US5162410A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Hot-melt silicon pressure sensitive adhesives with phenyl-containing siloxane fluid additive and related methods and articles
Assignee: Dow Silicones Corp
•
Filing: 1991-12-17
•
Granted: 1992-11-10
•
Expires: 2011-12-17
Abstract
Abstract Hot-melt silicone pressure sensitive adhesive compositions, methods of using the compositions, articles made using the compositions, and methods of making articles using the compositions. The hot-melt silicone pressure sensitive adhesive compositions include a mixture of (i) a silicone resin, (ii) a polyolimethylsiloxane fluid, and (iii) from about 0.5 to about 20 weight percent, based on the total weight of the silicone resin and the polydimethylsiloxane fluid, of a polyphenylmethylsiloxane fluid having a viscosity at 25° C. of from about 5 to about 60,000 centistokes so that the adhesive will be in a generally flowing state at temperatures above about 100° C., as well as being capable of transdermal drug delivery.
Inventors
- 👤 Randall P. Sweet
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:33
CPC Classifications
A; A61; A61K; A61K9/00; A61K9/70; A61K9/7023; A61K9/703; A61K9/7038; A61K9/7046; A61K9/7069; C; C08; C08L; C08L83/00; C09; C09J; C09J183/00; C09J183/04
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
124 words
A hot-melt silicone pressure sensitive adhesive composition, comprising a mixture of (i) a silicone resin and (ii) a polydimethylsiloxane fluid, said mixture exhibiting tackiness and adhesiveness, said mixture being blended homogeneously with (iii) from about 0.5 to about 20 weight percent, based on the total weight of said silicone resin and said polydimethylsiloxane fluid, of polyphenylmethylsiloxane copolymer fluid, (CH 3 ( 3 SiO[Si(C 6 H 5 )(OSi(CH 3 ) 3 )O] n Si(CH 3 ) 3 , where n is selected so that the viscosity of the homogeneously blended mixture is from about 5 to about 60,000 centistokes so that the adhesive will be in a generally flowing state at temperatures above about 100° C., as well as being capable of transdermal drug delivery.
Claim 2
Dependent Claim
124 words
A hot-melt silicone pressure sensitive adhesive composition, comprising a mixture of (i) a silicone resin and (ii) a polydimethylsiloxane fluid, said mixture exhibiting tackiness and adhesiveness, said mixture being blended homogeneously with (iii) from about 0.5 to about 20 weight percent, based on the total weight of said silicone resin and said polydimethylsiloxane fluid, of polyphenylmethylsiloxane copolymer fluid, (CH 3 ( 3 SiO[Si(C 6 H 5 )(OSi(CH 3 ) 3 )O] n Si(CH 3 ) 3 , where n is selected so that the viscosity of the homogeneously blended mixture is from about 5 to about 60,000 centistokes so that the adhesive will be in a generally flowing state at temperatures above about 100° C., as well as being capable of transdermal drug delivery.
Claim 3
Dependent Claim
62 words
The hot-melt silicone pressure sensitive adhesive composition as claimed in claim 1, wherein said silicone resin is employed in an amount from about 40 to about 70 parts by weight, and said polydimethylsiloxane fluid is employed in an amount from about 30 to about 60 parts by weight, wherein the total parts of the silicone resin and the polydimethylsiloxane fluid equal 100.
Claim 4
Dependent Claim
62 words
The hot-melt silicone pressure sensitive adhesive composition as claimed in claim 1, wherein said silicone resin is employed in an amount from about 50 to about 60 parts by weight, and said polydimethylsiloxane fluid is employed in an amount from about 40 to about 50 parts by weight, wherein the total parts of the silicone resin and the polydimethylsiloxane fluid equal 100.
Claim 5
Dependent Claim
21 words
The hot-melt silicone pressure sensitive adhesive composition as claimed in claim 1, wherein the hot-melt silicone pressure sensitive adhesive is fillerless.
Claim 6
Dependent Claim
31 words
The hot-melt silicone pressure sensitive adhesive composition as claimed in claim 1, wherein the hot-melt silicone pressure sensitive adhesive composition contains less than about 5 weight % of an inorganic filler.
