Assignee: Lockheed Martin Corp
•
Filing: 1980-12-29
•
Granted: 1983-02-08
•
Expires: 2000-12-29
Abstract
Abstract A sample of polymeric composite material is cured using conventional curing methods. The optimum time during the cure cycle for applying pressure to the sample is determined by standard resin advancement measuring techniques. A dielectrometer monitoring device (15) is then attached to another material of the same type which is cured under the same conditions to develop an analog signal denoting variations in dissipation of the material. The dissipation curve characteristically has a first and second maximum value, with the latter occurring in the general vicinity of the optimum time for applying pressure for a particular frequency. Thus by changing the frequency, the dissipation is shifted along the time axis so that the second maximum coincides with the optimum time for applying pressure. The generation of a readily recognizable and repeatable feature on the analog wave form, a minimum or maximum, is a prerequisite to triggering process control functions. Thereafter, a voltage at that particular frequency is applied to other similar materials during their cure cycles to obtain a dissipation curve which has a second maximum value coinciding with the optimum pressure application point. The dielectric monitoring unit (15) is connected to a microprocessor ( 20) which determines the time at which such maximum value is reached, in response to which a command signal is sent to a pressure control system (24) connected to the microprocessor (20) for applying pressure to the material, all in an automatic, closed-loop system.
Inventors
- 👤 Andrew Zsolnay
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:48
CPC Classifications
B; B01; B01J; B01J19/00; B01J19/0006; B29; B29C; B29C35/00; B29C35/02; B29C35/0288
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
142 words
The method of curing a thermosetting polymeric material which undergoes an addition-type reaction during curing, comprising the steps of: (a) determining from a first sample of said material the optimum time for applying pressure to said material; (b) determining that frequency of an alternating current signal applied to a second sample of said material which causes a characteristic value of dissipation to occur at said optimum time; (c) applying heat to a third sample of said material to initiate curing thereof; (d) applying an alternating current signal having said determined frequency to said third sample to generate a dissipation curve, as said curing progresses, having said characteristic value at said optimum time; (e) generating a pressure application control signal when said characteristic value is reached; and (f) applying pressure to said third sample of said material in response to said control signal.
Claim 2
Independent Claim
142 words
The method of curing a thermosetting polymeric material which undergoes an addition-type reaction during curing, comprising the steps of: (a) determining from a first sample of said material the optimum time for applying pressure to said material; (b) determining that frequency of an alternating current signal applied to a second sample of said material which causes a characteristic value of dissipation to occur at said optimum time; (c) applying heat to a third sample of said material to initiate curing thereof; (d) applying an alternating current signal having said determined frequency to said third sample to generate a dissipation curve, as said curing progresses, having said characteristic value at said optimum time; (e) generating a pressure application control signal when said characteristic value is reached; and (f) applying pressure to said third sample of said material in response to said control signal.
Claim 3
Dependent Claim
42 words
The method of claim 1 wherein said step for determining the optimum time includes: (a) observing the curing of said first sample of said material; and (b) periodically testing said first sample of said material to determine the onset of gelation thereof.
Claim 4
Dependent Claim
81 words
The method of claim 1 wherein said step for determining said frequency includes: (a) applying an alternating current voltage to said second sample of said material; (b) applying heat to said second sample of said material to initiate the curing thereof; (c) measuring the dissipation of said second sample of said material during the curing thereof to determine said characteristic value thereof; and (d) changing the frequency of said alternating current voltage until said characteristic value occurs at said optimum time.
Claim 5
Dependent Claim
13 words
The method of claim 1 wherein said characteristic value is a maximum value.
Claim 6
Independent Claim
197 words
The method of curing a thermosetting polymeric material which undergoes an addition-type reaction during curing, comprising the steps of: (a) determining from a first sample of said material the optimum time for applying pressure to said material; (b) applying an alternating current signal to a second sample of said material to generate, as said second sample is being cured, a dissipation curve of said material having a characteristic value; (c) applying heat to said second sample to initiate the curing thereof; (d) varying the frequency of said alternating current signal to determine that frequency of said alternating current signal which causes said dissipation curve to shift an amount along the time axis such that said characteristic value occurs at said optimum time; (e) applying heat to a third sample of said material to initiate curing thereof; (f) applying an alternating current signal having said determined frequency to said third sample to generate said dissipation curve, as said curing progresses, having said characteristic value at said optimum time; (g) generating a pressure application control signal when said characteristic value is reached; and (h) applying pressure to said third sample of said material in response to said control signal.
Claim 7
Independent Claim
197 words
The method of curing a thermosetting polymeric material which undergoes an addition-type reaction during curing, comprising the steps of: (a) determining from a first sample of said material the optimum time for applying pressure to said material; (b) applying an alternating current signal to a second sample of said material to generate, as said second sample is being cured, a dissipation curve of said material having a characteristic value; (c) applying heat to said second sample to initiate the curing thereof; (d) varying the frequency of said alternating current signal to determine that frequency of said alternating current signal which causes said dissipation curve to shift an amount along the time axis such that said characteristic value occurs at said optimum time; (e) applying heat to a third sample of said material to initiate curing thereof; (f) applying an alternating current signal having said determined frequency to said third sample to generate said dissipation curve, as said curing progresses, having said characteristic value at said optimum time; (g) generating a pressure application control signal when said characteristic value is reached; and (h) applying pressure to said third sample of said material in response to said control signal.
Claim 8
Dependent Claim
42 words
The method of claim 5 wherein said step for determining the optimum time includes: (a) observing the curing of said first sample of said material; and (b) periodically testing said first sample of said material to determine the onset of gelation thereof.
Claim 9
Dependent Claim
13 words
The method of claim 5 wherein said characteristic value is a maximum value.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-02-07 | 1986-08-09 | 1987-02-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-02-07 | 1990-08-09 | 1991-02-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-02-07 | 1994-08-09 | 1995-02-08 | $7700.00 | Window Closed / Lapsed |