Electrolytic bath solution and method for improving the surface wear resistance of tools
Assignee: Individual
•
Filing: 1991-08-05
•
Granted: 1993-05-25
•
Expires: 2011-08-05
Abstract
Abstract In accordance with one embodiment, a method for increasing the useful working life of a tool comprises providing a bath capable of removing a surface region of an unused tool containing material near the surface under mechanical stress, immersing the tool in the bath and applying an electric potential for a time period sufficient to remove the region.
Inventors
- 👤 Norman R. Hozer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:55
CPC Classifications
C; C25; C25F; C25F1/00; C25F1/02; C25F1/04; C25F1/06
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
134 words
A method for enhancing the cutting edge of an unused steel cutting tool having complex carbide particles positioned beneath an oxide layer overlaying a region of the cutting surface of the unused cutting tool comprising the steps of: (a) providing a bath of solution capable of selectively removing the oxide layer which overlaps the cutting surface region and envelopes the complex carbide particles when said tool is immersed in said bath solution, (b) immersing said unused tool within said bath solution, and (c) applying a predetermined electrical potential between said unused tool and an electrode located within said bath solution for a time sufficient to remove the oxide layer and expose the complex carbide particles thereby increasing the abrasiveness and enhancing the ability of the cutting edge of the unused tool to cut objects.
Claim 2
Independent Claim
134 words
A method for enhancing the cutting edge of an unused steel cutting tool having complex carbide particles positioned beneath an oxide layer overlaying a region of the cutting surface of the unused cutting tool comprising the steps of: (a) providing a bath of solution capable of selectively removing the oxide layer which overlaps the cutting surface region and envelopes the complex carbide particles when said tool is immersed in said bath solution, (b) immersing said unused tool within said bath solution, and (c) applying a predetermined electrical potential between said unused tool and an electrode located within said bath solution for a time sufficient to remove the oxide layer and expose the complex carbide particles thereby increasing the abrasiveness and enhancing the ability of the cutting edge of the unused tool to cut objects.
Claim 3
Dependent Claim
36 words
The method of claim 1 in which said electrolytic bath is comprised of phosphoric acid, nickel carbonate, ferric oxide, one of group consisting of chromic acid or chromic sequesoxide, sodium thiosulfate, and alta violet basic salts.
Claim 4
Dependent Claim
19 words
The method of claim 2 in which said bath has a specific gravity of between about 1.4 and 1.57.
Claim 5
Dependent Claim
13 words
The method of claim 2 in which the bath solution includes sulfuric acid.
Claim 6
Dependent Claim
21 words
The method of claim 2 in which the phosphoric acid comprises between about 53% to 78% of the electrolytic bath solution.
Claim 7
Dependent Claim
18 words
The method of claim 2 in which the temperature of the bath is about 80° to 145° F.
Claim 8
Dependent Claim
17 words
The method of claim 2 in which the electrical potential is from about 1 to 8 volts.
Claim 9
Dependent Claim
21 words
The method of claim 6 in which the tool is immersed for a time period of 15 seconds to 60 minutes.
Claim 10
Independent Claim
103 words
A method for the pretreating the wearing surface of an unused tool comprising the steps of: (a) providing a bath of aqueous solution capable of removing a surface region of an unused tool containing material near the surface thereof under mechanical stress when said tool is immersed in the bath under an electric potential between said tool and an electrode located within said bath, (b) immersing said tool with said bath, (c) locating said tool with said bath, and (d) applying an electric potential for a time period sufficient to remove said surface region thereby exposing previously underlying regions having less mechanical stress.
Claim 11
Independent Claim
103 words
A method for the pretreating the wearing surface of an unused tool comprising the steps of: (a) providing a bath of aqueous solution capable of removing a surface region of an unused tool containing material near the surface thereof under mechanical stress when said tool is immersed in the bath under an electric potential between said tool and an electrode located within said bath, (b) immersing said tool with said bath, (c) locating said tool with said bath, and (d) applying an electric potential for a time period sufficient to remove said surface region thereby exposing previously underlying regions having less mechanical stress.
Claim 12
Dependent Claim
19 words
The method of claim 17 in which said bath has a specific gravity of between about 1.4 and 1.57.
Claim 13
Dependent Claim
13 words
The method of claim 17 in which the bath solution includes sulfuric acid.
Claim 14
Dependent Claim
21 words
The method of claim 17 in which the phosphoric acid comprises between about 53% to 78% of the electrolytic bath solution.
Claim 15
Dependent Claim
20 words
The method of claim 11 in which the temperature of the bath solution is about 80° F. to 145° F.
Claim 16
Dependent Claim
115 words
An electrolytic bath solution useful in the strengthening of a tool working surface comprising (a) a first solution portion having between about 53% to 78% by volume of phosphoric acid and added stabilizers of ferric oxide, nickel carbonate and one of a group selected from a group consisting of chromic acid and chromic sequesoxide and (b) a second solution portion added to said first solution portion in an amount between 0.5 to 1% of the volume of said first portion, said second portion comprising about 18 to 20% by volume of phosphoric acid, 80 to 82% by volume of water, about 0.1% sodium thiosulfate by weight, and a predetermined amount of alta violet basic salts.
Claim 17
Dependent Claim
115 words
An electrolytic bath solution useful in the strengthening of a tool working surface comprising (a) a first solution portion having between about 53% to 78% by volume of phosphoric acid and added stabilizers of ferric oxide, nickel carbonate and one of a group selected from a group consisting of chromic acid and chromic sequesoxide and (b) a second solution portion added to said first solution portion in an amount between 0.5 to 1% of the volume of said first portion, said second portion comprising about 18 to 20% by volume of phosphoric acid, 80 to 82% by volume of water, about 0.1% sodium thiosulfate by weight, and a predetermined amount of alta violet basic salts.
Claim 18
Dependent Claim
21 words
The solution of claim 14 in which the first portion includes sulfuric acid in an amount not exceeding 25% by volume.
Claim 19
Dependent Claim
17 words
The solution of claim 14 in which the specific gravity thereof is between about 1.4 and 1.57.
Claim 20
Independent Claim
130 words
A method for the treatment of a wearing surface of a tool comprising the steps of: (a) providing a bath of aqueous solution capable of removing a surface region of said tool containing material under stress when said tool is immersed in the bath under an electric potential between said tool and an electrode located within said bath, said bath including an aqueous solution of a phosphoric acid, ferric oxide, one of group consisting of chromic acid or chromic sequesoxide, sodium thiosulfate, and a predetermined amount of alta violet basic salts, (b) immersing said tool within said bath, and (c) applying the electrical potential between said tool and said electrode for a time period sufficient to remove said surface region thereby exposing regions of said tool having less mechanical stress.
Claim 21
Independent Claim
130 words
A method for the treatment of a wearing surface of a tool comprising the steps of: (a) providing a bath of aqueous solution capable of removing a surface region of said tool containing material under stress when said tool is immersed in the bath under an electric potential between said tool and an electrode located within said bath, said bath including an aqueous solution of a phosphoric acid, ferric oxide, one of group consisting of chromic acid or chromic sequesoxide, sodium thiosulfate, and a predetermined amount of alta violet basic salts, (b) immersing said tool within said bath, and (c) applying the electrical potential between said tool and said electrode for a time period sufficient to remove said surface region thereby exposing regions of said tool having less mechanical stress.
References Cited (Backward Citations)
US4710279A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-05-24 | 1996-11-23 | 1997-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-05-24 | 2000-11-23 | 2001-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-05-24 | 2004-11-23 | 2005-05-25 | $7700.00 | Window Closed / Lapsed |