Method to recover organic templates from freshly synthesized molecular sieves
Assignee: Mobil Oil AS
•
Filing: 1991-07-18
•
Granted: 1992-09-01
•
Expires: 2011-07-18
Abstract
Abstract This invention relates to a method for removing organic directing agents from as-synthesized molecular sieves comprising: (a) contacting said porous synthetic material with polar solvent having dissolved therein at least one cation donor, wherein said polar solvent is characterized by solubility parameters fd, fp, and fh wherein the values of solubility parameters fd, fp, and fh are defined by a circular region of the Teas diagram of Figure 41, said circular region having a center defined by the coordinates (fd=46, fp=22, fh=32) and encompassing about 21 percent of the total area of said Teas diagram of Figure 41, and wherein each of said sorbed templating agent and said cation donor are soluble in said polar solvent; and (b) holding said porous synthetic material, said nonaqueous polar solvent, and said cation donor of step (a) in contact at elevated temperature for a period of time sufficient to absorb at least a portion of said templating agent from said synthetic material.
Inventors
- 👤 D. Duayne Whitehurst
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:40
CPC Classifications
C; C01; C01B; C01B39/00; C01B39/02; C01B39/04; B; B01; B01J; B01J29/00; B01J29/82; C01B37/00; C01B37/02; C01B37/06; C01B37/08; C01B39/46; C01B39/48; B01J2229/00; B01J2229/30; B01J2229/36
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
183 words
A method for removing a templating agent from a porous synthetic material having said templating agent sorbed within pores of said synthetic material comprising: (a) contacting said porous synthethic material with polar solvent having dissolved therein at least one cation donor, wherein said polar solvent is characterized by Solubility parameters f d , f p , and f h wherein the values of solubility parameters f d , f p , and f h are defined by a circular region of the Teas diagram of FIG. 41, said circular region having a center defined by the coordinates (f d =46, f p =22, f h =32) and encompassing about 21 percent of the total area of said Teas diagram in FIG. 41, and wherein each of said sorbed templating agent and said cation donor are soluble in said polar solvent; and (b) holding said porous synthetic material, said nonaqueous polar solvent, and said cation donor of step (a) in contact at elevated temperature for a period of time sufficient to desorb at least a portion of said templating agent from said synthetic material.
Claim 2
Independent Claim
183 words
A method for removing a templating agent from a porous synthetic material having said templating agent sorbed within pores of said synthetic material comprising: (a) contacting said porous synthethic material with polar solvent having dissolved therein at least one cation donor, wherein said polar solvent is characterized by Solubility parameters f d , f p , and f h wherein the values of solubility parameters f d , f p , and f h are defined by a circular region of the Teas diagram of FIG. 41, said circular region having a center defined by the coordinates (f d =46, f p =22, f h =32) and encompassing about 21 percent of the total area of said Teas diagram in FIG. 41, and wherein each of said sorbed templating agent and said cation donor are soluble in said polar solvent; and (b) holding said porous synthetic material, said nonaqueous polar solvent, and said cation donor of step (a) in contact at elevated temperature for a period of time sufficient to desorb at least a portion of said templating agent from said synthetic material.
Claim 3
Dependent Claim
43 words
The method of claim 1 wherein said circular region has a center defined by the coordinates (f d =58, f p =15 , f h =27) and wherein said circular region encompasses about 7 percent of the total area of said Teas diagram.
Claim 4
Dependent Claim
19 words
The method of claim 1 wherein said cation donor comprises an inorganic acid or salt of said inorganic acid.
Claim 5
Dependent Claim
28 words
The method of claim 1 wherein said polar solvent is selected from the group consisting of aromatic or aliphatic ethers, alcohols, amines, esters halogenated hydrocarbons, and carboxylic acids.
Claim 6
Dependent Claim
13 words
The method of claim 3 wherein said cation donor comprises an ammonium salt.
Claim 7
Dependent Claim
13 words
The method of claim 1 wherein the temperature is at least 70° C.
Claim 8
Independent Claim
134 words
A method for removing a directing agent from a porous synthetic crystalline material having said templating agent sorbed within pores of said synthetic material comprising: (a) contacting said porous synthethic material with polar solvent having dissolved therein at least one cation donor, said polar solvent characterized by solubility parameters f d , f p , and f h which are defined by the area of the larger circle of the Teas diagram of FIG. 41, wherein each of said sorbed templating agent and said cation donor are soluble in said extraction solvent; and (b) holding said porous synthetic material, said extraction solvent, and said cation donor of step (a) in contact at elevated temperature for a period of time sufficient to desorb at least a portion of said templating agent from said synthetic material.
Claim 9
Independent Claim
134 words
A method for removing a directing agent from a porous synthetic crystalline material having said templating agent sorbed within pores of said synthetic material comprising: (a) contacting said porous synthethic material with polar solvent having dissolved therein at least one cation donor, said polar solvent characterized by solubility parameters f d , f p , and f h which are defined by the area of the larger circle of the Teas diagram of FIG. 41, wherein each of said sorbed templating agent and said cation donor are soluble in said extraction solvent; and (b) holding said porous synthetic material, said extraction solvent, and said cation donor of step (a) in contact at elevated temperature for a period of time sufficient to desorb at least a portion of said templating agent from said synthetic material.
