Coated plastic substrates for coating compositions

Claim 1

A method for providing a solid organic polymeric surface with a hard, strongly adhered, abrasionresistant, mar-resistant, chemically resistant, acetone-resistant, coating wherein a thermosettable resin system is cured in a short time, said method comprising the steps of: 1. applying onto said polymeric substrate an organic solvent solution of a coating composition prepared by a method which comprises: a. heating methyltrialkoxysilane, wherein the alkoxy group contains between one and six carbon atoms, with between about 1.5 moles to about 10 moles of water per mole of total silane in the presence of an effective catalyzing amount of a acid hydrolysis catalyst between about 40°C. up to and including the reflux temperature for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, b. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, c. precuring the resultant product by heating below the gel point thereof to remove volatiles and produce a solvent-soluble, further-curable organopolysiloxane, and d. adding in an amount, of between about 3% to about 15% by weight based on organopolysiloxane solids, an alkylated melamine-formaldehyde partial condensate resin to said solvent-soluble, further-curable organopolysiloxane, said alkylated resin being a methylated and C 2 -C 4 alkylated resin wherein the molar ratio of methylation to C 2 -C 4 alkylation is at least 1:1 and wherein said resin, based on a 66-67 weight percent solution in a 1:1 weight mixture of isobutanol to isopropanol has a hydrocarbon tolerance of about 20-200 and a water tolerance of about at least 300, and 2. evaporating said solvent, and heating said substrate at a temperature and for a time sufficient to thermoset the residual coating composition and form a hard, mar-resistant, abrasion-resistant, chemically resistant, acetone-resistant, strongly adhered coating consisting essentially of the heat cured product of an organopolysiloxane and a methylated and lower alkylated melamine-formaldehyde resin, on said substrate.

Claim 2

A method for providing a solid organic polymeric surface with a hard, strongly adhered, abrasionresistant, mar-resistant, chemically resistant, acetone-resistant, coating wherein a thermosettable resin system is cured in a short time, said method comprising the steps of: 1. applying onto said polymeric substrate an organic solvent solution of a coating composition prepared by a method which comprises: a. heating methyltrialkoxysilane, wherein the alkoxy group contains between one and six carbon atoms, with between about 1.5 moles to about 10 moles of water per mole of total silane in the presence of an effective catalyzing amount of a acid hydrolysis catalyst between about 40°C. up to and including the reflux temperature for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, b. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, c. precuring the resultant product by heating below the gel point thereof to remove volatiles and produce a solvent-soluble, further-curable organopolysiloxane, and d. adding in an amount, of between about 3% to about 15% by weight based on organopolysiloxane solids, an alkylated melamine-formaldehyde partial condensate resin to said solvent-soluble, further-curable organopolysiloxane, said alkylated resin being a methylated and C 2 -C 4 alkylated resin wherein the molar ratio of methylation to C 2 -C 4 alkylation is at least 1:1 and wherein said resin, based on a 66-67 weight percent solution in a 1:1 weight mixture of isobutanol to isopropanol has a hydrocarbon tolerance of about 20-200 and a water tolerance of about at least 300, and 2. evaporating said solvent, and heating said substrate at a temperature and for a time sufficient to thermoset the residual coating composition and form a hard, mar-resistant, abrasion-resistant, chemically resistant, acetone-resistant, strongly adhered coating consisting essentially of the heat cured product of an organopolysiloxane and a methylated and lower alkylated melamine-formaldehyde resin, on said substrate.

Claim 9

A method of forming a hard, abrasion-resistant, strongly adhered, mar-resistant, chemically resistant, acetone-resistant coating on solid organic polymeric substrates which comprises: 1. applying onto said polymeric substrate an organic solvent solution of a coating composition prepared by a process which comprises: a. heating methyltrialkoxysilane, wherein the alkoxy group contains between 1 and 6 carbon atoms, with between about 1.5 and 10 moles of water per mole of total silane in the presence of an effective catalyzing amount of a acid hydrolysis catalyst between about 40°C. up to and including the reflux temperature for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, b. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, c. adding an alkylated, melamine-formaldehyde partial condensate resin to said solution of step (b), in an amount of between about 3% to about 15% by weight based on organopoly-siloxane solids, said alkylated resin being a methylated and C 2 - C 4 alkylated resin wherein the molar ratio of methylation to C 2 - C 4 alkylation is at least 1:1 and wherein said resin, based on a 66-67 weight percent solution in a 1:1 weight mixture of isobutanol to isopropanol has a hydrocarbon tolerance of about 20-200 and a water tolerance of about at least 300, and

