Process for reclaiming thermally strained polyester scrap material
Assignee: Hoechst AG
•
Filing: 1991-10-30
•
Granted: 1993-07-06
•
Expires: 2011-10-30
Abstract
Abstract Reclaiming of polyester waste material for re-use in the production of high-quality PET plastic material comprises shredding, cleaning, sorting and postcondensing said waste materials. The shredded scrap material comprises polyester waste materials of various molecular weights and degrees of purifying. The shredded material is molten and filtered The filtered melt is either post-condensed in the molten state and then granulated or is first granulated and then subjected to a solid phase post-condensation. The granules obtained in each case are preferably fed into an extruder and extruded together with virgin raw material so as to produce a useful film or article.
Inventors
- 👤 Guenther Deiringer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 02:15
CPC Classifications
C; C08; C08J; C08J11/00; C08J11/04; C08J11/06; B; B29; B29B; B29B17/00; B29B17/0026; B29B7/00; B29B7/30; B29B7/58; B29B7/66; B29B7/80; B29B7/84; B29B7/845; B29B7/88; B29B7/885; B29B17/02; B29B17/04; B29B9/00; B29B9/16; B29B2009/165; B29B2017/0213; B29B2017/0217; B29B2017/0224; B29B7/34; B29B7/38; B29B9/02; B29B9/06; B29K; B29K2067/00; B29K2067/003; C08J2367/00; C08J2367/02; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62; Y10; Y10S; Y10S264/00; Y10S264/911; Y10S264/913; Y10S264/916; Y10S264/918; Y10S264/92
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
148 words
A process for reclaiming thermally strained polyester waste materials comprising the steps of: a) shredding a mixture of polyester waste materials, said mixture comprising polyesters of different molecular weights and different degrees of conversion, so as to form a shredded polyester mixture, b) melting said shredded mixture so as to form a molten material, c) filtering said molten material down to a particle size of about 5 to 10 microns, by removing those impurities having a particle size of equal to about 5 to 10 microns and removing those impurities having a size of greater than 5 to 10 microns, so as to produce a filtered melt, d) increasing by about 12 to about 150% as compared to the initial molecular weight of said filtered melt, the average molecular weight of said polyesters, by post-condensation, so as to produce a condensed mixture, and e) recovering said condensed mixture.
Claim 2
Dependent Claim
11 words
A process of claim 1, wherein said post-condensation comprises liquid-phase post-condensation.
Claim 3
Dependent Claim
32 words
A process of claim 2, additionally comprising the step of: f) feeding said recovered mixture to an extreuder and extruding it together with virgin polyester so as to produce an extruded article.
Claim 4
Dependent Claim
30 words
A process of claim 1, wherein said mixture of polyester waste materials comprises polyesters selected from the group consisting of polyethylene terephthalate, polytetramethylene terephthalate, poly-1,4-cyclohexylenedimethyl terephthalate, polyethylene-2,6-naphthalate, and mixtures thereof.
Claim 5
Dependent Claim
35 words
A process of claim 4, wherein said mixture of polyester waste materials consists essentially of a clean mixture of said polyesters, comprising essentially no labels, lids, coatings, dirt, adhesives, or polymers other than said polyesters.
Claim 6
Dependent Claim
21 words
A process of claim 4, wherein said mixture of polyester waste materials consists essentially of a mixture of polyethylene terephthalate polyesters
Claim 7
Dependent Claim
23 words
A process of claim 1, wherein the specific viscosity of the polyesters employed in step a) is from about 600 to about 1100.
Claim 8
Dependent Claim
30 words
A process of claim 1, wherein said step d) is performed continuously with agitation and degassing at a reduced pressure and a temperature above the melting point of said polyesters.
Claim 9
Dependent Claim
41 words
A process of claim 8, wherein said temperature is about 270 to about 310° C., wherein said pressure is about 0.5 to about 5 mbar and said step c) occurs continuously over a period of about 0.5 to about 4 hours.
