US5207968A — Method for making a dimensionally stable green ce…

Claim 1

Independent Claim 182 words

A process for dimensionally stabilizing a green card cut from a cast sheet of frit bound together with a binder, said process comprising, (a) contacting said card with moisture at a temperature in the range from about 40° C. to about 100° C., in humidifying zone which is essentially free of a solvent for a water-soluble thermoplastic synthetic resinous component of said binder, said humidifying zone being maintained with a relatively humid atmosphere in the range from 50% relative humidity to 100% relative humidity; (b) maintaining said card in contact with said moisture for sufficient time, less than about 1 hr, to allow said moisture thoroughly to contact the card, resulting in a humidified card; and, (c) storing said humidified card in ambient atmosphere in the range from about 10° C. to about 30° C. for a period of at least 10 min, whereby upon further drying at a temperature below 200° C., said humidified card shrinks no more than 0.1 mil/inch in the direction of either lateral axis, or either diagonal axis, so as to yield a dimensionally stable green card.

Claim 2

Dependent Claim 182 words

A process for dimensionally stabilizing a green card cut from a cast sheet of frit bound together with a binder, said process comprising, (a) contacting said card with moisture at a temperature in the range from about 40° C. to about 100° C., in humidifying zone which is essentially free of a solvent for a water-soluble thermoplastic synthetic resinous component of said binder, said humidifying zone being maintained with a relatively humid atmosphere in the range from 50% relative humidity to 100% relative humidity; (b) maintaining said card in contact with said moisture for sufficient time, less than about 1 hr, to allow said moisture thoroughly to contact the card, resulting in a humidified card; and, (c) storing said humidified card in ambient atmosphere in the range from about 10° C. to about 30° C. for a period of at least 10 min, whereby upon further drying at a temperature below 200° C., said humidified card shrinks no more than 0.1 mil/inch in the direction of either lateral axis, or either diagonal axis, so as to yield a dimensionally stable green card.

Claim 3

Dependent Claim 34 words

The process of claim 1 wherein in step (a), said humid atmosphere is maintained at about 90-100% relative humidity, and in step (d) said card is stored for from 10 minutes to 8 hours.

Claim 4

Dependent Claim 30 words

The process of claim 1 comprising, before step (d) and after step (c), drying at least the surfaces of said green card, resulting in an essentially moisture free dried card.

Claim 5

Dependent Claim 38 words

The process of claim 1 wherein said binder includes a plasticizer which is soluble in water and is present in a ratio in the range from about 1.2 to 10 of resin per part by weight of plasticizer.

Claim 6

Dependent Claim 39 words

The process of claim 1 wherein said humid atmosphere is maintained at a temperature in the range from about 60° C. to about 90° C. for a period in the range from about 5 minutes to about 1 hour.

Claim 7

Dependent Claim 17 words

The process of claim 1 wherein said further drying is effected at a temperature below 100° C.

Claim 8

Dependent Claim 18 words

The process of claim 1 wherein said card is from about 2 mils to about 40 mils thick.

Claim 9

Dependent Claim 11 words

The process of claim 8 wherein said resin is polyvinyl butyral.

Claim 10

Dependent Claim 80 words

The process of claim 8 wherein said frit is selected from the group consisting of a ceramic powder and glass, said ceramic powder selected from alumina, aluminum silicate, cordierite, mullite, spinel, forsterite, barium titanate, magnesium silicate, steatite, titanium dioxide, zircon, zirconium dioxide; and said glass frit is selected from the group consisting of alumina silicate glasses, lead borate, lead silicate, borosilicate, lead borosilicate, titanium silicate cadmium borate, lead-cadmium borosilicate, zinc borosilicate and sodium-cadmium borosilicate frits, fused silica and silica glass.

Claim 11

Dependent Claim 169 words

A process for dimensionally stabilizing a green card cut from a cast sheet of frit bound together with a binder, said process comprising, (a) contacting said card in an aqueous bath which is essentially free of a solvent for a water-insoluble thermoplastic synthetic resinous component of said binder, said aqueous bath being at a temperature in the range from about 0° C. to about 95° C.; (b) maintaining said card in said bath at least until said card reaches the temperature of said bath; (c) drying said card until essentially all water from within pores of said card is removed; and, p1 (d) storing said dried card in ambient atmosphere in the range from about 10° C. to about 30° C. for a period from 30 min to 8 hr, whereby upon further drying at a temperature below 200° C., said dried card shrinks no more than 0.1 mil/inch in the direction of either lateral axis, or either diagonal axis, so as to yield a dimensionally stable green card.

