US5162426A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Coatings comprising dispersed polymers with silane crosslinking
Assignee: EIDP Inc
•
Filing: 1990-12-17
•
Granted: 1992-11-10
•
Expires: 2010-12-17
Abstract
Abstract A coating composition containing a film-forming organosilane polymer and a sterically dispersed polymer having macromonomer chains which react with the silane functionality of the organosilane polymer. Silane functionalities in the core of the dispersed polymer provides post-cure crosslinking in the core. The coating composition can be used as the clearcoat over a conventional pigmented basecoat, or as a basecoat or monocoat or primer when a suitable amount of pigment is incorporated therein. The coating composition provides improved chemical resistance and is not prone to cracking.
Inventors
- 👤 Isidor Hazan
- 👤 Mitzie K. Rummel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 03:45
CPC Classifications
C; C09; C09D; C09D143/00; C09D143/04; C09D151/00; C09D151/06; C08; C08L; C08L51/00; C08L51/06
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
287 words
A composition useful for coating a substrate, which composition comprises: (a) from about 20 to 90% by weight, based on the weight of the binder solids, of a film-forming organosilane polymer having a weight average molecular weight of about 500-30,000 comprising (i) from about 30 to 95% by weight, based on the weight of the organosilane polymer, of ethylenically unsaturated monomers which do not contain a silane functionality and about 5 to 70% by weight ethylenically unsaturated monomers which contain a silane functionality; and (b) from about 10 to 60%, based on the weight of the binder solids, of a dispersed polymer comprising: (i) a core comprising a macromolecular polymer, wherein a portion of the monomers making up said macromolecular polymer have silane functionalities such that no crosslinking between silane functionalities occurs in said macromolecular core until after the composition is applied as a coating to a substrate, but which crosslinking occurs under the influence of an outside source after the composition has been applied to the surface of the substrate; and (ii) attached to the macromolecular core, a plurality of macromonomer chains having a weight average molecular weight of about 1,000 to 30,000, comprising 5 to 30% by weight, based on the weight of the macromonomer, of polymerized ethylenically unsaturated monomers which comprise a crosslinking functionality; and about 70 95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without a crosslink functionality; whereby covalent bonding between said crosslinking functionalities in said dispersed polymer and silane functionalities in said organosilane polymer occurs during drying or curing; and (c) from about 25 to 50% by weight, based on the weight of the composition, of a liquid organic carrier.
Claim 2
Dependent Claim
287 words
A composition useful for coating a substrate, which composition comprises: (a) from about 20 to 90% by weight, based on the weight of the binder solids, of a film-forming organosilane polymer having a weight average molecular weight of about 500-30,000 comprising (i) from about 30 to 95% by weight, based on the weight of the organosilane polymer, of ethylenically unsaturated monomers which do not contain a silane functionality and about 5 to 70% by weight ethylenically unsaturated monomers which contain a silane functionality; and (b) from about 10 to 60%, based on the weight of the binder solids, of a dispersed polymer comprising: (i) a core comprising a macromolecular polymer, wherein a portion of the monomers making up said macromolecular polymer have silane functionalities such that no crosslinking between silane functionalities occurs in said macromolecular core until after the composition is applied as a coating to a substrate, but which crosslinking occurs under the influence of an outside source after the composition has been applied to the surface of the substrate; and (ii) attached to the macromolecular core, a plurality of macromonomer chains having a weight average molecular weight of about 1,000 to 30,000, comprising 5 to 30% by weight, based on the weight of the macromonomer, of polymerized ethylenically unsaturated monomers which comprise a crosslinking functionality; and about 70 95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without a crosslink functionality; whereby covalent bonding between said crosslinking functionalities in said dispersed polymer and silane functionalities in said organosilane polymer occurs during drying or curing; and (c) from about 25 to 50% by weight, based on the weight of the composition, of a liquid organic carrier.
Claim 3
Dependent Claim
18 words
The composition of claim 1, whereby the macromolecular core crosslinks with itself soley by means of silane-containing groups.
Claim 4
Dependent Claim
26 words
The composition of claim 1, wherein the outside source is heating, H 2 O, and/or catalyst which occurs during and/or after the curing of the composition.
Claim 5
Dependent Claim
21 words
The composition of claim 1, whereby 1 to 10% of the monomers in said macromolecular polymer contain a reactive silane group.
Claim 6
Dependent Claim
22 words
The composition of claim 1, whereby 2 to 5 percent of the monomers in said macromolecular polymer contain a reactive silane group.