Claim 10
Dependent Claim
29 words
The method of claim 7 wherein said polar solvent is characterized by solubility parameters which are defined by the smaller circle of the Teas dia gram of FIG. 41.
Claim 11
Dependent Claim
17 words
The method of claim 7 wherein the pH of said extraction solvent is less than about 7.
Claim 12
Dependent Claim
12 words
The method of claim 7 wherein said temperature is above 70° C.
Claim 13
Dependent Claim
19 words
The method of claim 7 wherein said cation donor comprises an inorganic acid or salt of said inorganic acid.
Claim 14
Dependent Claim
27 words
The method of claim 7 wherein said polar solvent is selected from the group consisting of aromatic or aliphatic ethers, alcohols, amines, halogenated hydrocarbons, and carboxylic acids.
Claim 15
Dependent Claim
13 words
The method of claim 7 wherein said cation donor comprises an ammonium salt.
Claim 16
Dependent Claim
18 words
The method of claim 7 wherein said polar solvent comprises an azeotropic mixture of at least two components.
Claim 17
Dependent Claim
12 words
The method of claim 14 wherein said components comprise heptane and ethanol.
Claim 18
Dependent Claim
15 words
The method of claim 15 wherein heptane and ethanol are present in approximately equal weights.
Claim 19
Dependent Claim
25 words
The process of claim 7 further comprising separating said polar solvent from extracted templating agent and recycling recovered polar solvent to said contacting step (a).
Claim 20
Dependent Claim
25 words
The process of claim 17 further comprising separating said cation donor from extracted templating agent and recycling recovered cation donor to said contacting step (a).
Claim 21
Independent Claim
198 words
A method for removing a directing agent from a porous synthetic material comprising an inorganic, porous, non-layered crystalline phase material exhibiting, after calcination, an X-ray diffraction pattern with at least one peak at a d-spacing greater than about 18 Angstrom Units with a relative intensity of 100, and a benzene adsorption capacity of greater than 15 grams benzene per 100 grams of said material at 50 torr and 25° C., said porous synthetic material having said templating agent sorbed within pores of said synthetic material, said recovery method comprising: (a) contacting said porous synthethic material with polar solvent having dissolved therein at least one cation donor, said polar solvent characterized by solubility parameters f d , f p , and f h which are defined by the area of the larger circle of the Teas diagram of FIG. 41, wherein each of said sorbed templating agent and said cation donor are soluble in said extraction solvent; and (b) holding said porous synthetic material, said extraction solvent, and said cation donor of step (a) in contact at elevated temperature for a period of time sufficient to desorb at least a portion of said templating agent from said synthetic material.
Claim 22
Independent Claim
198 words
A method for removing a directing agent from a porous synthetic material comprising an inorganic, porous, non-layered crystalline phase material exhibiting, after calcination, an X-ray diffraction pattern with at least one peak at a d-spacing greater than about 18 Angstrom Units with a relative intensity of 100, and a benzene adsorption capacity of greater than 15 grams benzene per 100 grams of said material at 50 torr and 25° C., said porous synthetic material having said templating agent sorbed within pores of said synthetic material, said recovery method comprising: (a) contacting said porous synthethic material with polar solvent having dissolved therein at least one cation donor, said polar solvent characterized by solubility parameters f d , f p , and f h which are defined by the area of the larger circle of the Teas diagram of FIG. 41, wherein each of said sorbed templating agent and said cation donor are soluble in said extraction solvent; and (b) holding said porous synthetic material, said extraction solvent, and said cation donor of step (a) in contact at elevated temperature for a period of time sufficient to desorb at least a portion of said templating agent from said synthetic material.
Claim 23
Dependent Claim
27 words
The method of claim 19 wherein said polar solvent is selected from the group consisting of aromatic or aliphatic ethers, alcohols, amines, halogenated hydrocarbons, and carboxylic acids.
Claim 24
Dependent Claim
13 words
The method of claim 19 wherein said cation donor comprises an ammonium salt.
Claim 25
Dependent Claim
18 words
The method of claim 19 wherein said polar solvent comprises an azeotropic mixture of at least two components.
Claim 26
Dependent Claim
12 words
The method of claim 22 wherein said components comprise heptane and ethanol.
Claim 27
Dependent Claim
15 words
The method of claim 23 wherein heptane and ethanol are present in approximately equal weights.
Claim 28
Dependent Claim
25 words
The process of claim 19 further comprising separating said polar solvent from extracted templating agent and recycling recovered polar solvent to said contacting step (a).
Claim 29
Dependent Claim
25 words
The process of claim 25 further comprising separating said cation donor from extracted templating agent and recycling recovered cation donor to said contacting step (a).
References Cited (Backward Citations)
US3791964A
Cited
US3355246A
Cited
US4176090A
Cited
US4216188A
Cited
US4248739A
Cited
US4385994A
Cited
US4310440A
Cited
US4335020A
Cited
US4367163A
Cited
GB2109402A
Cited
US4440871A
Cited
US4673559A
Cited
US4880611A
Cited
US4831006A
Cited
US4859648A
Cited
US4916097A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-01 | 1996-03-02 | 1996-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-01 | 2000-03-02 | 2000-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-01 | 2004-03-02 | 2004-09-01 | $7700.00 | Window Closed / Lapsed |