Assignee: UNITED OF AMERICA DEPARTMENT OF ENERGY, Secretary of
•
Filing: 1992-09-08
•
Granted: 1993-11-23
•
Expires: 2012-09-08
Abstract
Abstract A process for laser patterning of a substrate so that it can be subsequently electroplated or electrolessly plated. The process utilizes a laser to treat an inactive (inert) layer formed over an active layer to either combine or remove the inactive layer to produce a patterned active layer on which electrodeposition can occur. The process is carried out by utilizing laser alloying and laser etching, and involves only a few relatively high yield steps and can be performed on a very small scale.
Inventors
- 👤 Steven T. Mayer
- 👤 Leland B. Evans
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:27
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/02; C25D5/022; H; H05; H05K; H05K3/00; H05K3/10; H05K3/108; H05K2203/00; H05K2203/10; H05K2203/107; H05K3/38; H05K3/388
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
92 words
A process for forming a metallic interconnect on an electronic component having at least one layer of electrochemically active material covered by a layer of electrochemically inactive material, comprising the steps of: directing localized energy from a source onto a selected area of the layer of inactive material causing heating thereof and elimination of the inactive material only in the area of the localized heating; at least exposing the active material normally located under the selected area of the heated inactive material; and forming a metallic interconnect on the exposed active material.
Claim 2
Dependent Claim
92 words
A process for forming a metallic interconnect on an electronic component having at least one layer of electrochemically active material covered by a layer of electrochemically inactive material, comprising the steps of: directing localized energy from a source onto a selected area of the layer of inactive material causing heating thereof and elimination of the inactive material only in the area of the localized heating; at least exposing the active material normally located under the selected area of the heated inactive material; and forming a metallic interconnect on the exposed active material.
Claim 3
Dependent Claim
28 words
The process of claim 1, wherein the step of heating of the inactive material is carried out by directing localized laser energy onto the layer of inactive material.
Claim 4
Dependent Claim
28 words
The process of claim 2, wherein the step of heating is carried out during an etching operation to remove the selected area of the layer of inactive material.
Claim 5
Dependent Claim
28 words
The process of claim 1, wherein the step of heating is carried out during an etching operation to remove the selected area of the layer of inactive material.
Claim 6
Dependent Claim
46 words
The process of claim 1, additionally including the step of positioning the component within an etching environment for removing the selected area of the layer of inactive material prior to the step of directing localized energy onto a selected area of the layer of inactive material.
Claim 7
Dependent Claim
56 words
The process of claim 1, wherein the step of heating the selected area of the layer of inactive material additionally causes heating of a selected area of the layer of active material located beneath the selected area of the layer of inactive material, causing melting of both the selected areas of the inactive and active material.
Claim 8
Dependent Claim
59 words
The method of claim 1, additionally including the steps of forming at least a portion of the electronic component, comprising: forming an adhesion layer on a substrate; depositing at least one layer of conductive material constituting the active material on the substrate; and depositing on the layer of conductive material an outer layer of material constituting the inactive material.
Claim 9
Dependent Claim
28 words
The method of claim 7, wherein the step of forming the adhesion layer is carried out by depositing a layer of a tungsten containing material on the substrate.
Claim 10
Dependent Claim
20 words
The method of claim 8, wherein the tungsten containing material is selected from the group of tungsten and titanium-tungsten alloy.
Claim 11
Dependent Claim
22 words
The method of claim 7, wherein the layer of conductive material is selected from the group consisting of copper, gold and nickel.
Claim 12
Dependent Claim
22 words
The method of claim 10, wherein the outer layer is selected from the group consisting of titanium-tungsten, tungsten, chromium, and amorphous carbon.
Claim 13
Dependent Claim
21 words
The method of claim 10, wherein the outer layer is selected from the group consisting of a-Si and SiO 2 .
Claim 14
Dependent Claim
26 words
The method of claim 10, wherein the outer layer is formed from a metal which is catalytically inactive relative to the metal forming the metallic interconnect.
Claim 15
Dependent Claim
33 words
The method of claim 7, wherein the substrate is formed to include at least a surface of silicon dioxide, and the adhesion layer is formed on the silicon dioxide surface of the substrate.
Claim 16
Dependent Claim
41 words
The method of claim 7, wherein the step of heating causes melting of the selected area of the layer of conductive material and the selected area of the outer layer forming a mix thereof to which the metallic interconnect is electrodeposited.
Claim 17
Dependent Claim
42 words
The method of claim 7, wherein the step of heating is carried out in an etching environment causing removal of the selected area of the outer layer, and wherein the metallic interconnect is electrodeposited on the selected area of the conductive material.
Claim 18
Dependent Claim
39 words
The method of claim 15, wherein the adhesion layer is composed of a tungsten rich material, wherein the conductive material is composed of copper, and wherein the outer layer is selected from the group consisting of chromium and titanium.
Claim 19
Dependent Claim
41 words
The method of claim 16, wherein the adhesion layer is composed of a tungsten rich material, wherein the conductive material is composed of copper, and wherein the outer layer is selected from the group consisting of a-Si and SiO 2 .
Claim 20
Dependent Claim
46 words
The method of claim 18, wherein the etching environment utilizes an etchant selected from the group consisting of a gas from the group of Cl 2 , SF 6 and Freon, and a liquid from the group of dilute HF in water and dilute Cr etch.
Claim 21
Dependent Claim
24 words
The method of claim 19, wherein the outer layer is composed of a-Si and the etchant is composed of chlorine (Cl 2 ) gas.
Claim 22
Dependent Claim
99 words
A process for forming a metallic interconnect on an electronic component having at least one layer of electrochemically active material covered by at least one layer of electrochemically inactive material, comprising the steps of: positioning the electronic component within an etching environment; directing localized energy from a source onto a selected area of the inactive material causing heating and elimination of the inactive material only in the area of the localized heating; at least exposing the active material normally located under the selected area of the heated inactive material; and forming a metallic interconnect on the exposed active material.
Claim 23
Dependent Claim
99 words
A process for forming a metallic interconnect on an electronic component having at least one layer of electrochemically active material covered by at least one layer of electrochemically inactive material, comprising the steps of: positioning the electronic component within an etching environment; directing localized energy from a source onto a selected area of the inactive material causing heating and elimination of the inactive material only in the area of the localized heating; at least exposing the active material normally located under the selected area of the heated inactive material; and forming a metallic interconnect on the exposed active material.
Claim 24
Dependent Claim
45 words
The process of claim 21, additionally including the step of forming the inactive material from the group consisting of a metal which is catalytically inactive with respect to the material of the layer of active material on which it is deposited and an insulating material.
Claim 25
Dependent Claim
37 words
The process of claim 22, wherein the metal is selected from the group consisting of titanium, titanium-tungsten, tungsten, chromium, and amorphous carbon; and the insulating material is selected from the group of amorphous silicon and silicon oxide.
References Cited (Backward Citations)
US3506545A
Cited
US4217183A
Cited
US4448636A
Cited
US4414059A
Cited
US4626315A
Cited
US4574095A
Cited
US4701347A
Cited
US4842677A
Cited
US4897150A
Cited
US4962057A
Cited
US4983250A
Cited
US5098526A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-22 | 1997-05-24 | 1997-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-22 | 2001-05-24 | 2001-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-22 | 2005-05-24 | 2005-11-23 | $7700.00 | Window Closed / Lapsed |