US5158718A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Contact lens casting
Assignee: Novartis AG
•
Filing: 1991-08-19
•
Granted: 1992-10-27
•
Expires: 2011-08-19
Abstract
Abstract Hydrophobic casting moulds are treated with electrical discharge, such as corona discharge, to provide enhanced compatibility with hydrophilic objects introduced into the mould, without interfering with the release properties of the mould. A preferred embodiment involves treatment of contact lens casting moulds with corona discharge to provide improvements in the lens manufacturing procedure, as well as enhancement in the quality of the contact lenses themselves. The invention is particularly applicable to the production of contact lenses having a colored iris pattern imprinted thereon.
Inventors
- 👤 Ashok Thakrar
- 👤 Norman M. Van Houten
- 👤 John M. Evans
- 👤 Richard S. Skipper
- 👤 Peter H. Stafford
- 👤 John T. Phoenix
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 08:22
CPC Classifications
B; B29; B29C; B29C33/00; B29C33/38; B29C33/3842; B29C37/00; B29C37/0025; B29C37/0028; B29C37/0032; B29C59/00; B29C59/10; B29D; B29D11/00; B29D11/00009; B29D11/00038; B29D11/00125; B29D11/00317; B29D11/00865; B29D11/00923; C; C07; C07C; C07C62/00; C07C62/30; C07C62/32; B29C39/00; B29K; B29K2105/00; B29K2105/0002; B29K2995/00; B29K2995/0018; B29K2995/002; B29L; B29L2011/00; B29L2011/0016; B29L2011/0041; Y; Y10; Y10S; Y10S425/00; Y10S425/808
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
118 words
The method of producing a contact lens comprising the steps of treating a surface of a hydrophobic lens casting mould with electrical corona discharge, selecting an active material which is insoluble in the monomer material to be used in the lens, dispersing said active material in a hydrophilic carrier system which is compatible with said monomer material, using the resulting dispersion to coat the electrical corona discharge treated surface of said casting mould, introducing a hydrophilic monomeric lens forming liquid in said mould in contact with said coated surface, polymerizing said liquid to produce a lens blank having an active material impregnated in said blank, adjacent an optical surface thereof, and subsequently removing said lens from said mould.
Claim 2
Independent Claim
118 words
The method of producing a contact lens comprising the steps of treating a surface of a hydrophobic lens casting mould with electrical corona discharge, selecting an active material which is insoluble in the monomer material to be used in the lens, dispersing said active material in a hydrophilic carrier system which is compatible with said monomer material, using the resulting dispersion to coat the electrical corona discharge treated surface of said casting mould, introducing a hydrophilic monomeric lens forming liquid in said mould in contact with said coated surface, polymerizing said liquid to produce a lens blank having an active material impregnated in said blank, adjacent an optical surface thereof, and subsequently removing said lens from said mould.
Claim 3
Dependent Claim
14 words
The method of claim 1 in which the active material is a colouring material.
Claim 4
Dependent Claim
14 words
The method of claim 1 in which the active material is a therapeutic agent.
Claim 5
Dependent Claim
16 words
The method of claim 1 in which said carrier system comprises a monomeric hydrogel forming material.
Claim 6
Dependent Claim
17 words
The method of claim 1 in which said lens casting mould is made from a polyolefin material.
Claim 7
Dependent Claim
55 words
The method of claim 1 in which, area sections of the mould surface, whose area are within the area of the surface which corresponds to the pupil of the contact lens or the periphery surrounding the section to which the colouring/coloured pattern is applied, are masked during the electrical corona discharge treatment of the surface.
Claim 8
Independent Claim
115 words
The method of producing a coloured contact lens comprising the steps of treating the surface of a lens casting mould with electrical corona discharge, selecting a colouring material which is insoluble in the monomer material to be used in the lens, dispersing said colouring material in a carrier system which is compatible with said monomer material, using the resulting dispersion to imprint a pattern on a surface of a casting mould, introducing a monomeric lens forming liquid in said mould in contact with said imprinted surface, polymerizing said liquid to produce a lens blank having a coloured pattern impregnated in said blank, adjacent an optical surface thereof, and subsequently removing said lens from said mould.
