Composition for the electrolytic coating of circuit boards without an electroless metal coating
Assignee: Techno Instruments Investments 1983 Ltd
•
Filing: 1986-06-06
•
Granted: 1990-01-02
•
Expires: 2006-06-06
Abstract
Abstract A process and composition are disclosed for directly electrometallizing a non-conductive substrate such as the non conductive surfaces of a circuit board and to directly effect through hole plating and/or form circuits on the boards without employing an electroless metal coating. A process and composition is also described for depositing metals on a non-conductive substrate by using the reductive capacity of hydrogen in the presence of a metal catalyst on the substrate. The metal catalyst is combined with hydrogen that is generated electrolytically from a protic bath. The metal catalyst combined with hydrogen is contacted with a metal salt. The metal salt may be combined with the protic bath so that the hydrogen that is generated electrolytically combines with the metal catalyst and the metal salt is converted to a metal coating on the substrate.
Inventors
- 👤 Abrahm M. Holtzman
- 👤 Joseph Relis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 14:11
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/40; H05K3/42; H05K3/423; H05K3/424; C; C25; C25D; C25D5/00; C25D5/54; C25D5/56; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0716; H05K2203/12; H05K2203/122; H05K3/425; H05K3/427
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
143 words
A catalyst composition comprising a metal catalyst for use in a process for depositing metals on a non-conductive substrate by using the reductive capacity of hydrogen in the presence of said metal catalyst on such substrate, said metal catalyst being capable of combining with hydrogen where hydrogen is generated electrolytically from a protic bath, said metal catalyst being in association with a stabilizer, said metal catalyst being present in an amount sufficient so that when it is applied to a non-conductive substrate immersed in a protic bath it will combine with hydrogen generated electrolytically from said bath so that said hydrogen combined with said metal catalyst will reduce a metal coating compound brought into contact with said catalyst and form a metal coating on said substrate, said stabilizer being present in an amount sufficient to stabilize said metal catalyst in an aqueous environment.
Claim 2
Dependent Claim
143 words
A catalyst composition comprising a metal catalyst for use in a process for depositing metals on a non-conductive substrate by using the reductive capacity of hydrogen in the presence of said metal catalyst on such substrate, said metal catalyst being capable of combining with hydrogen where hydrogen is generated electrolytically from a protic bath, said metal catalyst being in association with a stabilizer, said metal catalyst being present in an amount sufficient so that when it is applied to a non-conductive substrate immersed in a protic bath it will combine with hydrogen generated electrolytically from said bath so that said hydrogen combined with said metal catalyst will reduce a metal coating compound brought into contact with said catalyst and form a metal coating on said substrate, said stabilizer being present in an amount sufficient to stabilize said metal catalyst in an aqueous environment.
Claim 3
Dependent Claim
39 words
The catalyst composition of claim 1 further comprising a promoter selected from the group consisting of: (a) organic hydroxy compounds (b) surfactants (c) thiourea compounds (d) amino acids (e) polycarboxylic acids and (f) water soluble polymers or combinations thereof.
Claim 4
Dependent Claim
22 words
The catalyst composition of claim 2 where said stabilizer minimizes said metal catalyst's sensitivity to water, said stabilizer comprising a metal salt.
Claim 5
Dependent Claim
22 words
The catalyst composition of claim 1 where said stabilizer minimizes said metal catalyst's sensitivity to water, said stabilizer comprising a metal salt.
Claim 6
Dependent Claim
23 words
The composition of claim 2 where said catalyst is based on a metal from Group VIII of the Periodic Table of the Elements.
Claim 7
Dependent Claim
14 words
The composition of claims 1, 2, 3 or 4 further comprising a protective colloid.
Claim 8
Dependent Claim
15 words
The composition of claims 1, 2, 3 or 4 further comprising a tin protective colloid.
Claim 9
Dependent Claim
39 words
The composition of claim 3 where said stabilizer is a water-soluble stable salt selected from the group consisting of salts of magnesium, titanium, zirconium, hafnium, manganese, cobalt, nickel, silver, zinc, cadmium, aluminum, gallium, indium and thallium and mixtures thereof.
