US5043117A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of manufacturing ceramic products, and a method of manufacturing ceramic springs
Assignee: NHK Spring Co Ltd
•
Filing: 1988-10-25
•
Granted: 1991-08-27
•
Expires: 2008-10-25
Abstract
Abstract A method of manufacturing ceramic products. This method comprises the steps of mixing ceramic powder, organic materials imparting formability to the ceramic powder, and a first solvent, thereby preparing a mixture, shaping the mixture thereby forming a product of a simple shape, drying the product, immersing the dried product in a bath of a second solvent, thereby plasticizing the product, and re-shaping the plasticized product.
Inventors
- 👤 Takaji Adachi
- 👤 Masahiko Nakatani
- 👤 Shigemi Sato
- 👤 Toyoyuki Higashino
- 👤 Suguru Nomura
- 👤 Ryusuke Adachi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:51
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/63404; C04B35/63416; C04B35/6342; C04B35/63424; C04B35/63448; C04B35/63456; C04B35/636; C04B35/6365
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
148 words
A method of manufacturing ceramic products, comprising the steps of: preparing a mixture of mixing together ceramic powder, organic materials including at least a binder and a plasticizer for imparting formability to the ceramic powder, and a first solvent; shaping the mixture, thereby forming a product of a simple shape; drying the product to remove substantially all of the first solvent from the product; immersing the dried product in a bath of a second solvent which dissolves a plasticizer contained in the product and which is a poor solvent to the binder so that is softens the binder but does not dissolve the binder, for thereby plasticizing the product; re-shaping the plasticized product into a product having a given size and shape; and drying the re-shaped product to remove second solvent therefrom whereby shrinkage of the re-shaped product is substantially negligible during the removal of the second solvent.
Claim 2
Independent Claim
148 words
A method of manufacturing ceramic products, comprising the steps of: preparing a mixture of mixing together ceramic powder, organic materials including at least a binder and a plasticizer for imparting formability to the ceramic powder, and a first solvent; shaping the mixture, thereby forming a product of a simple shape; drying the product to remove substantially all of the first solvent from the product; immersing the dried product in a bath of a second solvent which dissolves a plasticizer contained in the product and which is a poor solvent to the binder so that is softens the binder but does not dissolve the binder, for thereby plasticizing the product; re-shaping the plasticized product into a product having a given size and shape; and drying the re-shaped product to remove second solvent therefrom whereby shrinkage of the re-shaped product is substantially negligible during the removal of the second solvent.
Claim 3
Dependent Claim
24 words
The method according to claim 1, further comprising the steps of: burning organic components contained in the re-shaped product, and sintering the re-shaped product.
Claim 4
Dependent Claim
15 words
The method according to claim 1, wherein said organic materials further include a dispersing agent.
Claim 5
Dependent Claim
34 words
The method according to claim 3, wherein said binder comprises at least one element selected from the group consisting of methylcellulose, polyvinyl alcohol, water-soluble urethane, a copolymer of polymethacrylate, polyvinyl butyral, polyacrylate, and polymethacrylate.
Claim 6
Dependent Claim
41 words
The method according to claim 1, wherein said second solvent is an organic solvent selected from the group consisting of alcohol, ketone, aromatic hydrocarbon, aliphatic hydrocarbon, alycrylic hydrocarbon, chlorinated hydrocarbon, or a mixture of at least two of these organic solvents.
Claim 7
Independent Claim
147 words
A method of manufacturing a ceramic coil spring, comprising the steps of: preparing a mixture by mixing together ceramic powder, organic materials including at least a binder and a plasticizer for imparting formability to the ceramic powder, and a first solvent; extruding the mixture into a wire; drying the wire to remove substantially all of the first solvent form the extruded wire; immersing the dried wire in a bath of a second solvent which dissolves a plasticizer contained in the wire and which is a poor solvent to the binder so that is softens the binder but does not dissolve the binder, for thereby plasticizing the wire; coiling the plasticized wire by winding the plasticized wire around a core rod; drying the wire as it is wound around the core rod to remove second solvent therefrom; and then removing the coil-shaped dried wire from the core rod.
Claim 8
Independent Claim
147 words
A method of manufacturing a ceramic coil spring, comprising the steps of: preparing a mixture by mixing together ceramic powder, organic materials including at least a binder and a plasticizer for imparting formability to the ceramic powder, and a first solvent; extruding the mixture into a wire; drying the wire to remove substantially all of the first solvent form the extruded wire; immersing the dried wire in a bath of a second solvent which dissolves a plasticizer contained in the wire and which is a poor solvent to the binder so that is softens the binder but does not dissolve the binder, for thereby plasticizing the wire; coiling the plasticized wire by winding the plasticized wire around a core rod; drying the wire as it is wound around the core rod to remove second solvent therefrom; and then removing the coil-shaped dried wire from the core rod.
Claim 9
Dependent Claim
26 words
The method according to claim 6, further comprising the steps of: burning organic compounds contained in the coil-shaped dried wire, and sintering the coil-shaped dried wire.
Claim 10
Dependent Claim
15 words
The method according to claim 6, wherein said organic materials further include a dispersing agent.
Claim 11
Dependent Claim
34 words
The method according to claim 8, wherein said binder comprises at least one element selected from the group consisting of methylcellulose, polyvinyl alcohol, water-soluble urethane, a copolymer of polymethacrylate, polyvinyl butyral, polyacrylate, and polymethacrylate.
Claim 12
Dependent Claim
41 words
The method according to claim 6, wherein said second solvent is an organic solvent selected from the group consisting of alcohol, ketone, aromatic hydrocarbon, aliphatic hydrocarbon, alycrylic hydrocarbon, chlorinated hydrocarbon, or a mixture of at least two of these organic solvents.
Claim 13
Independent Claim
156 words
A method of manufacturing a ceramic coned disk or leaf spring, comprising the steps of: preparing a mixture by mixing together ceramic powder, organic materials including at least a binder and a plasticizer for imparting formability to the ceramic powder, and a first solvent; shaping the mixture into a sheet-like product; drying the sheet-like product to remove substantially all of the first solvent from the sheet-like product; immersing the dried product in a bath of a second solvent which dissolves a plasticizer contained in the sheet-like product and which is a poor solvent to the binder to that it softens the binder but does not dissolve the binder, for thereby plasticizing the product; re-shaping the plasticized sheet-like product into a coned disk or leaf spring; and drying the re-shaped coned disk or leaf spring product to remove second solvent therefrom, whereby shrinkage of the re-shaped product is substantially negligible during the removal of the second solvent.
Claim 14
Independent Claim
156 words
A method of manufacturing a ceramic coned disk or leaf spring, comprising the steps of: preparing a mixture by mixing together ceramic powder, organic materials including at least a binder and a plasticizer for imparting formability to the ceramic powder, and a first solvent; shaping the mixture into a sheet-like product; drying the sheet-like product to remove substantially all of the first solvent from the sheet-like product; immersing the dried product in a bath of a second solvent which dissolves a plasticizer contained in the sheet-like product and which is a poor solvent to the binder to that it softens the binder but does not dissolve the binder, for thereby plasticizing the product; re-shaping the plasticized sheet-like product into a coned disk or leaf spring; and drying the re-shaped coned disk or leaf spring product to remove second solvent therefrom, whereby shrinkage of the re-shaped product is substantially negligible during the removal of the second solvent.
Claim 15
Dependent Claim
24 words
The method according to claim 11, further comprising the steps of: burning organic components contained in the re-shaped product, and sintering the re-shaped product.
Claim 16
Dependent Claim
15 words
The method according to claim 11, wherein said organic materials further includes a dispersing agent.
Claim 17
Dependent Claim
34 words
The method according to claim 13, wherein said binder comprises at least one element selected from the group consisting of methylcellulose, polyvinyl alcohol, water-soluble urethane, a copolymer of polymethacrylate, polyvinyl butyral, polyacrylate, and polymethacrylate.
Claim 18
Dependent Claim
41 words
The method according to claim 11, wherein said second solvent is an organic solvent selected from the group consisting of alcohol, ketone, aromatic hydrocarbon, aliphatic hydrocarbon, alycrylic hydrocarbon, chlorinated hydrocarbon, or a mixture of at least two of these organic solvents.
References Cited (Backward Citations)
US2939199A
Cited
US4104345A
Cited
JPS58178032A
Cited
JPS6054966A
Cited
JPS6188033A
Cited
JPS627659A
Cited
JPS6225013A
Cited
JPS62242144A
Cited
JPH01110909A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-26 | 1995-02-25 | 1995-08-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-26 | 1999-02-25 | 1999-08-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-26 | 2003-02-25 | 2003-08-27 | $7700.00 | Window Closed / Lapsed |