Electroplated gold-copper-silver alloys
Assignee: Shipley Co Inc
•
Filing: 1992-04-15
•
Granted: 1993-10-26
•
Expires: 2012-04-15
Abstract
Abstract A solution for electroplating gold-copper-silver alloys. The solution comprises gold, copper and silver, each in the form of a cyanide complex. The solution further comprises a divalent sulfur compound capable of brightening and leveling the electroplated deposit of the gold-copper-silver alloy. Optionally, a source of cyanide ions such as a free alkali cyanide, is included in the solution. In addition, additives such as surface active agents, buffers and/or conductivity salts may also be included to impart a particular feature or characteristic to the solution. The invention additionally comprises a process for electroplating up to about 20 microns of a gold-copper-silver alloy upon a substrate utilizing these novel solutions. The alloy is deposited upon a substrate which is immersed in the solution, by electroplating at a current density of between about 1 and 15 ASF, a pH of between about 8-11 at a temperature of between about 100°-170° F. for a time sufficient to obtain the desired thickness. Improved brightness results are obtained with the process of the invention by manipulating the electroplating current.
Inventors
- 👤 William R. Brasch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 08:24
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25D3/62
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
99 words
A solution for electroplating a gold-copper-silver alloy which comprises: a soluble gold compound present as a gold cyanide complex in the solution; a soluble copper compound present as a copper cyanide complex in the solution; a soluble silver compound present as a silver cyanide complex in the solution in an amount of at least about 0.1 gm/l; and a solution soluble divalent sulfur compound of thiourea, imidazolidine-thione or thiobarbituric acid in an amount of at least about 0.075 gm/l to brighten alloys deposited by said solution during electroplating; said solution having a pH of between about 8 and 11.
Claim 2
Dependent Claim
99 words
A solution for electroplating a gold-copper-silver alloy which comprises: a soluble gold compound present as a gold cyanide complex in the solution; a soluble copper compound present as a copper cyanide complex in the solution; a soluble silver compound present as a silver cyanide complex in the solution in an amount of at least about 0.1 gm/l; and a solution soluble divalent sulfur compound of thiourea, imidazolidine-thione or thiobarbituric acid in an amount of at least about 0.075 gm/l to brighten alloys deposited by said solution during electroplating; said solution having a pH of between about 8 and 11.
Claim 3
Dependent Claim
18 words
The solution of claim 1 wherein the concentration of gold ranges between about 1-12 gm/l. as gold metal.
Claim 4
Dependent Claim
18 words
The solution of claim 1 wherein the concentration of copper ranges between about 5-50 gm/l. as copper metal.
Claim 5
Dependent Claim
26 words
The solution of claim 1 wherein the concentration of silver ranges between about 01.-1 gm/l. as silver metal, and the solution is substantially free of cadmium.
Claim 6
Dependent Claim
13 words
The solution of claim 1 which further comprises a source of cyanide ions.
Claim 7
Dependent Claim
16 words
The solution of claim 5 wherein said source of cyanide ions is a free alkali cyanide.
Claim 8
Dependent Claim
11 words
The solution of claim 6 wherein said cyanide is potassium cyanide.
Claim 9
Dependent Claim
17 words
The solution of claim 6 wherein said alkali cyanide is sodium cyanide, ammonium cyanide or mixtures thereof.
Claim 10
Dependent Claim
20 words
The solution of claim 1 wherein said divalent sulfur compound is present in a concentration of between about 0.075-1 gm/l.
Claim 11
Dependent Claim
19 words
The solution of claim 1 which further comprises from about 1-100 gm/l. of a buffer material or conductivity salt.
Claim 12
Dependent Claim
23 words
The solution of claim 10 wherein said buffer material or conductivity salt is a borate, phosphate, carbonate, bicarbonate, citrate, acetate, or mixtures thereof.
Claim 13
Dependent Claim
23 words
The solution of claim 1 which further comprises at least one surface active agent in a concentration of up to about 10 ml/l.
Claim 14
Dependent Claim
22 words
The solution of claim 12 where said surface active agent is based on fatty compounds of amine oxide, betaine, alkoxylate or phosphate.
Claim 15
Dependent Claim
16 words
The solution of claim 13 wherein said surface active agent is an ethoxylated fatty acid phosphate.
Claim 16
Dependent Claim
32 words
The solution of claim 1 wherein said gold cyanide complex is KAu(CN) 2 , said copper cyanide complex is K 2 CU(CN) 3 and said silver cyanide complex is KAg(CN) 2 .
Claim 17
Dependent Claim
142 words
A solution for electroplating a gold-copper-silver alloy consisting essentially of: a soluble gold compound present as a gold cyanide complex in the solution and being present at a concentration of between about 1-12 gm/l as gold metal; a soluble copper compound present as a copper cyanide complex in the solution and being present at a concentration of between about 5-50 gm/l as copper metal; a soluble silver compound present as a silver cyanide complex in the solution and being present at a concentration of between about 0.1-1 gm/l as silver metal; a solution soluble divalent sulfur compound, said divalent sulfur compound present at a concentration of between about 0.075-1 gm/l in said solution for brightening alloys deposited by said solution; and at least one surface active agent present in said solution, said solution having a pH of between about 8 and 11.
