Method for recycling polymeric film
Assignee: BANK OF OKLAHOMA NA
•
Filing: 1991-03-21
•
Granted: 1993-12-07
•
Expires: 2011-03-21
Abstract
Abstract A method for producing rolled plastic pellets comprising from about 5 to about 10 weight percent cellulosic fiber and less than about 10 weight percent water from mixed plastic waste comprising polymeric film.
Inventors
- 👤 Joe G. Brooks
- 👤 Billy D. Goforth
- 👤 Charles L. Goforth
- 👤 J. Douglas Brooks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 10:36
CPC Classifications
B; B03; B03B; B03B5/00; B03B5/28; B03B1/00; B03B1/04; B03B9/00; B03B9/06; B03B9/061; B29; B29B; B29B17/00; B29B17/02; D; D21; D21B; D21B1/00; D21B1/02; D21B1/026; D21B1/04; D21B1/12; D21B1/30; D21B1/32; D21B1/322; B29B2017/0213; B29B2017/0217; B29B2017/0237; B29B2017/0244; B29B2017/0286; B29B2017/0289; B29B17/04; B29B2017/0424; B29B2017/0484; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2105/00; B29K2105/06; B29K2105/065; B29K2705/00; B29K2711/00; B29K2711/12; B29K2711/14; B29L; B29L2007/00; B29L2007/008; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/52; Y02W30/62; Y02W30/64
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
133 words
A method for reclaiming polymeric film from mixed plastic waste comprising polymeric film and cellulosic fiber, said method comprising the steps of: Introducing the plastic waste into apparatus adapted to reduce the polymeric film to pieces having a maximum dimension ranging between about 1 inch and about 4 inches; Separating the polymeric film from a portion of the cellulosic fiber by passing the plastic waste through at least one wash tank; Further reducing the size of the pieces of polymeric film to pieces having a maximum dimension of about 1/2 inch; Separating the polymeric film and a further portion of the cellulosic fiber by flotation with agitation; Dewatering the polymeric film; Drying the polymeric film to a moisture content of less than about 10 weight percent; and Rolling the polymeric film into pellets.
Claim 2
Dependent Claim
22 words
The method of claim 1 wherein the plastic waste comprises from about 6 percent to about 33 percent cellulosic fiber by weight.
Claim 3
Dependent Claim
11 words
The method of claim 1 wherein the plastic waste is baled.
Claim 4
Dependent Claim
32 words
The method of claim 3 wherein the baled plastic waste is cut into sections before reducing the pieces of polymeric film to a maximum dimension between about 1 and about 4 inches.
Claim 5
Dependent Claim
14 words
The method of claim 1 wherein the plastic waste is screened prior to washing.
Claim 6
Dependent Claim
37 words
The method of claim 1 wherein the step of reducing the polymeric film to pieces having a maximum dimension between about 1 and about 4 inches includes the step of reducing the plastic waste in a shredder.
Claim 7
Dependent Claim
33 words
The method of claim 1 wherein the step of reducing the polymeric film to a maximum dimension of about 1/2 inch includes the step of reducing the maximum dimension in a wet grinder.
Claim 8
Dependent Claim
25 words
The method of claim 1 wherein the step of dewatering the polymeric film comprises the step of passing it through a screw press for dewatering.
Claim 9
Dependent Claim
23 words
The method of claim 1 wherein the dewatered polymeric film is dried to a moisture content or less than about 10 weight percent.
Claim 10
Dependent Claim
29 words
The method of claim 1 comprising the additional step of passing the dried polymeric film through a cyclone separator to remove an additional portion of the cellulosic fiber therefrom.
Claim 11
Dependent Claim
21 words
The method of claim 1 wherein the pellets comprise from about 5 percent to about 10 percent cellulosic fiber by weight.
Claim 12
Dependent Claim
17 words
The method of claim 1 wherein the pellets comprise less than about 8 percent moisture by weight.
Claim 13
Dependent Claim
13 words
The method of claim 1 wherein the polymeric film is high density polyethylene.
References Cited (Backward Citations)
CA695881A
Cited
US3284282A
Cited
GB1228276A
Cited
US4000031A
Cited
US3843060A
Cited
US4092458A
Cited
US4134544A
Cited
US4160722A
Cited
US4332748A
Cited
US4123489A
Cited
US4162768A
Cited
DE3002061A1
Cited
US4436104A
Cited
US4830219A
Cited
US4784595A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-12-06 | 1997-06-07 | 1997-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-12-06 | 2001-06-07 | 2001-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-12-06 | 2005-06-07 | 2005-12-07 | $7700.00 | Window Closed / Lapsed |