Process for controlling curing and thermoforming of resins and composites
Assignee: Ineos Composites IP LLC
•
Filing: 1991-11-12
•
Granted: 1993-06-15
•
Expires: 2011-11-12
Abstract
Abstract Composite material consisting of reinforcing fibers are impregnated with polymeric matrices which may contain fillers and are then cured or thermoformed in a heating system such as an autoclave, press or oven. As the curing or thermoforming process proceeds, dielectric detection is employed to closely monitor critical process events such as the release of volatiles, chemical reactions such as cross linking, melting and solidification. Curves are generated by plotting factors of the dielectric loss of the polymer matrix versus time during the process, and these curves have a distinctive shape or signature that is characteristic of the particular polymer matrix being processed. These distinctive features or signatures have been found to correlate with critical process events, and these features are stored in a computer. During a cure cycle, the computer actuates the controls of the heating system so that the appropriate process actions or modifications will occur at the optimum time. The process controls are thereby adapted to produce an optimized, high quality product which is fairly independent of variations in raw material, preprocessing, tooling and the heating equipment.
Inventors
- 👤 L. Brian Keller
- 👤 Arturo A. Castillo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:51
CPC Classifications
B; B29; B29C; B29C35/00; B29C35/02; B29C35/0288; G; G01; G01N; G01N33/00; G01N33/44; G01N33/442; G01N2203/00; G01N2203/0058; G01N2203/0092
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
169 words
A process for curing or thermoforming a resin with a fiber fabric or filler reinforcement to form a composite, comprising: a.) measuring curing or thermoforming conditions by dielectric means applied on opposite sides and through the composite, during the cure or thermoforming process to produce a process curve for a specific resin which is correlated with physical and chemical changes in the resin; b.) comparing the process curve for the specific resin with a signature curve defining peaks, valleys, flats, rises and falls which are correlated with physical and chemical changes in the resin and fabric, the comparison being made at critical process events along the curves which are critical to the curing or thermoforming reaction; and, c.) applying reaction conditions in real time to the resin and fabric to conform the process curve with the signature curve, including the said critical process events, to form the composite, the composite having fewer voids and improved and uniform quality, and the process resulting increased yields and reduced process cycle time.
Claim 2
Dependent Claim
169 words
A process for curing or thermoforming a resin with a fiber fabric or filler reinforcement to form a composite, comprising: a.) measuring curing or thermoforming conditions by dielectric means applied on opposite sides and through the composite, during the cure or thermoforming process to produce a process curve for a specific resin which is correlated with physical and chemical changes in the resin; b.) comparing the process curve for the specific resin with a signature curve defining peaks, valleys, flats, rises and falls which are correlated with physical and chemical changes in the resin and fabric, the comparison being made at critical process events along the curves which are critical to the curing or thermoforming reaction; and, c.) applying reaction conditions in real time to the resin and fabric to conform the process curve with the signature curve, including the said critical process events, to form the composite, the composite having fewer voids and improved and uniform quality, and the process resulting increased yields and reduced process cycle time.
Claim 3
Dependent Claim
36 words
The process of claim 1, in which the physical and chemical changes in the resin and fabric are measured by differential scanning calorimetry, determined through measurement of viscosity and determined through measurement of glass transition temperature.
Claim 4
Dependent Claim
54 words
The process of claim 1, in which the reaction conditions applied include: vacuum to remove volatile solvents, venting and variations in temperature and pressure, and the critical process events include release of volatiles, the onset of reaction between initial reactants, prepolymer formation, onset and termination of cross linking, onset of melting and complete solidification.
Claim 5
Dependent Claim
16 words
The process of claim 1, in which the dielectric measurements include resistance loss and capacitance loss.
Claim 6
Dependent Claim
21 words
The process of claim 1, in which the critical process events are determined by thermal analysis, rheological analysis and dielectric measurements.
Claim 7
Dependent Claim
21 words
The process of claim 4, in which the dielectric measurements are made at a sensor frequency of about 1,000 Hz-10,000 Hz.
