Abstract The present invention relates to a novel heat treatment process, and the alloy products produced thereby. The heat treatment process includes heating an alloy at a temperature and for a time sufficient to cause crystallization, cooling the alloy at a rate greater than about 10° C. per minute, preferably greater than about 50° C. per minute, and most preferably greater than about 100° C. per minute. Alloys of many compositions and having either amorphous, surface crystallized or partially bulk crystallized structure may be beneficially treated. Alloy strips and cores heat treated according to the present invention display B-H loops which display a discontinuous change in slope at near zero field conditions. Alloy strips which have been heat treated according to the present invention display greatly increased resonant output voltages and are particularly useful as resonant markers in article surveillance systems. Cores which have been heat treated according to the present invention display constant permeabilities up to about 1 MHz and are particularly useful as EMI filters and high frequency transformers.
A process comprising the steps of: providing a metal strip of a positive magnetostrictive alloy having at least one crystallization temperature and an essentially surface crystalline phase defining a major surface of said strip and an amorphous phase contiguous with said crystalline phase and remote from said major surface; heating said metal strip to a temperature between about 70% and about 99% of the first crystallization temperature; and cooling said heated metal strip at a rate greater than about 10° C./min.
Claim 2
Dependent Claim
81 words
A process comprising the steps of: providing a metal strip of a positive magnetostrictive alloy having at least one crystallization temperature and an essentially surface crystalline phase defining a major surface of said strip and an amorphous phase contiguous with said crystalline phase and remote from said major surface; heating said metal strip to a temperature between about 70% and about 99% of the first crystallization temperature; and cooling said heated metal strip at a rate greater than about 10° C./min.
Claim 3
Dependent Claim
27 words
The process of claim 1 wherein said heat treated metal strip displays a B-H loop which has an abrupt change in slope at near zero field conditions.
Claim 4
Dependent Claim
24 words
The process of claim 1 wherein said metal strip is annealed at a temperature between about 80% and about 90% of first crystallization temperature.
Claim 5
Dependent Claim
19 words
The process of claim 1 wherein said cooling is carried out at a rate of at least 50° C./min.
Claim 6
Dependent Claim
19 words
The process of claim 1 wherein said cooling is carried out at a rate of at least 100° C./min.
Claim 7
Dependent Claim
61 words
A process comprising the steps of: providing a core comprising an annealed amorphous alloy ribbon having a surface crystalline phase and a bulk amorphous phase; heating said core to a temperature between about 70% and about 99% of a first crystallization temperature of the amorphous alloy; and cooling said heat treated core so that said core displays a pinched B-H loop.
Claim 8
Dependent Claim
61 words
A process comprising the steps of: providing a core comprising an annealed amorphous alloy ribbon having a surface crystalline phase and a bulk amorphous phase; heating said core to a temperature between about 70% and about 99% of a first crystallization temperature of the amorphous alloy; and cooling said heat treated core so that said core displays a pinched B-H loop.
Claim 9
Dependent Claim
19 words
The process of claim 6 wherein said cooling is carried out at a rate of at least 10° C./min.
Claim 10
Dependent Claim
19 words
The process of claim 6 wherein said cooling is carried out at a rate of at least 50° C./min.
Claim 11
Dependent Claim
18 words
The process of claim 6 wherein said cooling is carried out at a rate of at 100° C./min.