Producing low shrink packaging film
Assignee: Applied Extrusion Technologies Inc
•
Filing: 1991-01-30
•
Granted: 1992-10-06
•
Expires: 2011-01-30
Abstract
Abstract Biaxially oriented film is post-treated by an annealing process in a limited temperature range of 45 DEG C. to 120 DEG C. for various time periods based on the temperature for annealing in order to produce a film having less than a 0.2% shrinkage in the machine direction as measured at 51.7 DEG C. for 24 hours. This film has a wide range of uses, such as overwrapping film.
Inventors
- 👤 Paul C. Gillette
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:49
CPC Classifications
B; B29; B29C; B29C71/00; B29C71/02; B29C2071/022; B29C55/00; B29K; B29K2995/00; B29K2995/0037; B29K2995/0049; B29K2995/005; B29K2995/0053
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
74 words
A process for increasing stability of formed and biaxially oriented polyolefin film comprising heat treating said formed and biaxially oriented polyolefin film under unconstrained conditions within a temperature range of from about 45° C. to about 120° C. over a corresponding time period of from at least about 48 hours to not more than about 2 seconds to obtain a film having shrink properties of less than about 0.2% measured in the machine direction.
Claim 2
Dependent Claim
74 words
A process for increasing stability of formed and biaxially oriented polyolefin film comprising heat treating said formed and biaxially oriented polyolefin film under unconstrained conditions within a temperature range of from about 45° C. to about 120° C. over a corresponding time period of from at least about 48 hours to not more than about 2 seconds to obtain a film having shrink properties of less than about 0.2% measured in the machine direction.
Claim 3
Dependent Claim
20 words
The process of claim 1 wherein the polyolefin film is an alpha-olefin homopolymer or copolymer having 2 to 5 carbons.
Claim 4
Dependent Claim
10 words
The process of claim 2 wherein the alpha-olefin is polypropylene.
Claim 5
Dependent Claim
60 words
The process of claim 1 wherein the treating step is effected at a time/temperature relationship defined by parameters selected from the group consisting of i) not less than 24 hours at 52° C., ii) not less than 8 hours at 55° C., iii) not less than 2 hours at 65° C., iv) not less than 1.5 hours at 75° C.
Claim 6
Dependent Claim
34 words
The process of claim 4 wherein the surface layer comprises 1 to 20%, based on the weight of the core layer, of a copolymer of ethylene/propylene containing 92 to 97% by weight of propylene.
Claim 7
Dependent Claim
53 words
The process of claim 5 wherein the formed and biaxially oriented film comprises isotactic polypropylene having a density from abut 0.86 to about 0.92 g/cc measured at 23° C., a melt flow index of from 1 to 15 g/10 minutes, orientation of 500% in the machine direction and 900% in the transverse direction.
Claim 8
Dependent Claim
56 words
The process of claim 1 wherein the polyolefin film is a laminate having (a) a core layer comprised of 70% to 100% by weight of polypropylene and 0% to 30% by weight hydrogenated terpene or petroleum resin having a molecular weight less than that of said polyolefin, plus (b) at least one heat sealable surface layer.
References Cited (Backward Citations)
GB873220A
Cited
US3361728A
Cited
US3508944A
Cited
US3570052A
Cited
US3671383A
Cited
US3632733A
Cited
US4343852A
Cited
US4415523A
Cited
US4390385A
Cited
US4597920A
Cited
US4436888A
Cited
US4652409A
Cited
US4652490A
Cited
US4649009A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-06 | 1996-04-06 | 1996-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-06 | 2000-04-06 | 2000-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-06 | 2004-04-06 | 2004-10-06 | $7700.00 | Window Closed / Lapsed |