Claim 7
Dependent Claim
30 words
The coating composition of claim 1, wherein the crosslink functional groups in the dispersed polymer are selected from the group comprising hydroxy, epoxide, silane, anhydride, carboxylic acid, and isocyanate moieties.
Claim 8
Dependent Claim
26 words
The coating composition of claim 1, wherein the crosslink functional groups in the dispersed polymer are selected from the group consisting of hydroxy, epoxide, and silane.
Claim 9
Dependent Claim
17 words
The coating composition of claim 1, wherein the film-forming organosilane polymer may also comprise hydroxy functional groups.
Claim 10
Dependent Claim
27 words
The coating composition of claim 1, further comprising a polyol polymer having a hydroxyl number of about 50-200 and a weight average molecular weight of about 1,000-200,000.
Claim 11
Dependent Claim
14 words
The coating composition of claim 9, wherein the polypol polymer comprises an acrylic polyol.
Claim 12
Dependent Claim
11 words
The coating composition of claim 1 further comprising a cross-linking agent.
Claim 13
Dependent Claim
15 words
The coating composition of claim 3, wherein the H 2 O is provided by humidity.
Claim 14
Dependent Claim
15 words
The coating composition of claim 11, wherein the crosslinking agent is an alkylated melamine formaldehyde.
Claim 15
Dependent Claim
14 words
The coating composition of claim 1, wherein the film-forming polymer is an acrylosilane polymer.
Claim 16
Dependent Claim
72 words
The coating composition of claim 14, wherein the acrylosilane polymer consists essentially of ethylenically unsaturated non-silane containing monomers selected from the group consisting of styrene, alkyl acrylate, alkyl methacrylate, cycloaliphatic acrylates, cycloaliphatic methacrylates, aryl acrylates, aryl methacrylates and any mixtures thereof, and ethylenically unsaturated silane monomers selected from the group consisting of alkoxy silane monomers, acyloxy silane monomers, and any mixtures thereof, wherein said alkyl, cycloaliphatic, and aryl have 1-12 carbon atoms.
Claim 17
Dependent Claim
100 words
The coating composition of claim 1, wherein the ethylenically unsaturated monomers containing a silane functionality have the following structural formula: ##STR4## wherein R is selected from the group consisting of CH 3 , CH 3 CH 2 , CH 3 O, or CH 3 CH 2 O; R 1 and R 2 are individually selected from the group consisting of CH 3 or CH 3 CH 2 ; and R 3 is selected from the group consisting of H, CH 3 , or CH 3 CH 2 and n is 0 or a positive integer of not greater than 8.
Claim 18
Dependent Claim
78 words
The coating composition of claim 1, wherein the ethylenically unsaturated monomers containing a silane functionality have the following structural formula: ##STR5## wherein R is selcted from the group consisting of CH 3 , CH 3 CH 2 , CH 3 O, OR CH 3 CH 2 O; R 1 AND R 2 are individually selected from the group consisting of CH 3 or CH 3 CH 2 ; and n is 0 or a positive integer of 1-10.
Claim 19
Dependent Claim
100 words
The coating composition of claim 1 wherein the ehtylenically unsaturated monomers containing a silane functionality have the following structural formula: ##STR6## wherein R is selected from the group consisting or CH 3 , CH 3 CH 2 , CH 3 O, or CH 3 CH 2 O; R 1 and R 2 are individually selected from the group consisting of CH 3 or CH 3 CH 2 ; and R 4 is selected from the group consisting of H or CH 3 , R 5 is an alkylene group having 1-5 carbon atoms and n is positive integer of 1-8.
Claim 20
Dependent Claim
46 words
The coating composition of claim 14, wherein the acrylosilane consists essentially of polymerized monomers of about 15-25% by weight styrene, about 25-50% by weight cycloalkyl or alkyl methacrylate or acrylate, and about 30-60% by weight trimethoxylsilane-containing monomer, wherein said alkyl and cycloalkyl have 1-6 carbon atoms.
Claim 21
Dependent Claim
87 words
The coating composition of claim 1, wherein (a) the core of the dispersed polymer comprises polymerized monomers of styrene, an alkyl methacrylate, wherein said alkyl has 1-12 carbon atoms, an ehtylenically unsaturated monocarboxylic acid; and (b) the macromonomers attached to the core comprise polymerized alkyl methacrylate, alkyl acrylate monomers or mixtures thereof, each having 1-12 carbon atoms in the alkyl group, hydroxy alkyl acrylate or hydroxy alkyl methacrylate monomers or mixtures thereof, each having 1-4 carbon atoms in the alkyl group, and glycidyl acrylate or glycidyl methacrylate.
