bonded and thermally fused during a thermoforming operation at the interface between said substrate and said coating.
Claim 21
Dependent Claim
17 words
The method of claim 18 wherein said polyvinyl chloride substrate has a molecular weight of about 50,000-350,000.
Claim 22
Dependent Claim
29 words
The method of claim 18 wherein said thermoplastic polymer of said coating composition is present at a concentration of about 15-30% and has a molecular weight of about 25,000-150,000.
Claim 23
Dependent Claim
25 words
The method of claim 18 wherein said thermoplastic polymer of said coating composition comprises polyvinyl chloride, chlorinated polyvinyl chloride, chlorinated rubber, chlorinated polyethylene, or acrylic.
Claim 24
Dependent Claim
26 words
The method of claim 18 wherein said pigment is present in said coating composition at a concentration of about 3-20% and is heat and light stable.
Claim 25
Dependent Claim
22 words
The method of claim 22 wherein said pigment of said coating composition comprises metal flake, organic pigment, inorganic pigment, or mixtures thereof.
Claim 26
Dependent Claim
30 words
The method of claim 18 wherein said solvent is present in said coating composition at a concentration of about 60 to 85% forming a true solution with said thermoplastic polymer.
Claim 27
Dependent Claim
33 words
The method of claim 24 wherein said solvent of said coating composition comprises cyclohexanone, methyl ethyl ketone, methyl amyl ketone, methyl isoamyl ketone, methyl isobutyl ketone, xylene, toluene, chlorinated solvents, acetates, or dimethylformamide.
Claim 28
Dependent Claim
24 words
The method of claim 18 wherein said coating composition is curtain coated, sprayed or roll coated onto said surface of said polyvinyl chloride substrate.
Claim 29
Dependent Claim
27 words
The method of claim 18 wherein said discrete coating has a thickness of about 1-15 mils when wet and a thickness of about 0.2-4 mils when dry.
Claim 30
Dependent Claim
16 words
The method of claim 18 wherein said coating composition has a viscosity of about 70-1,000 cps.
Claim 31
Dependent Claim
20 words
The method of claim 18 wherein said coated polyvinyl chloride substrate is heated to a temperature of about 260°-300° F.
References Cited (Backward Citations)
US3793106A
Cited
US3798096A
Cited
US3788961A
Cited
US3839129A
Cited
US3960181A
Cited
US3864147A
Cited
US4093683A
Cited
US3868343A
Cited
US3935346A
Cited
US4361457A
Cited
US4139026A
Cited
US4350739A
Cited
US4336309A
Cited
US4422996A
Cited
US4356230A
Cited
US4463780A
Cited
US4603057A
Cited
US4474725A
Cited
US4553308A
Cited
US4737390A
Cited
US4708887A
Cited
US4936936A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-12-06 | 1997-06-07 | 1997-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-12-06 | 2001-06-07 | 2001-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-12-06 | 2005-06-07 | 2005-12-07 | $7700.00 | Window Closed / Lapsed |