Claim 10
Dependent Claim
26 words
The composition of claim 8 where said stabilizer is selected from a member of the group consisting of the salts of aluminum, titanium, zirconium and hafnium.
Claim 11
Dependent Claim
14 words
The composition of claim 8 where said stabilizer comprises stable water soluble halide salts.
Claim 12
Dependent Claim
19 words
The composition of claim 8 where said stabilizer forms complexes with the Group VIII metals or tin or both.
Claim 13
Dependent Claim
12 words
The composition of claim 10 where said stabilizer comprises an aluminum halide.
Claim 14
Dependent Claim
13 words
The composition of claim 9 where said stabilizer comprises water soluble halide salts.
Claim 15
Dependent Claim
140 words
A catalyst for applying an electrolytic coating to a non-conductive substrate comprising: (a) a metal which can combine with hydrogen, (b) an acid; (c) an Sn 2+ salt; (d) a member selected from the group consisting of an alkali metal stannate and an Sn 4+ salt; (e) a metal salt stabilizer; said metal which can combine with hydrogen being present in an amount sufficient so that when it is applied to a non-conductive substrate immersed in a protic bath is will combine with hydrogen generated electrolytically from said bath so that said hydrogen combined with said metal will reduce a metal coating compound brought into contact with said catalyst and form a metal coating on said substrate, said metal salt stabilizer being present in an amount sufficient to stabilize said metal which can combine with hydrogen in an aqueous environment
Claim 16
Dependent Claim
140 words
A catalyst for applying an electrolytic coating to a non-conductive substrate comprising: (a) a metal which can combine with hydrogen, (b) an acid; (c) an Sn 2+ salt; (d) a member selected from the group consisting of an alkali metal stannate and an Sn 4+ salt; (e) a metal salt stabilizer; said metal which can combine with hydrogen being present in an amount sufficient so that when it is applied to a non-conductive substrate immersed in a protic bath is will combine with hydrogen generated electrolytically from said bath so that said hydrogen combined with said metal will reduce a metal coating compound brought into contact with said catalyst and form a metal coating on said substrate, said metal salt stabilizer being present in an amount sufficient to stabilize said metal which can combine with hydrogen in an aqueous environment
Claim 17
Dependent Claim
86 words
The composition of claim 14 where the components of said composition are present in the following amounts on a molar basis: (a) from about 0.1 to about 2 parts of said metal; (b) from about 3 to about 6 parts of said acid; (c) from about 4 to about 85 parts of said Sn 2+ salt; (d) from about 0.5 to about 10 parts of said alkali metal stannate or Sn 4+ salt; (e) from about 100 to about 1000 parts of said metal salt stabilizer.
Claim 18
Dependent Claim
21 words
The composition of claim 14 where said salt metal is a Group VIII metal of the Periodic Table of the Elements.
Claim 19
Dependent Claim
10 words
The composition of claim 16 where said metal is palladium.
Claim 20
Dependent Claim
40 words
The composition of claim 16 where said stabilizer is a water-soluble stable salt selected from the group consisting of the salts of magnesium, titanium, zirconium, hafnium, manganese, cobalt, nickel, silver, zinc, cadmium, aluminum, gallium, indium and thallium and mixtures thereof.
Claim 21
Dependent Claim
23 words
The composition of claim 18 where said stabilizer is selected from the group consisting of the salts of aluminum, titanium, zirconium and hafnium.
Claim 22
Dependent Claim
10 words
The composition of claim 18 where said stabilizer comprises aluminum.
Claim 23
Dependent Claim
12 words
The composition of claim 18 where said stabilizer comprises an aluminum halide.
References Cited (Backward Citations)
US3099608A
Cited
US3303111A
Cited
GB1222969A
Cited
US3930963A
Cited
GB2123036A
Cited
DE3304004A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-01 | 1993-07-03 | 1994-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-01 | 1997-07-03 | 1998-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-01 | 2001-07-03 | 2002-01-02 | $7700.00 | Window Closed / Lapsed |