Claim 10
Dependent Claim
73 words
A process of claim 9, wherein said mixture of polyester waste materials consists essentially of polyethylene terephthalate, wherein said temperature is about 280 to about 295° C., said pressure is about 1.5 to about 2 mbar, and said step d) is performed continuously over a period of about 0.5 to about 1.5 hours, wherein the specific viscosity of said polyethylene terephthalate is increased from about 800 to about 1050 during said step d).
Claim 11
Dependent Claim
73 words
A process of claim 9, wherein said mixture of polyester waste materials consists essentially of polyethylene terephthalate, wherein said temperature is about 280° to about 295° C., said pressure is about 3 to about 5 mbar, and said step d) is performed continuously over a period of about 1 to about 2 hours, wherein the specific viscosity of said polyethylene terephthalate is increased from about 800 to about 950 during said step d).
Claim 12
Dependent Claim
66 words
A process of claim 1 additionally comprising between steps c) and d) the steps of: i) solidifying said filtered melt, so as to produce a solidified mixture, ii) granulating said solidified mixture so as to produce a granulated mixture, and iii) increasing by about 30 to 150%, as compared to the initial molecular weight of said granulated mixture, the average molecular weight of said granulated mixture.
Claim 13
Dependent Claim
32 words
A process of claim 12, additionally comprising the step of: f) feeding said granulated mixture to an extruder and extruding it together with virgin polyester so as to produce an extruded article.
Claim 14
Dependent Claim
30 words
A process of claim 12, wherein said mixture of polyester waste materials comprises polyesters selected from the group consisting of polyethylene terephthalate, polytetramethylene terephthalate, poly-1,4-cyclohexylenedimethyl terephthalate, polyethylene-2,6-naphthalate, and mixtures thereof.
Claim 15
Dependent Claim
35 words
A process of claim 14, wherein said mixture of polyester waste materials consists essentially of a clean mixture of said polyesters, comprising essentially no labels, lids, coatings, dirt, adhesives, or polymers other than said polyesters.
Claim 16
Dependent Claim
21 words
A process of claim 15, wherein said mixture of polyester waste materials consists essentially of a mixture of polyethylene terephthalate polyesters.
Claim 17
Dependent Claim
23 words
A process of claim 14, wherein the specific viscosity of said mixture of polyester waste materials is from about 600 to about 1100.
Claim 18
Dependent Claim
17 words
A process of claim 12, wherein said granulated mixture comprises granules of relative uniform size and shape.
Claim 19
Dependent Claim
27 words
A process of claim 12, wherein said step d) is performed continuously in a fluidized bed apparatus, using inert gases as heat transfer agents and flushing gases.
Claim 20
Dependent Claim
11 words
A process of claim 19, wherein said inert gases comprise nitrogen.
Claim 21
Dependent Claim
53 words
A process of claim 19, wherein said polyester waste material consists essentially of polyethylene terephthalate, and during step d), the temperature is about 200° to about 250° C., and the treatment time is about 8 hours so as to increase the specific viscosity of said polyethylene terephthalate from about 800 to about 1050.
Claim 22
Dependent Claim
53 words
A process of claim 12, wherein said polyester waste material consists essentially of polyethylene terephthalate, wherein step d) is performed discontinuously, at a reduced pressure of about 0.1 mbar, over a period of about 12 hours, so as to increase the specific viscosity of said polyethylene terephthalate from about 800 to about 1050.
Claim 23
Dependent Claim
24 words
A process of claim 22, wherein step d) is performed in a tumbler drier at a temperature of about 200 to about 250° C.
Claim 24
Dependent Claim
20 words
A process of claim 12, wherein said postcondensation comprises solid phase postcondensation so as to produce a condensed, granulated mixture.
References Cited (Backward Citations)
US3389203A
Cited
DE1454875A1
Cited
US3344091A
Cited
US3585259A
Cited
US4064079A
Cited
US4092458A
Cited
JPS552031A
Cited
JPS5731529A
Cited
GB2130124A
Cited
DE3433791A1
Cited
US4756858A
Cited
US5102594A
Cited
US4958006A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-07-05 | 1997-01-04 | 1997-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-07-05 | 2001-01-04 | 2001-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-07-05 | 2005-01-04 | 2005-07-06 | $7700.00 | Window Closed / Lapsed |