Method for simultaneously forming silicide and effecting dopant activation on a semiconductor wafer
Assignee: Micron Technology Inc
•
Filing: 1992-06-18
•
Granted: 1993-08-17
•
Expires: 2012-06-18
Abstract
Abstract A method for forming silicides while simultaneously activating underlying silicon substrate active regions eliminates the need for separate annealing of the active region following ion-implantation procedures. The required energy for such simultaneous processing is provided by laser irradiation directed to the surface of a wafer after blanketing it with a layer of the metal desired in the silicide.
Inventors
- 👤 Gurtej S. Sandhu
- 👤 Trung T. Doan
- 👤 Chang Yu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:00
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/21; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10P30/202; H10P30/204; H10P30/28; H10P95/00; H10P95/90
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
164 words
A method for forming silicide and effecting dopant activation in underlying ion implanted active regions of devices on a semiconductor wafer, comprising the following sequential steps: selectively fabricating a wafer by depositing and patterning different conductive and insulating layers and by ion implant doping of silicon areas to begin producing electronic devices and desired integrated circuits on the wafer, the electronic devices having exposed ion implanted silicon areas; depositing a blanketing layer of metal on the wafer in direct contact with the exposed silicon areas thereby defining metal-silicon interfaces, the blanketing metal layer covering the entirety of the wafer; exposing all areas of the blanketing layer of metal to laser irradiation at an application rate and time sufficient to produce a silicide layer at the metal-silicon interfaces while in the same laser exposing step also effecting crystal damage repair occurring as a result of the ion implantation and activation of the ion implanted dopants; and removing unreacted portions of the blanketing layer of metal.
Claim 2
Independent Claim
164 words
A method for forming silicide and effecting dopant activation in underlying ion implanted active regions of devices on a semiconductor wafer, comprising the following sequential steps: selectively fabricating a wafer by depositing and patterning different conductive and insulating layers and by ion implant doping of silicon areas to begin producing electronic devices and desired integrated circuits on the wafer, the electronic devices having exposed ion implanted silicon areas; depositing a blanketing layer of metal on the wafer in direct contact with the exposed silicon areas thereby defining metal-silicon interfaces, the blanketing metal layer covering the entirety of the wafer; exposing all areas of the blanketing layer of metal to laser irradiation at an application rate and time sufficient to produce a silicide layer at the metal-silicon interfaces while in the same laser exposing step also effecting crystal damage repair occurring as a result of the ion implantation and activation of the ion implanted dopants; and removing unreacted portions of the blanketing layer of metal.
Claim 3
Dependent Claim
12 words
The method of claim 1, wherein the metal is a transition metal.
Claim 4
Dependent Claim
10 words
The method of claim 1, wherein the metal is titanium.
Claim 5
Dependent Claim
67 words
The method of claim 1, wherein the metal thickness is 300 to 600 Angstroms, the dopant is boron implanted by ion implantation at energy levels of 20-40 KeV, the implant dose is 1.0 to 5.0×10 15 /cm 2 , and the wafer is exposed to laser irradiation at a substrate temperature of 300° to 400° C. and an optical fluence of 2.0 to 3.0 J/cm 2 .
Claim 6
Dependent Claim
67 words
The method of claim 1, wherein the metal thickness is 300 to 600 Angstroms, the dopant is phosphorous implanted by ion implantation at energy levels of 40-60 KeV, the implant dose is 1.0 to 5.0×10 15 /cm 2 , and the wafer is exposed to laser irradiation at a substrate temperature of 300° to 400° C. and an optical fluence of 2.0 to 3.0 J/cm 2 .
Claim 7
Dependent Claim
67 words
The method of claim 1, wherein the metal thickness is 300 to 600 Angstroms, the dopant is arsenic implanted by ion implantation at energy levels of 80-120 KeV, the implant dose is 1.0 to 5.0×10 15 /cm 2 , and the wafer is exposed to laser irradiation at a substrate temperature of 300° to 400° C. and an optical fluence of 2.0 to 3.0 J/cm 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-08-16 | 1997-02-15 | 1997-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-08-16 | 2001-02-15 | 2001-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-08-16 | 2005-02-15 | 2005-08-17 | $7700.00 | Window Closed / Lapsed |