Claim 10

A method of forming a hard, abrasion-resistant, strongly adhered, mar-resistant, chemically resistant, acetone-resistant coating on solid organic polymeric substrates which comprises: 1. applying onto said polymeric substrate an organic solvent solution of a coating composition prepared by a process which comprises: a. heating methyltrialkoxysilane, wherein the alkoxy group contains between 1 and 6 carbon atoms, with between about 1.5 and 10 moles of water per mole of total silane in the presence of an effective catalyzing amount of a acid hydrolysis catalyst between about 40°C. up to and including the reflux temperature for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, b. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, c. adding an alkylated, melamine-formaldehyde partial condensate resin to said solution of step (b), in an amount of between about 3% to about 15% by weight based on organopoly-siloxane solids, said alkylated resin being a methylated and C 2 - C 4 alkylated resin wherein the molar ratio of methylation to C 2 - C 4 alkylation is at least 1:1 and wherein said resin, based on a 66-67 weight percent solution in a 1:1 weight mixture of isobutanol to isopropanol has a hydrocarbon tolerance of about 20-200 and a water tolerance of about at least 300, and

Claim 18

A method for forming hard, abrasionresistant, strongly adhered, mar-resistant, acetone-resistant, chemically resistant coatings on a solid polycarbonate substrate which comprises: 1. adding in an amount of between about 3% to about 15% by weight based on organopolysiloxane solids a methylated and isobutylated melamine-formaldehyde partial condensate resin to an organic solvent solution of a hydrolyzed and partially condensed thermosettable organopolysiloxane so as to form a solution of a coating composition, said organopolysiloxane being prepared by the process consisting essentially of a. heating methyltriethoxysilane with about 1.5 to about 5 moles of water per mole of silane in the presence of an effective catalyzing amount of HCl between about 50°C. to about 90°C. for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane therein and then, b. concentrating the solution containing said hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of said organopolysiloxane, said methylation and isobutylation being in a ratio of about 2:1 - 2.5:1 and an 80% by weight solution of said resin in isobutanol having a xylene tolerance of about 275 and a viscosity at 25°C. of Z 2 - Z 5 ,

Claim 19

A method for forming hard, abrasionresistant, strongly adhered, mar-resistant, acetone-resistant, chemically resistant coatings on a solid polycarbonate substrate which comprises: 1. adding in an amount of between about 3% to about 15% by weight based on organopolysiloxane solids a methylated and isobutylated melamine-formaldehyde partial condensate resin to an organic solvent solution of a hydrolyzed and partially condensed thermosettable organopolysiloxane so as to form a solution of a coating composition, said organopolysiloxane being prepared by the process consisting essentially of a. heating methyltriethoxysilane with about 1.5 to about 5 moles of water per mole of silane in the presence of an effective catalyzing amount of HCl between about 50°C. to about 90°C. for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane therein and then, b. concentrating the solution containing said hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of said organopolysiloxane, said methylation and isobutylation being in a ratio of about 2:1 - 2.5:1 and an 80% by weight solution of said resin in isobutanol having a xylene tolerance of about 275 and a viscosity at 25°C. of Z 2 - Z 5 ,

Claim 22

A method for providing a solid polycarbonate substrate with a hard, strongly adhered, abrasion-resistant, mar-resistant, chemical-resistant, and acetone-resistant coating which comprises: 1. heating methyltrialkoxysilane, wherein the alkoxy group contains between one and six carbon atoms, with between about 1.5 to about 10 moles of water per mole of total silane, in the presence of an effective catalyzing amount of a acid hydrolysis catalyst, between about 40°C. up to and including the reflux temperature for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, 2. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, 3. adding to said solution containing said hydrolyzed and further partially condensed organopolysiloxane, in an amount of between about 3% to 15% by weight based on organopolysiloxane solids, an alkylated melamine formaldehyde partial condensate resin which is soluble in said solution, wherein alkylation is effected with methanol and a C 2 - C 4 alkanol in a mole ratio of methanol to said alkanol of at least about 1:1, 4. applying a solution of the product of step (3) onto a polycarbonate substrate, evaporating free volatiles therefrom, and heating said substrate at a temperature and for a time sufficient to thermoset the residual coating composition and form a hard, abrasion-resistant, mar-resistant, chemically resistant, acetone-resistant, strongly adhered coating consisting essentially of the heat cured product of an organopolysiloxane and a methylated and lower alkylated melamine-formaldehyde resin, on said substrate.

Claim 23

A method for providing a solid polycarbonate substrate with a hard, strongly adhered, abrasion-resistant, mar-resistant, chemical-resistant, and acetone-resistant coating which comprises: 1. heating methyltrialkoxysilane, wherein the alkoxy group contains between one and six carbon atoms, with between about 1.5 to about 10 moles of water per mole of total silane, in the presence of an effective catalyzing amount of a acid hydrolysis catalyst, between about 40°C. up to and including the reflux temperature for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, 2. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, 3. adding to said solution containing said hydrolyzed and further partially condensed organopolysiloxane, in an amount of between about 3% to 15% by weight based on organopolysiloxane solids, an alkylated melamine formaldehyde partial condensate resin which is soluble in said solution, wherein alkylation is effected with methanol and a C 2 - C 4 alkanol in a mole ratio of methanol to said alkanol of at least about 1:1, 4. applying a solution of the product of step (3) onto a polycarbonate substrate, evaporating free volatiles therefrom, and heating said substrate at a temperature and for a time sufficient to thermoset the residual coating composition and form a hard, abrasion-resistant, mar-resistant, chemically resistant, acetone-resistant, strongly adhered coating consisting essentially of the heat cured product of an organopolysiloxane and a methylated and lower alkylated melamine-formaldehyde resin, on said substrate.