Claim 18
Dependent Claim
142 words
A solution for electroplating a gold-copper-silver alloy consisting essentially of: a soluble gold compound present as a gold cyanide complex in the solution and being present at a concentration of between about 1-12 gm/l as gold metal; a soluble copper compound present as a copper cyanide complex in the solution and being present at a concentration of between about 5-50 gm/l as copper metal; a soluble silver compound present as a silver cyanide complex in the solution and being present at a concentration of between about 0.1-1 gm/l as silver metal; a solution soluble divalent sulfur compound, said divalent sulfur compound present at a concentration of between about 0.075-1 gm/l in said solution for brightening alloys deposited by said solution; and at least one surface active agent present in said solution, said solution having a pH of between about 8 and 11.
Claim 19
Dependent Claim
21 words
The solution of claim 16 which further comprises an alkali cyanide compound as a source of cyanide ions for the solution.
Claim 20
Dependent Claim
19 words
The solution of claim 17 wherein said divalent sulfur compound includes a >C═S, --SH, .tbd.S═S, --S--CN or --N═C═S group.
Claim 21
Dependent Claim
16 words
The solution of claim 18 wherein said divalent sulfur compound is thiourea, imidazolidinethione, or thiobarbituric acid.
Claim 22
Dependent Claim
19 words
The solution of claim 19 which further comprises from about 1-100 gm/l. of a buffer material or conductivity salt.
Claim 23
Dependent Claim
75 words
A process for electroplating gold-copper-silver alloys which comprises: formulating the solution of claim 1 or 18; immersing a substrate at least partially into the solution; and electroplating a gold-copper-silver alloy upon the substrate at a pH of between about 8 and 11, a current density of between about 1 to 15 ASF and at a temperature of between about 100° and 170° F. for a sufficient time to deposit a sufficient thickness of the alloy.
Claim 24
Dependent Claim
21 words
The process of claim 21 wherein the electroplating step includes manipulating the current to improve brightness and leveling of the deposit.
Claim 25
Dependent Claim
144 words
A process for electroplating gold-copper-silver alloys which comprises: formulating a solution having a pH of between 8 and 11 and comprising a soluble gold compound present as a gold cyanide complex, a soluble copper compound present as a copper cyanide complex, a soluble silver compound present as a silver cyanide complex in an amount of at least about .1 gm/l, and a solution soluble divalent sulfur compound in an amount of at least about 0.075 gm/l; immersing a substrate at least partially into the solution; and electroplating a gold-copper-silver alloy upon the substrate at a current density of between about 1 to 15 ASF and at a temperature of between about 100° and 170° F. for a sufficient time with a current manipulating step which includes switching current on and off at predetermined intervals to deposit a sufficient thickness of a desired gold alloy.
Claim 26
Dependent Claim
144 words
A process for electroplating gold-copper-silver alloys which comprises: formulating a solution having a pH of between 8 and 11 and comprising a soluble gold compound present as a gold cyanide complex, a soluble copper compound present as a copper cyanide complex, a soluble silver compound present as a silver cyanide complex in an amount of at least about .1 gm/l, and a solution soluble divalent sulfur compound in an amount of at least about 0.075 gm/l; immersing a substrate at least partially into the solution; and electroplating a gold-copper-silver alloy upon the substrate at a current density of between about 1 to 15 ASF and at a temperature of between about 100° and 170° F. for a sufficient time with a current manipulating step which includes switching current on and off at predetermined intervals to deposit a sufficient thickness of a desired gold alloy.
Claim 27
Dependent Claim
28 words
The process of claim 23 wherein the current manipulating step comprises switching said current on for a time at least as long as said current is switched off.
Claim 28
Dependent Claim
30 words
The process of claim 24 wherein the current manipulating step comprises switching said current on for from about one to about four times the time said current is switched off.
Claim 29
Dependent Claim
35 words
The process of claim 23 wherein the current manipulating step comprises selecting an interval of between about 1 and 7 seconds with the current turned on, followed by one second with the current turned off.
Claim 30
Dependent Claim
31 words
The process of claim 26 wherein the current manipulating step comprises selecting intervals of about five seconds with the current turned on, followed by one second with the current turned off.
Claim 31
Dependent Claim
22 words
The process of claim 23 which further comprises agitating the solution or moving the work while electroplating to obtain optimum electroplating results.
Claim 32
Dependent Claim
25 words
The process of claim 23 which further comprises adding a free alkali cyanide to said solution to provide a source of free cyanide ions thereto.
Claim 33
Dependent Claim
37 words
The process of claim 29 which further comprises adding a copper compound to said solution which is capable of dissolving in situ and forming a complex with said free alkali cyanide to form said copper cyanide complex.
Claim 34
Dependent Claim
37 words
The process of claim 29 which further comprises adding a silver compound to said solution which is capable of dissolving in situ and forming a complex with said free alkali cyanide to form said silver cyanide complex.
Claim 35
Dependent Claim
18 words
The process of claim 23 which further comprises controlling the pH of said solution to the desired range.
Claim 36
Dependent Claim
22 words
The process of claim 23 which further comprises adding a surface active agent to said solution prior to immersing the substrate therein.
Claim 37
Dependent Claim
19 words
The process of claim 23 wherein the temperature of said solution is maintained between about 130° and 150° F.
Claim 38
Dependent Claim
17 words
The process of claim 23 wherein the current density is maintained at between 4 and 6 ASF.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-10-25 | 1997-04-26 | 1997-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-10-25 | 2001-04-26 | 2001-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-10-25 | 2005-04-26 | 2005-10-26 | $7700.00 | Window Closed / Lapsed |