Energy absorbing, water blown, rigid polyurethane foam
Assignee: BASF Corp
•
Filing: 1991-11-21
•
Granted: 1992-09-01
•
Expires: 2011-11-21
Abstract
Abstract The invention relates to energy absorbing, water blown, rigid polyurethane foams. The foams of the present invention are low density, predominantly open celled foams which exhibit a relatively constant consistency of compressive strength over deflection. Such foams are suitable as light weight alternatives in traditional energy absorbing applications.
Inventors
- 👤 Richard C. Rossio
- 👤 Mark A. Easterle
- 👤 Jackson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 05:03
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/65; C08G18/30; C08G18/32; C08G18/3203; C08G18/40; C08G18/48; C08G18/487; C08G18/4883; C08G18/66; C08G18/6666; C08G18/667; C08G18/6674; C08G18/6677; C08G18/70; C08G18/72; C08G18/74; C08G18/76; C08G18/7657; C08G18/7664; C08G2110/00; C08G2110/0025; C08G2110/0041; C08G2110/005; C08G2110/0058; C08G2110/0083; C08G2120/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
167 words
A method of preparing an energy absorbing polyurethane foam, comprising; A) reacting in a closed, preheated, prepared mold a formulation capable of producing a predominantly open-celled energy absorbing foam, comprising; i) a compound containing isocyanate reactive hydroxyl groups selected from the group consisting of aliphatic glycols, dihydroxy aromatics, bisphenols, hydroxyl terminated polyoxyalkylenes polyols, polyesters, polyacetals, and mixtures thereof, ii) an organic isocyanate selected from the group consisting of 4,4'-diphenylmethane diisocyanate, mixtures of 4,4'- and 2,4-diphenylmethane diisocyanate, polymethylene polyphenylene polyisocyanate, modified diphenylmethane diisocyanates and mixtures thereof, wherein other organic isocyanates may be present in minor amounts. iii) a catalyst, iv) water present in amounts sufficient to act as a blowing agent and a cell opening agent, v) a surfactant, and vi) a cross-linker, B) demolding and curing said article, wherein the cured foam has a molded density of from about 2.0 pcf to about 4.5 pcf and a crush strength which remains constant from about 10 percent to about 70 percent deflection at loads less than 70 psi.
Claim 2
Independent Claim
167 words
A method of preparing an energy absorbing polyurethane foam, comprising; A) reacting in a closed, preheated, prepared mold a formulation capable of producing a predominantly open-celled energy absorbing foam, comprising; i) a compound containing isocyanate reactive hydroxyl groups selected from the group consisting of aliphatic glycols, dihydroxy aromatics, bisphenols, hydroxyl terminated polyoxyalkylenes polyols, polyesters, polyacetals, and mixtures thereof, ii) an organic isocyanate selected from the group consisting of 4,4'-diphenylmethane diisocyanate, mixtures of 4,4'- and 2,4-diphenylmethane diisocyanate, polymethylene polyphenylene polyisocyanate, modified diphenylmethane diisocyanates and mixtures thereof, wherein other organic isocyanates may be present in minor amounts. iii) a catalyst, iv) water present in amounts sufficient to act as a blowing agent and a cell opening agent, v) a surfactant, and vi) a cross-linker, B) demolding and curing said article, wherein the cured foam has a molded density of from about 2.0 pcf to about 4.5 pcf and a crush strength which remains constant from about 10 percent to about 70 percent deflection at loads less than 70 psi.
Claim 3
Dependent Claim
19 words
A method as claimed in claim 1, wherein the compound containing isocyanate reactive groups is a hydroxyl-terminated polyoxyalkylene polyol.
Claim 4
Dependent Claim
39 words
A method as claimed in claim 1, wherein the compound containing isocyanate reactive groups is a propylene oxide adduct of a sucrose/dipropylene glycol mixed initiator having a molecular weight of about 620 and a hydroxyl number of about 400.
Claim 5
Dependent Claim
15 words
A method as claimed in claim 1, wherein the isocyanate is a polymeric polymethylene polyphenylisocyanate.
Claim 6
Dependent Claim
14 words
A method as claimed in claim 1, wherein the surfactant is a silicone surfactant.
Claim 7
Dependent Claim
12 words
A method as claimed in claim 1, wherein the crosslinker is glycerin.
Claim 8
Dependent Claim
23 words
A method as claimed in claim 1, wherein water is present in amounts from about 2 wt. % to about 30 wt. %.
Claim 9
Dependent Claim
23 words
A method as claimed in claim 1, wherein water is present in amounts from about 6 wt. % to about 15 wt. %.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-01 | 1996-03-02 | 1996-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-01 | 2000-03-02 | 2000-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-01 | 2004-03-02 | 2004-09-01 | $7700.00 | Window Closed / Lapsed |