Claim 24

A method for providing a solid organic polymeric surface with a hard, strongly adhered, abrasion-resistant, mar-resistant, chemically resistant, acetone-resistant coating wherein a thermosettable resin system is cured in a short time, said method comprising the steps of: 1. applying onto said polymeric substrate an organic solvent solution of a coating composition prepared by a method which comprises: a. heating methyltrialkoxysilane, wherein the alkoxy group contains between 1-6 carbon atoms, with between about 1.5 moles to about 10 moles of water per mole of total silane, in the presence of an effective catalyzing amount of a acid hydrolysis catalyst, between about 40°C. up to and including the reflux temperature for a period of about 1 to 10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, b. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, c. precuring the resultant product by heating below the gel point thereof to provide a solvent-soluble, further-curable organopolysiloxane, d. adding to said siloxane, in an amount of between about 3 to about 15% by weight based on organopolysiloxane solids, an alkylated melamine formaldehyde partial condensate resin wherein alkylation is effected with methanol and a C 2 -C 4 alkanol in a mole ratio of methanol to said alkanol of at least about 1:1,

Claim 25

A method for providing a solid organic polymeric surface with a hard, strongly adhered, abrasion-resistant, mar-resistant, chemically resistant, acetone-resistant coating wherein a thermosettable resin system is cured in a short time, said method comprising the steps of: 1. applying onto said polymeric substrate an organic solvent solution of a coating composition prepared by a method which comprises: a. heating methyltrialkoxysilane, wherein the alkoxy group contains between 1-6 carbon atoms, with between about 1.5 moles to about 10 moles of water per mole of total silane, in the presence of an effective catalyzing amount of a acid hydrolysis catalyst, between about 40°C. up to and including the reflux temperature for a period of about 1 to 10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, b. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, c. precuring the resultant product by heating below the gel point thereof to provide a solvent-soluble, further-curable organopolysiloxane, d. adding to said siloxane, in an amount of between about 3 to about 15% by weight based on organopolysiloxane solids, an alkylated melamine formaldehyde partial condensate resin wherein alkylation is effected with methanol and a C 2 -C 4 alkanol in a mole ratio of methanol to said alkanol of at least about 1:1,

Claim 28

A method of forming a hard, abrasion-resistant, strongly adhered, mar-resistant, chemically resistant, acetone-resistant coating on solid organic polymeric substrates which comprises: 1. applying onto said polymeric substrate an organic solvent solution of a coating composition prepared by a process which comprises: a. heating methyltrialkoxysilane, wherein the alkoxy group contains between one to six carbon atoms, with between about 1.5 to about 10 moles of water per mole of total silane, in the presence of an effective catalyzing amount of a acid hydrolysis catalyst, between about 40°C. up to and including the reflux temperature for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, b. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, c. adding to said solution containing said hydrolyzed and further partially condensed organopolysiloxane, in an amount of between about 3 to about 15% by weight based on organopolysiloxane solids, an alkylated melamine formaldehyde partial condensate resin which is soluble in said solution wherein alkylation is effected with methanol and a C 2 -C 4 alkanol in a mole ratio of methanol to said alkanol of at least about 1:1,

Claim 29

A method of forming a hard, abrasion-resistant, strongly adhered, mar-resistant, chemically resistant, acetone-resistant coating on solid organic polymeric substrates which comprises: 1. applying onto said polymeric substrate an organic solvent solution of a coating composition prepared by a process which comprises: a. heating methyltrialkoxysilane, wherein the alkoxy group contains between one to six carbon atoms, with between about 1.5 to about 10 moles of water per mole of total silane, in the presence of an effective catalyzing amount of a acid hydrolysis catalyst, between about 40°C. up to and including the reflux temperature for a period of about 1-10 hours so as to produce a substantially gel-free solution which contains a dissolved, hydrolyzed and partially condensed organopolysiloxane, b. concentrating the solution containing said dissolved, hydrolyzed and partially condensed organopolysiloxane by heating to remove some but not all volatile material, including alkanol by-product and some water, so as to obtain a solution of a hydrolyzed and further partially condensed organopolysiloxane, c. adding to said solution containing said hydrolyzed and further partially condensed organopolysiloxane, in an amount of between about 3 to about 15% by weight based on organopolysiloxane solids, an alkylated melamine formaldehyde partial condensate resin which is soluble in said solution wherein alkylation is effected with methanol and a C 2 -C 4 alkanol in a mole ratio of methanol to said alkanol of at least about 1:1,