Claim 22
Dependent Claim
70 words
The coating composition of claim 20, wherein (a) the core of the dispersed polymer consists essentially of polymerized monomers of methacrylic acid, hydroxy ethyl acrylate, methyl methacrylate, methyl acrylate, glycidyl methacrylate, and styrene; and (b) the macromonomers attached to the core consist essentially of polymerized prepolymer and glycidyl methacrylate; wherein the prepolymer consists essentially of polymerized monomers of styrene, butyl methacrylate, butyl acrylate, hydroxy ethylacrylate, acrylic acid, and ethyl methacrylate.
Claim 23
Dependent Claim
25 words
The coating composition of claim 1, wherein the composition contains about 0.1-4% by weight, based on the weight of the composition, of an acid catalyst.
Claim 24
Dependent Claim
33 words
The coating composition of claim 1, wherein the composition contains about 0.1-5% by weight, based on the weight of the composition, of an organo tin catalyst, an aluminum catalyst or a zirconium catalyst.
Claim 25
Dependent Claim
62 words
A process for coating a substrate, comprising the steps of: (a) applying a layer of a pigmented basecoating to the substrate to form a basecoat thereon; (b) applying to the basecoat a layer of the composition of claim 1 to form a top coat over said basecoat; (c) curing the basecoat and topcoat to form a basecoat and topcoat on the substrate.
Claim 26
Dependent Claim
9 words
A substrate coated with a composition of claim 1.
Claim 27
Dependent Claim
280 words
A composition useful for coating a substrate, which composition comprises: (a) from about 20 to 90% by weight, based on the weight of the binder solids, of a film-forming organosilane polymer having a weight average molecular weight of about 500-30,000 comprising (i) from about 30 to 95% by weight, based on the weight of the organosilane polymer, of ethylenically unsaturated monomers which do not contain a silane functionality and about 5 to 70% by weight ethylenically unsaturated monomers which contain a silane functionality; and (b) from about 10 to 60%, based on the weight of the binder solids, of a dispersed polymer comprising: (i) a core comprising a macromolecular polymer, wherein 1 to 10% of the monomers making up said macromolecular polymer have silane functionalities such that no crosslinking between silane functionalities occurs in said macromolecular core until after the composition is applied as a coating to a substrate, but which crosslinking occurs under the influence of an outside source after the composition has been applied to the surface of the substrate and wherein said crosslinking is the major means of crosslinking in the macromolecular core; and (ii) attached to the macromolecular core, a plurality of macromonomer chains having a weight average molecular weight of about 1,000 to 30,000, comprising 5 to 30% by weight, based on the weight of the macromonomer, of polymerized ethylenically unsaturated monomers which comprise a crosslinking functionality; and about 70 to 95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without a crosslink functionality; and (c) from about 25 to 50% by weight, based on the weight of the composition, of a liquid organic carrier.
Claim 28
Dependent Claim
280 words
A composition useful for coating a substrate, which composition comprises: (a) from about 20 to 90% by weight, based on the weight of the binder solids, of a film-forming organosilane polymer having a weight average molecular weight of about 500-30,000 comprising (i) from about 30 to 95% by weight, based on the weight of the organosilane polymer, of ethylenically unsaturated monomers which do not contain a silane functionality and about 5 to 70% by weight ethylenically unsaturated monomers which contain a silane functionality; and (b) from about 10 to 60%, based on the weight of the binder solids, of a dispersed polymer comprising: (i) a core comprising a macromolecular polymer, wherein 1 to 10% of the monomers making up said macromolecular polymer have silane functionalities such that no crosslinking between silane functionalities occurs in said macromolecular core until after the composition is applied as a coating to a substrate, but which crosslinking occurs under the influence of an outside source after the composition has been applied to the surface of the substrate and wherein said crosslinking is the major means of crosslinking in the macromolecular core; and (ii) attached to the macromolecular core, a plurality of macromonomer chains having a weight average molecular weight of about 1,000 to 30,000, comprising 5 to 30% by weight, based on the weight of the macromonomer, of polymerized ethylenically unsaturated monomers which comprise a crosslinking functionality; and about 70 to 95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without a crosslink functionality; and (c) from about 25 to 50% by weight, based on the weight of the composition, of a liquid organic carrier.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-10 | 1996-05-11 | 1996-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-10 | 2000-05-11 | 2000-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-10 | 2004-05-11 | 2004-11-10 | $7700.00 | Window Closed / Lapsed |