Claim 9
Independent Claim
115 words
The method of producing a coloured contact lens comprising the steps of treating the surface of a lens casting mould with electrical corona discharge, selecting a colouring material which is insoluble in the monomer material to be used in the lens, dispersing said colouring material in a carrier system which is compatible with said monomer material, using the resulting dispersion to imprint a pattern on a surface of a casting mould, introducing a monomeric lens forming liquid in said mould in contact with said imprinted surface, polymerizing said liquid to produce a lens blank having a coloured pattern impregnated in said blank, adjacent an optical surface thereof, and subsequently removing said lens from said mould.
Claim 10
Dependent Claim
29 words
The method of claim 7 in which the surface of said lens casting mould is treated with electrical corona discharge for a period of from 0.2 to 2.0 seconds.
Claim 11
Dependent Claim
36 words
The method of claim 7 in which the surface of the lens casting mould is treated with electrical corona discharge of between 2 and 80 KV at an Hz value of between 22 and 500 Hz.
Claim 12
Dependent Claim
17 words
The method of claim 7 in which said lens casting mould is made from a polyolefin material.
Claim 13
Dependent Claim
13 words
The method of claim 7 in which said pattern is an iris pattern.
Claim 14
Dependent Claim
13 words
The method of claim 7 in which the monomer is a hydrogel-forming material.
Claim 15
Dependent Claim
16 words
The method of claim 7 in which said carrier system comprises a monomeric hydrogel forming material.
Claim 16
Dependent Claim
32 words
The method of claim 7 in which said carrier system comprises a monomeric hydrogel forming material which is the same as the hydrogel-forming material from which the lens is to be made.
Claim 17
Dependent Claim
13 words
The method of claim 7 in which the monomer is a hydroxyethyl methacrylate.
Claim 18
Dependent Claim
13 words
The method of claim 7 in which the colouring material is titanium dioxide.
Claim 19
Dependent Claim
13 words
The method of claim 7 in which the colouring material is phthalocyanine blue.
Claim 20
Dependent Claim
13 words
The method of claim 7 in which the colouring material is phthalocyanine green.
Claim 21
Dependent Claim
21 words
The method of claim 7 in which the colouring material is a mixture of titanium dioxide, phthalocyanine blue and phthalocyanine green.
Claim 22
Dependent Claim
55 words
The method of claim 7 in which, area sections of the mould surface, whose area are within the area of the surface which corresponds to the pupil of the contact lens or the periphery surrounding the section to which the colouring/coloured pattern is applied, are masked during the electrical corona discharge treatment of the surface.
Claim 23
Independent Claim
115 words
The method of producing a coloured contact lens comprising the steps of treating the surface of a hydrophobic casting mould with electrical corona discharge, preparing a colouring dispersion comprising from 10 to 90% by weight of monomeric hydroxyethyl methacrylate and from 10 to 90% by weight of a colouring material which is insoluble in hydroxyethyl methacrylate, using the said dispersion to imprint a pattern on a surface of said treated casting mould, introducing additional hydroxyethyl methacrylate monomer in said mould in contact with said imprinted surface, polymerizing said monomer to produce a lens blank having a coloured pattern impregnated in said blank, adjacent an optical surface thereof, and subsequently removing said lens from said mould.
Claim 24
Independent Claim
115 words
The method of producing a coloured contact lens comprising the steps of treating the surface of a hydrophobic casting mould with electrical corona discharge, preparing a colouring dispersion comprising from 10 to 90% by weight of monomeric hydroxyethyl methacrylate and from 10 to 90% by weight of a colouring material which is insoluble in hydroxyethyl methacrylate, using the said dispersion to imprint a pattern on a surface of said treated casting mould, introducing additional hydroxyethyl methacrylate monomer in said mould in contact with said imprinted surface, polymerizing said monomer to produce a lens blank having a coloured pattern impregnated in said blank, adjacent an optical surface thereof, and subsequently removing said lens from said mould.
Claim 25
Dependent Claim
44 words
The process of claim 21 in which the colouring dispersion comprises from 60 to 80% hydroxyethyl methacrylate monomer, from 1 to 25% titanium dioxide, from 0.01 to 5% phthalocyanine blue, from 0.01 to 3% black iron oxide, and from 1 to 5% fumed silica.
