Method for forming tin-indium or tin-bismuth solder connection having increased melting temperature
Assignee: Motorola Solutions Inc
•
Filing: 1992-10-05
•
Granted: 1993-06-22
•
Expires: 2012-10-05
Abstract
Abstract A solder connection (30) is formed based upon a tinindium or tin-bismuth alloy, but having a melting temperature greater than the melting temperature of the initial solder alloy. A deposit (26) of solder alloy is placed against a tin plate (24) applied, preferably by electrodeposition, to a first faying surface (18). Following assembling with a second faying surface (22), the assembly is heated to melt the solder deposit, whereupon tin from the tin plate dissolves into the solder liquid to form a tin-enriched alloy having an increased melting temperature.
Inventors
- 👤 Cynthia M. Melton
- 👤 Andrew Skipor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 00:27
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K3/3485; B; B23; B23K; B23K1/00; B23K1/0008; B23K1/0016; B23K35/00; B23K35/001; B23K35/22; B23K35/24; B23K35/26; B23K35/262; B23K35/264; H05K3/346; B23K35/02; B23K35/0222; B23K35/0244; B23K35/025; H05K2201/00; H05K2201/10; H05K2201/10613; H05K2201/10621; H05K2201/10636; H05K2201/10954; H05K2201/10992; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0723; H05K3/22; H05K3/24; H05K3/244; H05K3/341; H05K3/3431; H05K3/3442; H05K3/3473; Y; Y02; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
159 words
A soldering method for bonding a first and a second faying surface using a tin-base solder alloy, said method comprising applying a tin plate to the first faying surface, placing a solder deposit in contact with the tin plate, said solder deposit being formed of a tin alloy containing a metal selected from the group consisting of indium and bismuth and having a first melting temperature, assembling the first and second faying surfaces with the tin plate and solder deposit therebetween to form an assembly, heating the assembly to a temperature greater than the first temperature to melt the solder deposit to form a liquid phase in contact with the tin plate, whereupon tin from the tin plate dissolves into the liquid phase to form a tin-enriched alloy having a second melting temperature greater than the first melting temperature, and cooling the assembly to solidify the tin-enriched alloy to form a solder connection and thereby bond the faying surfaces.
Claim 2
Dependent Claim
159 words
A soldering method for bonding a first and a second faying surface using a tin-base solder alloy, said method comprising applying a tin plate to the first faying surface, placing a solder deposit in contact with the tin plate, said solder deposit being formed of a tin alloy containing a metal selected from the group consisting of indium and bismuth and having a first melting temperature, assembling the first and second faying surfaces with the tin plate and solder deposit therebetween to form an assembly, heating the assembly to a temperature greater than the first temperature to melt the solder deposit to form a liquid phase in contact with the tin plate, whereupon tin from the tin plate dissolves into the liquid phase to form a tin-enriched alloy having a second melting temperature greater than the first melting temperature, and cooling the assembly to solidify the tin-enriched alloy to form a solder connection and thereby bond the faying surfaces.
Claim 3
Dependent Claim
20 words
A soldering method in accordance with claim 1 wherein the solder deposit is formed of particles of said tin alloy.
Claim 4
Dependent Claim
26 words
A soldering method in accordance with claim 1 wherein the tin alloy comprises between about 55 and 65 weight percent bismuth and the balance substantially tin.
Claim 5
Dependent Claim
26 words
A soldering method in accordance with claim 1 wherein the tin alloy comprises between about 45 and 55 weight percent indium and the balance substantially tin.
Claim 6
Dependent Claim
20 words
A soldering method in accordance with claim 1 wherein the tin-enriched alloy comprises at least about 70 weight percent tin.
Claim 7
Dependent Claim
22 words
A soldering method in accordance with claim 1 wherein the liquidus temperature of the tin-enriched alloy is at least about 180° C.
Claim 8
Dependent Claim
19 words
A soldering method in accordance with claim 1 wherein the tin plate is at least about 40 microns thick.
Claim 9
Dependent Claim
217 words
A soldering method for bonding a first and a second solder-wettable faying surface using a tin-base solder alloy, said method comprising electrodepositing a tin plate to the first faying surface, said tin plate having a thickness of at least 40 microns, applying a solder paste to the tin plate, said solder paste comprising solder particles dispersed in a vaporizable vehicle and containing an expendable organic binder, said solder particles being composed of a near-eutectic tin alloy containing a metal selected from the group consisting of indium and bismuth and having a first melting temperature, drying the applied paste to from a solder deposit composed of said solder particles bonded by said expendable organic binder, assembling the second faying surface and the first faying surface to forming an assembly such that the second faying surface is in contact with the solder deposit, heating the assembly to a temperature greater than the first melting temperature to vaporize the expendable polymeric binder and to melt the solder deposit to form a liquid phase in contact with the tin plate, whereupon tin from the tin plate dissolves into the liquid phase to form a tin-enriched alloy having a second melting temperature greater than the first melting temperature, and cooling the assembly to solidify the tin-enriched alloy to form a solder joint.