Claim 12

Dependent Claim 169 words

A process for dimensionally stabilizing a green card cut from a cast sheet of frit bound together with a binder, said process comprising, (a) contacting said card in an aqueous bath which is essentially free of a solvent for a water-insoluble thermoplastic synthetic resinous component of said binder, said aqueous bath being at a temperature in the range from about 0° C. to about 95° C.; (b) maintaining said card in said bath at least until said card reaches the temperature of said bath; (c) drying said card until essentially all water from within pores of said card is removed; and, p1 (d) storing said dried card in ambient atmosphere in the range from about 10° C. to about 30° C. for a period from 30 min to 8 hr, whereby upon further drying at a temperature below 200° C., said dried card shrinks no more than 0.1 mil/inch in the direction of either lateral axis, or either diagonal axis, so as to yield a dimensionally stable green card.

Claim 13

Dependent Claim 17 words

The process of claim 10 wherein said further drying is effected at a temperature below 100° C.

Claim 14

Dependent Claim 38 words

The process of claim 10 wherein said binder includes a plasticizer which is soluble in water and is present in a ratio in the range from about 1.2 to 10 of resin per part by weight of plasticizer.

Claim 15

Dependent Claim 14 words

The process of claim 10 wherein said aqueous bath contains a plasticizer non-leaching agent.

Claim 16

Dependent Claim 142 words

A process for dimensionally stabilizing a green card cut from a cast sheet of frit bound together with a binder, comprising: (a) contacting said card with a relatively moisture free atmosphere having less than about 30% relative humidity for less than about 1 hour, at a temperature in the range from about 40° C. to about 95° C., to ensure that the card is essentially solvent free; (b) increasing the relative humidity to 100% and maintaining a temperature in the range from about 60-95° C. for sufficient time, but less than about 1 hour, to allow the water vapor to permeate the pores of the green card, resulting in a humidified green card; and (c) storing said humidified green card at storage temperature in the range from about 20° C. to 30° C. for at least 10 minutes to cool the card.

Claim 17

Dependent Claim 142 words

A process for dimensionally stabilizing a green card cut from a cast sheet of frit bound together with a binder, comprising: (a) contacting said card with a relatively moisture free atmosphere having less than about 30% relative humidity for less than about 1 hour, at a temperature in the range from about 40° C. to about 95° C., to ensure that the card is essentially solvent free; (b) increasing the relative humidity to 100% and maintaining a temperature in the range from about 60-95° C. for sufficient time, but less than about 1 hour, to allow the water vapor to permeate the pores of the green card, resulting in a humidified green card; and (c) storing said humidified green card at storage temperature in the range from about 20° C. to 30° C. for at least 10 minutes to cool the card.

Claim 18

Dependent Claim 38 words

The process of claim 14 wherein said binder includes a plasticizer which is soluble in water and is present in a ratio in the range from about 1.2 to 10 of resin per part by weight of plasticizer.

Claim 19

Dependent Claim 28 words

The process of claim 14 wherein said humid atmosphere at 100% RH is maintained for a period in the range from about 5 minutes to about 1 hour.

Claim 20

Dependent Claim 18 words

The process of claim 15 wherein said card is from about 2 mils to about 40 mils thick.

Claim 21

Dependent Claim 11 words

The process of claim 17 wherein said resin is polyvinyl butyral.

Claim 22

Dependent Claim 80 words

The process of claim 18 wherein said frit is selected from the group consisting of a ceramic powder and glass, said ceramic powder selected from alumina, aluminum silicate, cordierite, mullite, spinel, forsterite, barium titanate, magnesium silicate, steatite, titanium dioxide, zircon, zirconium dioxide; and said glass frit is selected from the group consisting of alumina silicate glasses, lead borate, lead silicate, borosilicate, lead borosilicate, titanium silicate cadmium borate, lead-cadmium borosilicate, zinc borosilicate and sodium-cadmium borosilicate frits, fused silica and silica glass.

Claim 23

Dependent Claim 66 words

The process of claim 14, comprising, after step (b) but before step (c), exhausting the moist air and replacing it with dry air so that the relative humidity drops to below 30% while maintaining said temperature in the range from about 60°-95° C., until substantially all the moisture from the surfaces and within the pores of the cards is removed resulting in a dried green card.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1996-05-03	1996-11-02	1997-05-04	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	2000-05-03	2000-11-02	2001-05-04	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2004-05-03	2004-11-02	2005-05-04	$7700.00	Window Closed / Lapsed

Method for making a dimensionally stable green ceramic sheet

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag