Process for metallization of a nonconductor surface, especially on a circuit board having preexisting copper surfaces
Assignee: Atotech Deutschland GmbH and Co KG
•
Filing: 1991-02-14
•
Granted: 1993-02-02
•
Expires: 2011-02-14
Abstract
Abstract The process for directly metallizing a circuit board having nonconductor surfaces, includes reacting the nonconductor surface with an alkaline permanganate solution to form manganese dioxide chemically adsorbed on the nonconductor surface; forming an aqueous solution of a weak acid having an acid dissociation constant, for loss of a proton in aqueous solution, between 0.1 and 0.01, and of pyrrole or a pyrrole derivative and soluble oligomers thereof; contacting the aqueous solution containing the pyrrole monomer and its oligomers with the nonconductor surface having the manganese dioxide adsorbed chemically thereon to deposit an adherent, electrically conducting, insoluble polymer product on the nonconductor surface; and directly electrodepositing metal on the nonconductor surface having the insoluble adherent polymer product formed thereon. The oligomers are advantageously formed in aqueous solution containing 0.1 to 200 g/l of the pyrrole monomer at a temperature between room temperature and the freezing point of the solution.
Inventors
- 👤 Burkhard Bressel
- 👤 Heinrich Meyer
- 👤 Walter Meyer
- 👤 Klaus Gedrat
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 19:06
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/188; C; C08; C08G; C08G61/00; C08G61/12; C08G61/122; C08G61/123; C25; C25D; C25D5/00; C25D5/54; C25D5/56; H05K2201/00; H05K2201/03; H05K2201/032; H05K2201/0329; H05K2203/00; H05K2203/07; H05K2203/0779; H05K2203/0786; H05K2203/0796; Y; Y10; Y10S; Y10S205/00; Y10S205/92
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
194 words
A process for directly metallizing a nonconductor surface on a circuit board also having copper surfaces, comprising the steps of reacting the nonconductor surface on the circuit board with permanganate to form manganese dioxide adsorbed on the nonconductor surface; depositing an adherent, insoluble polymer product the manganese dioxide adsorbed on the nonconductor surface from an aqueous solution of a weak acid having an acid dissociation constant, for loss of a proton in aqueous solution, between 0.1 and 0.01, a monomer selected from the group consisting of pyrrole and pyrrole derivatives, and at least one oligomer selected from the group consisting of oligomers of said pyrrole derivatives and said pyrrole; by contacting the aqueous solution with the manganese dioxide adsorbed on the nonconductor surface, the polymer product having an electrical conductance which is sufficient so that a metal can be directly electroplated on the polymer product, and then directly electroplating the metal on the polymer product, wherein any oxide film formed on said copper surfaces during said reacting with said permanganate is removed by said weak acid in said aqueous solution during said contacting to prevent formation of another polymer layer on said copper surfaces.
Claim 2
Dependent Claim
194 words
A process for directly metallizing a nonconductor surface on a circuit board also having copper surfaces, comprising the steps of reacting the nonconductor surface on the circuit board with permanganate to form manganese dioxide adsorbed on the nonconductor surface; depositing an adherent, insoluble polymer product the manganese dioxide adsorbed on the nonconductor surface from an aqueous solution of a weak acid having an acid dissociation constant, for loss of a proton in aqueous solution, between 0.1 and 0.01, a monomer selected from the group consisting of pyrrole and pyrrole derivatives, and at least one oligomer selected from the group consisting of oligomers of said pyrrole derivatives and said pyrrole; by contacting the aqueous solution with the manganese dioxide adsorbed on the nonconductor surface, the polymer product having an electrical conductance which is sufficient so that a metal can be directly electroplated on the polymer product, and then directly electroplating the metal on the polymer product, wherein any oxide film formed on said copper surfaces during said reacting with said permanganate is removed by said weak acid in said aqueous solution during said contacting to prevent formation of another polymer layer on said copper surfaces.
Claim 3
Dependent Claim
15 words
The process according to claim 1, wherein the aqueous solution also contains a solubilizing agent.
Claim 4
Dependent Claim
25 words
The process according to claim 1, further comprising the step of forming the at least one oligomer in the aqueous solution containing the weak acid.
Claim 5
Dependent Claim
43 words
The process according to claim 3, wherein the aqueous solution containing the weak acid has a freezing point and the step of forming the at least one oligomer proceeds at a temperature between the freezing point of the aqueous solution and room temperature.
Claim 6
Dependent Claim
22 words
The process according to claim 1, in which the aqueous solution contains 0.1 to 200 g/l of said monomers and said oligomers.
Claim 7
Dependent Claim
29 words
The process according to claim 1, wherein the metal directly electroplated on the polymer product is copper and the step of electroplating is performed in an acid copper bath.
Claim 8
Dependent Claim
16 words
The process according to claim 2, in which the solubilizing agent is a polar organic solvent.
Claim 9
Dependent Claim
38 words
The process according to claim 1, in which the circuit board is provided with a plurality of through-going holes having interior surfaces, said process further comprising metallizing the interior surfaces of the through-going holes of the circuit board.
Claim 10
Dependent Claim
21 words
The process according to claim 1, in which the contacting occurs by immersing, said nonconductor surface being immersed in said solution.
Claim 11
Dependent Claim
22 words
The process according to claim 1, in which the contacting occurs by a spraying, said nonconductor surface being sprayed with said solution.
Claim 12
Dependent Claim
17 words
The process according to claim 1, in which the depositing occurs in a continuous, horizontal treatment method.
Claim 13
Dependent Claim
58 words
The process according to claim 8, wherein the metallizing proceeds according to a conductor pattern, which is provided by the form and structure of the conducting polymer product, and said process further comprises treating the conducting polymer product with another solution containing a solute selected from the group consisting of acids and oxidizing agents prior to the metallizing.
Claim 14
Dependent Claim
14 words
The process according to claim 12, wherein said conductor pattern is provided by photoimpression.
Claim 15
Dependent Claim
152 words
A process for directly metallizing a non-conductor, comprising the steps of: a. reacting a surface of a nonconductor with a permanganate solution to form manganese dioxide adsorbed on the nonconductor surface, b. forming an aqueous solution of a monomer, said monomer being selected from the group consisting of pyrrole and pyrrole derivatives, and at least one soluble oligomer of said monomer, and an acid having an acid dissociation constant, for loss of a proton in the aqueous solution, between 0.1 and 0.01, and; c. contacting the aqueous solution containing the monomer and the oligomers with the nonconductor surface having the manganese dioxide adsorbed thereon to deposit an insoluble adherent polymer product on the nonconductor surface having an electrical conductance which is sufficient so that a metal can be directly electroplated from an electroplating bath on the nonconductor surface; and d. directly electroplating metal on the polymer product formed on the nonconductor surface.
Claim 16
Dependent Claim
152 words
A process for directly metallizing a non-conductor, comprising the steps of: a. reacting a surface of a nonconductor with a permanganate solution to form manganese dioxide adsorbed on the nonconductor surface, b. forming an aqueous solution of a monomer, said monomer being selected from the group consisting of pyrrole and pyrrole derivatives, and at least one soluble oligomer of said monomer, and an acid having an acid dissociation constant, for loss of a proton in the aqueous solution, between 0.1 and 0.01, and; c. contacting the aqueous solution containing the monomer and the oligomers with the nonconductor surface having the manganese dioxide adsorbed thereon to deposit an insoluble adherent polymer product on the nonconductor surface having an electrical conductance which is sufficient so that a metal can be directly electroplated from an electroplating bath on the nonconductor surface; and d. directly electroplating metal on the polymer product formed on the nonconductor surface.
Claim 17
Dependent Claim
24 words
The process according to claim 14, wherein said treating is such that said oxidizing agent adsorbed on the nonconductor surface is substantially said permanganate.
Claim 18
Dependent Claim
41 words
The process according to claim 14, wherein said treating is such that said oxidizing agent adsorbed on the nonconductor surface is substantially manganese oxide, and further comprising the step of forming said manganese dioxide by reacting of permanganate and the nonconductor.
Claim 19
Dependent Claim
48 words
The process according to claim 14, wherein the aqueous solution containing the acid has a freezing point, and further comprising the step of forming the soluble oligomers of said monomer in the aqueous solution at a temperature between the freezing point of the aqueous solution and room temperature.
Claim 20
Dependent Claim
28 words
The process according to claim 14, wherein said pyrrole derivatives include 3-chloropyrrole, 3-bromopyrrole, 4-chloropyrrole, 4-bromopyrrole, 3,4-dichloropyrrole, 3,4-dibromopyrroles, formyl pyrrole derivatives, carboxy pyrrole derivatives, N-methylpyrrole, N-ethylpyrrole, N-vinylpyrrole and 2,2'-dipyrrole.
Claim 21
Dependent Claim
20 words
The process according to claim 14, wherein said aqueous solution also contains a polar organic solvent as a solubilizing agent.
Claim 22
Dependent Claim
43 words
The process according to claim 14, wherein said acid is selected from the group consisting of formic acid, acetic acid, propionic acid, butyric acid, oxalic acid succinic acid, fumaric acid, maleic acid, azeliac acid, citric acid, malic acid, ascorbic acid and phosphoric acid.
Claim 23
Dependent Claim
27 words
The process according to claim 14, in which the contacting occurs by a spraying in a continuous, horizontal treatment method, said nonconductor being sprayed with said solution.
Claim 24
Dependent Claim
26 words
The process according to claim 14, in which the contacting occurs by immersing in a continuous, horizontal treatment method, said nonconductor being immersed in said solution.
Claim 25
Dependent Claim
32 words
The process according to claim 14, further comprising the step of forming the at least one soluble oligomers at a temperature between a freezing point of the aqueous solution and room temperature.
References Cited (Backward Citations)
FR2222459A1
Cited
US4567250A
Cited
US4566955A
Cited
US4710401A
Cited
US4696835A
Cited
US4617228A
Cited
WO1987000391A1
Cited
US4724062A
Cited
US4891069A
Cited
EP0266133A2
Cited
JPS63125696A
Cited
EP0406678A1
Cited
US5106473A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-02-02 | 1996-08-03 | 1997-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-02-02 | 2000-08-03 | 2001-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-02-02 | 2004-08-03 | 2005-02-02 | $7700.00 | Window Closed / Lapsed |