Claim 8
Dependent Claim
42 words
The process of claim 1, in which the said resin is selected from the group consisting of: phenolics, polyether ether ketones, polyimides, polyphenylene sulfides, polyesters, polysulfones, epoxies, polyethylene, polypropylene, nylon, bis-maleimides, PVC, polyamide-imides, urea-formaldehyde, furans, melamines, polyetherimides, ureas, polybenzimidazoles, and mixtures thereof.
Claim 9
Dependent Claim
31 words
The process of claim 7, in which the said fabric or filler reinforcement consists of: carbon black, graphite, glass fiber, quartz, SiC, aramid, metal fibers, Cu, Al, steel, or mixtures thereof.
Claim 10
Dependent Claim
22 words
The process of claim 1, in which the said process is controlled by means including computer, semi-automatic or on a manual basis.
Claim 11
Dependent Claim
19 words
The process of claim 1, in which the resin, composite and dielectric means are contained in a silicone bag.
Claim 12
Dependent Claim
19 words
The process of claim 1, in which the fabric is carbon fiber and the resin is polyether ether ketone.
Claim 13
Dependent Claim
18 words
The process of claim 1, in which the fabric is carbon fiber and the resin is a polyimide.
Claim 14
Dependent Claim
18 words
The process of claim 1, in which the fabric is carbon fiber and the resin is a phenolic.
Claim 15
Dependent Claim
18 words
The process of claim 1, in which the fabric is carbon fiber and the resin is an epoxy.
Claim 16
Dependent Claim
18 words
The process of claim 1, in which the fabric is carbon fiber and the resin is a bis-maleimide.
Claim 17
Dependent Claim
18 words
The process of claim 1, in which the fabric is carbon fiber and the resin is a polysulfone.
Claim 18
Dependent Claim
19 words
The process of claim 1, in which the fabric is carbon fiber and the resin is a polyphenylene sulfide.
Claim 19
Dependent Claim
21 words
The process of claim 9, in which the computer has a response time in the order of less than one second.
Claim 20
Dependent Claim
21 words
The process of claim 1, in which the composite is formed on a tool, and the dielectric means includes the tool.
Claim 21
Dependent Claim
173 words
A process for curing or thermoforming a resin with a fiber fabric or filler reinforcement to form a composite, comprising: a.) measuring curing or thermoforming conditions by dielectric means applied on opposite sides and through the composite, during the cure or thermoforming process to produce a process curve for a specific resin which is correlated with physical and chemical changes in the resin; b.) comparing the process curve for the specific resin with a signature curve which is characteristic of the resin or composite being processed and which is correlated with physical changes in the resin and fabric, the comparison being made at critical process events along the signature curve which are critical to the curing or thermoforming reaction; and, c.) applying reaction conditions in real time to the resin and fabric to conform the process curve with the signature curve, including the said critical process events, to form the composite, the composite having fewer voids and improved and uniform quality and the process resulting in increased yields and reduced process cycle time.
Claim 22
Dependent Claim
173 words
A process for curing or thermoforming a resin with a fiber fabric or filler reinforcement to form a composite, comprising: a.) measuring curing or thermoforming conditions by dielectric means applied on opposite sides and through the composite, during the cure or thermoforming process to produce a process curve for a specific resin which is correlated with physical and chemical changes in the resin; b.) comparing the process curve for the specific resin with a signature curve which is characteristic of the resin or composite being processed and which is correlated with physical changes in the resin and fabric, the comparison being made at critical process events along the signature curve which are critical to the curing or thermoforming reaction; and, c.) applying reaction conditions in real time to the resin and fabric to conform the process curve with the signature curve, including the said critical process events, to form the composite, the composite having fewer voids and improved and uniform quality and the process resulting in increased yields and reduced process cycle time.
Claim 23
Dependent Claim
21 words
The process of claim 20, in which the composite is formed on a tool, and the dielectric means includes the tool.
References Cited (Backward Citations)
US4373092A
Cited
US4399100A
Cited
US4515545A
Cited
US4510103A
Cited
US4551807A
Cited
US4868769A
Cited
US4773021A
Cited
US5032525A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-14 | 1996-12-14 | 1997-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-14 | 2000-12-14 | 2001-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-14 | 2004-12-14 | 2005-06-15 | $7700.00 | Window Closed / Lapsed |