Claim 10
Dependent Claim
217 words
A soldering method for bonding a first and a second solder-wettable faying surface using a tin-base solder alloy, said method comprising electrodepositing a tin plate to the first faying surface, said tin plate having a thickness of at least 40 microns, applying a solder paste to the tin plate, said solder paste comprising solder particles dispersed in a vaporizable vehicle and containing an expendable organic binder, said solder particles being composed of a near-eutectic tin alloy containing a metal selected from the group consisting of indium and bismuth and having a first melting temperature, drying the applied paste to from a solder deposit composed of said solder particles bonded by said expendable organic binder, assembling the second faying surface and the first faying surface to forming an assembly such that the second faying surface is in contact with the solder deposit, heating the assembly to a temperature greater than the first melting temperature to vaporize the expendable polymeric binder and to melt the solder deposit to form a liquid phase in contact with the tin plate, whereupon tin from the tin plate dissolves into the liquid phase to form a tin-enriched alloy having a second melting temperature greater than the first melting temperature, and cooling the assembly to solidify the tin-enriched alloy to form a solder joint.
Claim 11
Dependent Claim
20 words
A soldering method in accordance with claim 8 wherein the tin plate is between about 50 and 100 microns thick.
Claim 12
Dependent Claim
18 words
A soldering method in accordance with claim 8 wherein the solder deposit is at least 80 microns thick.
Claim 13
Dependent Claim
34 words
A soldering method in accordance with claim 8 wherein a layer of electrodeposited tin is not dissolved during heating and, following cooling, is bonded to the first faying surface and to the tin-enriched alloy.
Claim 14
Dependent Claim
20 words
A soldering method in accordance with claim 8 wherein the assembly is heated to a temperature greater than 180° C.
Claim 15
Dependent Claim
21 words
A soldering method in accordance with claims 8 wherein the assembly is heated to a temperature of at least 200° C.
Claim 16
Dependent Claim
19 words
A soldering method in accordance with claims 8 wherein the tin-enriched alloy comprises at least 70 weight percent tin.
Claim 17
Dependent Claim
226 words
A soldering method for bonding a first and second faying surface using a tin-base solder alloy, said method comprising electrodepositing a tin plate to the first faying surface, applying a solder paste to the tin plate, said solder paste comprising solder particles dispersed in vaporizable vehicle and containing an expendable organic binder, said particles being composed of a near-eutectic solder alloy selected from the group consisting of tin alloy containing between about 55 and 65 weight percent bismuth and tin alloy containing between about 45 and 55 weight percent indium. drying the applied paste to form a solder deposit having a thickness of at least 80 microns and composed of said solder particles bonded by said expendable organic binder, assembling the second faying surface and the first faying surface to form an assembly such that the second faying surface is in contact with solder deposit, heating the assembly to a temperature greater than 180° C. to vaporize the expendable organic binder and to reflow the solder deposit to form a liquid phase in contact with the tin plate, whereupon tim from the tin plate dissolves into the liquid phase to form a tin-enriched alloy containing at least 70 weight percent tin and having a liquidus temperature greater than the first melting temperature, and cooling the assembly to solidify the tin-enriched alloy to form a solder joint.
Claim 18
Dependent Claim
226 words
A soldering method for bonding a first and second faying surface using a tin-base solder alloy, said method comprising electrodepositing a tin plate to the first faying surface, applying a solder paste to the tin plate, said solder paste comprising solder particles dispersed in vaporizable vehicle and containing an expendable organic binder, said particles being composed of a near-eutectic solder alloy selected from the group consisting of tin alloy containing between about 55 and 65 weight percent bismuth and tin alloy containing between about 45 and 55 weight percent indium. drying the applied paste to form a solder deposit having a thickness of at least 80 microns and composed of said solder particles bonded by said expendable organic binder, assembling the second faying surface and the first faying surface to form an assembly such that the second faying surface is in contact with solder deposit, heating the assembly to a temperature greater than 180° C. to vaporize the expendable organic binder and to reflow the solder deposit to form a liquid phase in contact with the tin plate, whereupon tim from the tin plate dissolves into the liquid phase to form a tin-enriched alloy containing at least 70 weight percent tin and having a liquidus temperature greater than the first melting temperature, and cooling the assembly to solidify the tin-enriched alloy to form a solder joint.
Claim 19
Dependent Claim
29 words
A soldering method in accordance with claim 15 wherein a layer of electrodeposited tin remains adjacent the first faying surface following heating and is bonded to the tin-enriched alloy.
Claim 20
Dependent Claim
35 words
A soldering method in accordance with claim 15 wherein the assembly is heated to a temperature greater than about 200° C. to form a tin-enriched alloy containing between about 70 and 80 weight percent tin.
References Cited (Backward Citations)
US3292240A
Cited
US3839727A
Cited
US4746055A
Cited
US4831724A
Cited
US4950623A
Cited
US5038996A
Cited
US5062896A
Cited
US5060844A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-21 | 1996-12-21 | 1997-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-21 | 2000-12-21 | 2001-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-21 | 2004-12-21 | 2005-06-22 | $7700.00 | Window Closed / Lapsed |