Method of making metal oxide ceramic membranes with small pore sizes
Assignee: Wisconsin Alumni Research Foundation
•
Filing: 1991-02-11
•
Granted: 1992-12-08
•
Expires: 2011-02-11
Abstract
Abstract A method for the production of metal oxide ceramic membranes is composed of very small pore size. The process is particularly useful in the creation of titanium and other transition metal oxide membranes. The method utilizes a sol-gel process in which the rate of particle formation is controlled by substituting a relatively large alcohol in the metal alkoxide and by limiting the available water. Stable, transparent metal oxide ceramic membranes are created having a narrow distribution of pore size, with the pore diameter being manipulable in the range of 5 to 40 Angstroms.
Inventors
- 👤 Marc A. Anderson
- 👤 Qunyin Xu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 11:22
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0039; B01D67/0048; B01D71/00; B01D71/02; B01D71/024; B01J; B01J19/00; B01J19/24; B01J19/2475; B01J35/00; B01J35/50; B01J35/58; B01J35/59; B01J8/00; B01J8/008; B01J8/009; C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/48; C04B35/486; C04B35/49; C04B35/622; C04B35/624; C04B38/00; C04B38/0051; B01D2323/00; B01D2323/08; B01D2323/081; B01J2208/00; B01J2208/00008; B01J2208/00017; B01J2208/00548; B01J2208/00592; B01J2219/00; B01J2219/00049; B01J2219/00051; B01J2219/00164; B01J2219/00177
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
141 words
A method for making a metal oxide ceramic membrane of defined small pore size comprising steps of (a) dissolving a selected quantity of metal oloxide in alcohol, the alcohol in the metal alkoxide and the alcohol being the same alkyl alcohol which is of at least four carbon atoms and has a brached structure; (b) adding a selected quantity of water into a quantity of the same alkyl alcohol; (c) slowly adding the water-containing alcohol to the metal alkoxide-containing alcohol while stirring the solution so as to create small metal oxide particles in the solution without the need for peptization; (d) placing the solution in a humidity controlled environment for slow drying of the alcohol from the solution to create a gel; and (e) sintering the steel into a membrane by firing at a temperature not to exceed about 400° C.
Claim 2
Independent Claim
141 words
A method for making a metal oxide ceramic membrane of defined small pore size comprising steps of (a) dissolving a selected quantity of metal oloxide in alcohol, the alcohol in the metal alkoxide and the alcohol being the same alkyl alcohol which is of at least four carbon atoms and has a brached structure; (b) adding a selected quantity of water into a quantity of the same alkyl alcohol; (c) slowly adding the water-containing alcohol to the metal alkoxide-containing alcohol while stirring the solution so as to create small metal oxide particles in the solution without the need for peptization; (d) placing the solution in a humidity controlled environment for slow drying of the alcohol from the solution to create a gel; and (e) sintering the steel into a membrane by firing at a temperature not to exceed about 400° C.
Claim 3
Dependent Claim
12 words
A method as claimed in claim 1 wherein the metal is titanium.
Claim 4
Dependent Claim
18 words
A method as claimed in claim 1 wherein eh alcohol in steps (a) and (b) is tert-amyl alcohol.
Claim 5
Dependent Claim
20 words
A method as claimed in claim 1 wherein the molarity of the metal alkoxide in the solution is about 0.2M.
Claim 6
Dependent Claim
24 words
A method as claimed in claim 1 wherein the ratio of water to metal oxide molecules is calculated to be about 6 to 1.
Claim 7
Dependent Claim
25 words
A method as claimed in claim 1 wherein the water in step (b) has been previously acidified to a pH of between one and three.
Claim 8
Dependent Claim
24 words
A method as claimed in claim 1 wherein the alkyl alcohol is of at least five carbon atoms, which has a branched chain structure.
Claim 9
Dependent Claim
33 words
A method as claimed in claim 1 wherein step (d) is accomplished by placing the solution in a closed desiccator chamber for a time period sufficient for the alcohol to substantially evaporate therefrom.
Claim 10
Dependent Claim
37 words
A method as claimed in claim 1 wherein in the sintering in step (e), the temperature is raised only in increments of no more than about 0.1° C. per minute to prevent carbon deposition on the membrane.
Claim 11
Dependent Claim
61 words
A method as claimed in claim 1 wherein before the step (a), there is further the step of processing a metal alkoxide in which the alcohol is less than four carbon atoms in an alcohol exchange process to substitute for the alcohol in the metal alkoxide with the selected alkyl alcohol having a branched structure and at least four carbon atoms.
References Cited (Backward Citations)
US3892580A
Cited
US4158621A
Cited
US4800051A
Cited
US4584280A
Cited
US4801399A
Cited
WO1988002537A1
Cited
US4764357A
Cited
US4929406A
Cited
US5028568A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-12-08 | 1996-06-08 | 1996-12-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-12-08 | 2000-06-08 | 2000-12-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-12-08 | 2004-06-08 | 2004-12-08 | $7700.00 | Window Closed / Lapsed |