Claim 7
Dependent Claim
22 words
The hot-melt silicone pressure sensitive adhesive composition as claimed in claim 1, wherein said hot-melt silicone pressure sensitive adhesive composition is nonflammable.
Claim 8
Independent Claim
126 words
A method of making a hot-melt silicone pressure sensitive adhesive-coated substrate, comprising: (a) heating, to a coatable temperature above 100° C., a hot-melt silicone pressure sensitive adhesive composition which includes a mixture of (i) a silicone resin and (ii) a polydimethylsiloxane fluid, said mixture exhibiting tackiness and adhesiveness, said mixture being blended with (iii) from about 0.5 to about 20 weight percent, based on the total weight of said silicone resin and said polydimethylsiloxane fluid, of a phenyl-containing polysiloxane fluid having a viscosity at 24° C. of from about 5 to about 60,000 centistokes, (b) coating said heated hot-melt polydimethylsiloxane pressure sensitive adhesive composition onto a substrate, and (c) cooling the coated hot-melt silicone pressure sensitive adhesive composition until it is in a generally non-flowing state.
Claim 9
Independent Claim
126 words
A method of making a hot-melt silicone pressure sensitive adhesive-coated substrate, comprising: (a) heating, to a coatable temperature above 100° C., a hot-melt silicone pressure sensitive adhesive composition which includes a mixture of (i) a silicone resin and (ii) a polydimethylsiloxane fluid, said mixture exhibiting tackiness and adhesiveness, said mixture being blended with (iii) from about 0.5 to about 20 weight percent, based on the total weight of said silicone resin and said polydimethylsiloxane fluid, of a phenyl-containing polysiloxane fluid having a viscosity at 24° C. of from about 5 to about 60,000 centistokes, (b) coating said heated hot-melt polydimethylsiloxane pressure sensitive adhesive composition onto a substrate, and (c) cooling the coated hot-melt silicone pressure sensitive adhesive composition until it is in a generally non-flowing state.
Claim 10
Dependent Claim
57 words
The method as claimed in claim 7, wherein said silicone resin is employed in an amount from about 40 to about 70 parts by weight, and said polydimethylsiloxane fluid is employed in an amount from about 30 to about 60 parts by weight, wherein the total parts of the silicone resin and the polydimethylsiloxane fluid equal 100.
Claim 11
Dependent Claim
57 words
The method as claimed in claim 7, wherein said silicone resin is employed in an amount from about 50 to about 60 parts by weight, and said polydimethylsiloxane fluid is employed in an amount from about 40 to about 50 parts by weight, wherein the total parts of the silicone resin and the polydimethylsiloxane fluid equal 100.
Claim 12
Dependent Claim
17 words
The method as claimed in claim 7, wherein the hot-melt silicone pressure sensitive adhesive composition is fillerless.
Claim 13
Dependent Claim
26 words
The method as claimed in claim 7, wherein the hot-melt silicone pressure sensitive adhesive composition contains less than about 5 weight % of an inorganic filler.
Claim 14
Dependent Claim
17 words
The method as claimed in claim 7, wherein said hot-melt silicone pressure sensitive adhesive composition is nonflammable.
Claim 15
Dependent Claim
15 words
The method as claimed in claim 7, wherein said coatable temperature is above 100° C.
Claim 16
Dependent Claim
15 words
The method as claimed in claim 7, wherein said coatable temperature is above 150° C.
Claim 17
Dependent Claim
21 words
The hot-melt silicone pressure sensitive adhesive of claim 1, further comprising a bioactive agent having a Hildebrand solubility parameter above 9.76.
References Cited (Backward Citations)
US3954692A
Cited
US4001167A
Cited
US4064094A
Cited
US4038346A
Cited
US4253460A
Cited
US4335026A
Cited
US4427737A
Cited
US4551490A
Cited
US4634629A
Cited
US4699816A
Cited
US4714655A
Cited
US4680333A
Cited
US4728572A
Cited
US4793337A
Cited
US4904720A
Cited
US4831070A
Cited
US4814168A
Cited
US4865920A
Cited
US4882377A
Cited
US4988779A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-10 | 1996-05-11 | 1996-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-10 | 2000-05-11 | 2000-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-10 | 2004-05-11 | 2004-11-10 | $7700.00 | Window Closed / Lapsed |