Claim 26
Dependent Claim
17 words
The process of claim 21 in which the pigment particles are less than 5 microns in size.
Claim 27
Dependent Claim
23 words
The process of claim 21 in which the said lens blank is subsequently hydrated and finished to produce a coloured soft hydrogel lens.
Claim 28
Dependent Claim
56 words
The method of claim 21 in which, area sections of the mould surface, whose area are within the area of the surface which corresponds to the pupil of the contact lens or the periphery surrounding the section to which the colouring coloured pattern is applied, are masked during the electrical corona discharge treatment of the surface.
Claim 29
Independent Claim
128 words
The method of producing a contact lens comprising the steps of treating a surface of a lens casting mould with electrical corona discharge, selecting an active material which is insoluble in the monomer material to be used in the lens, dispersing said active material in a carrier system which is compatible with said monomer material, using the resulting dispersion to coat the corona discharge treated surface of said casting mould, treating the coated surface of said lens casting mould with further electrical corona discharge, introducing a monomeric lens forming liquid in said mould in contact with said coated surface, polymerizing said liquid to produce a lens blank having an active material impregnated in said blank, adjacent an optical surface thereof, and subsequently removing said lens from said mould.
Claim 30
Independent Claim
128 words
The method of producing a contact lens comprising the steps of treating a surface of a lens casting mould with electrical corona discharge, selecting an active material which is insoluble in the monomer material to be used in the lens, dispersing said active material in a carrier system which is compatible with said monomer material, using the resulting dispersion to coat the corona discharge treated surface of said casting mould, treating the coated surface of said lens casting mould with further electrical corona discharge, introducing a monomeric lens forming liquid in said mould in contact with said coated surface, polymerizing said liquid to produce a lens blank having an active material impregnated in said blank, adjacent an optical surface thereof, and subsequently removing said lens from said mould.
Claim 31
Independent Claim
129 words
The method of producing a contact lens comprising the steps of treating a surface of a lens casting mould with electrical corona discharge, selecting a colouring material which is insoluble in the monomer material to be used in the lens, dispersing said colouring material in a carrier system which is compatible with said monomer material, using the resulting dispersion to imprint a pattern on a surface of said casting mould, introducing a monomeric lens forming liquid in said treated mould, polymerizing said liquid to produce a lens blank having a first optical surface thereon and a colour pattern impregnated therein, generating a second optical surface on said blank while said casting mould containing said blank is mounted on a precision mandrel, and subsequently removing said lens from said mould.
Claim 32
Independent Claim
129 words
The method of producing a contact lens comprising the steps of treating a surface of a lens casting mould with electrical corona discharge, selecting a colouring material which is insoluble in the monomer material to be used in the lens, dispersing said colouring material in a carrier system which is compatible with said monomer material, using the resulting dispersion to imprint a pattern on a surface of said casting mould, introducing a monomeric lens forming liquid in said treated mould, polymerizing said liquid to produce a lens blank having a first optical surface thereon and a colour pattern impregnated therein, generating a second optical surface on said blank while said casting mould containing said blank is mounted on a precision mandrel, and subsequently removing said lens from said mould.
References Cited (Backward Citations)
US3171869A
Cited
US3294971A
Cited
US3419489A
Cited
US3526583A
Cited
US3668097A
Cited
US3661735A
Cited
US3925178A
Cited
US4072769A
Cited
US4055378A
Cited
US3854982A
Cited
US4073577A
Cited
US4157892A
Cited
US4038165A
Cited
US4214014A
Cited
US4297187A
Cited
US4409258A
Cited
US4445991A
Cited
US4457880A
Cited
US4568501A
Cited
US4594401A
Cited
US4534723A
Cited
EP0158999A2
Cited
US4740282A
Cited
US4836901A
Cited
US4702574A
Cited
US4786444A
Cited
US4955580A
Cited
EP0362137A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-27 | 1996-04-27 | 1996-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-27 | 2000-04-27 | 2000-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-27 | 2004-04-27 | 2004-10-27 | $7700.00 | Window Closed / Lapsed |