Process for preparing metallized polyimide film
Assignee: Ube Corp
•
Filing: 1990-11-15
•
Granted: 1992-07-14
•
Expires: 2010-11-15
Abstract
Abstract A process for preparing a metallized polyimide film, comprising the steps of: forming a solidified film containing 100 parts by weight of an aromatic polyamic acid in the form of a solution obtained by polymerizing approximately equal moles of an aromatic tetracarboxylic acid component and an aromatic diamine component and 5 to 150 parts by weight of an organic polar solvent; applying a surface treatment solution containing a heat-resistant surface treating agent to the surface of the solidified film; heating the solidified film to a high temperature to imidize the polyamic acid, while drying the film to prepare a polyimide film; forming a thin metal vapor-deposited layer by a vapor deposition of a metal on the treated surface of the polyimide film with the heat-resistant surface treatment agent; and applying metal plating onto the metal vapor deposited layer to form a metal plated layer thereon.
Inventors
- 👤 Seiichirou Takabayashi
- 👤 Kazuaki Mii
- 👤 Kenichiro Yano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 16:12
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/38; H05K3/388; C; C08; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1007; C08G73/1028; C08G73/1032; C08G73/1067; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/20; H05K3/389; H05K2201/00; H05K2201/01; H05K2201/0137; H05K2201/0154; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/31504; Y10T428/31678; Y10T428/31681
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
147 words
A process for preparing a metallized polyimide film, comprising the steps of: forming a solidified film containing 100 parts by weight of an aromatic polyamic acid in the form of a solution obtained by polymerizing approximately equal moles of an aromatic tetracarboxylic acid component and an aromatic diamine component and 5 to 150 parts by weight of an organic polar solvent; applying a surface treatment solution containing a heat-resistant surface treating agent to the surface of the solidified film; heating said solidified film to a high temperature to imidize the polyamic acid, while drying said film to prepare a polyimide film; forming a thin metal vapor deposited layer by a vapor deposition of a metal on the surface of the polyimide film treated with the heat-resistant surface treatment agent; and applying a metal plating onto the metal vapor deposited layer to form a metal plated layer thereon.
Claim 2
Dependent Claim
147 words
A process for preparing a metallized polyimide film, comprising the steps of: forming a solidified film containing 100 parts by weight of an aromatic polyamic acid in the form of a solution obtained by polymerizing approximately equal moles of an aromatic tetracarboxylic acid component and an aromatic diamine component and 5 to 150 parts by weight of an organic polar solvent; applying a surface treatment solution containing a heat-resistant surface treating agent to the surface of the solidified film; heating said solidified film to a high temperature to imidize the polyamic acid, while drying said film to prepare a polyimide film; forming a thin metal vapor deposited layer by a vapor deposition of a metal on the surface of the polyimide film treated with the heat-resistant surface treatment agent; and applying a metal plating onto the metal vapor deposited layer to form a metal plated layer thereon.
Claim 3
Dependent Claim
42 words
A process as claimed in claim 1, wherein said aromatic tetracarboxylic acid component contains 60 mole % or more of at least one component selected from the group consisting of biphenyltetracarboxylic acids, acid anhydrides thereof, and esterified products thereof with lower alcohols.
Claim 4
Dependent Claim
20 words
A process as claimed in claim 1, wherein said aromatic diamine component contains 60 mole % or more of p-phenylenediamine.
Claim 5
Dependent Claim
33 words
A process as claimed in claim 1, wherein said aromatic polyamic acid has a logarithmic viscosity of 0.1 to 7 determined at 30° C. and at a concentration of 0.5 g/100 ml N-methyl-2-pyrrolidone.
Claim 6
Dependent Claim
23 words
A process as claimed in claim 1, wherein the imidization degree is 85% or less, as determined by an infrared spectral analytical method.
Claim 7
Dependent Claim
32 words
A process as claimed in claim 1, wherein said organic polar solvent is an organic polar solvent capable of uniformly dissolving 2% to 50% by weight of the aromatic polyamic acid therein.
Claim 8
Dependent Claim
43 words
A process as claimed in claim 1, wherein said surface treating agent is at least one agent selected from the group consisting of heat-resistant aminosilane type, epoxysilane type and titanate type surface treating agents having a decomposition temperature of 275° C. or more.
Claim 9
Dependent Claim
32 words
A process as claimed in claim 1, wherein said metal is at least one member selected from the group consisting of noble metals, alkaline earth metals and transition metals and oxides thereof.
Claim 10
Dependent Claim
39 words
A process as claimed in claim 1, wherein said metal plated layer is composed of at least one member selected from the group consisting of copper, nickel, chromium, zinc, cadmium, tin, lead, gold, silver, cobalt, antimony, bismuth and arsenic.
Claim 11
Dependent Claim
44 words
A metallized polyimide film obtained by the process of claim 1, wherein the thicknesses of the polyimide film, the thin metal vapor deposited film, and the metal plated layer are 5 to 200 μm, 50 to 50,000 Å, and 1 to 100 μm, respectively.
Claim 12
Dependent Claim
68 words
A process for preparing a metallized polyimide film, comprising the steps of: forming a coating layer or a vapor deposited layer of an inorganic substance on one surface of an aromatic polyimide film; directly vapor-depositing a metal on the other surface of said film to form a thin metal deposited layer; and applying a metal plating onto the metal vapor deposited layer to form a metal plated layer.
Claim 13
Dependent Claim
68 words
A process for preparing a metallized polyimide film, comprising the steps of: forming a coating layer or a vapor deposited layer of an inorganic substance on one surface of an aromatic polyimide film; directly vapor-depositing a metal on the other surface of said film to form a thin metal deposited layer; and applying a metal plating onto the metal vapor deposited layer to form a metal plated layer.
Claim 14
Dependent Claim
29 words
A process as claimed in claim 11, wherein said aromatic polyimide film is obtained by polymerization and imidization of an aromatic tetracarboxylic acid component and an aromatic diamine component.
Claim 15
Dependent Claim
42 words
A process as claimed in claim 12, wherein said aromatic tetracarboxylic acid component contains 60 mole % or more of at least one component selected from the group consisting of biphenyltetracarboxylic acids, acid anhydrides thereof, and esterified products thereof with lower alcohols.
Claim 16
Dependent Claim
20 words
A process as claimed in claim 12, wherein said aromatic diamine component contains 60 mole % or more of p-phenylenediamine.
Claim 17
Dependent Claim
32 words
A process as claimed in claim 11, wherein said metal is at least one member selected from the group consisting of noble metals, alkaline earth metals and transition metals and oxides thereof.
Claim 18
Dependent Claim
39 words
A process as claimed in claim 11, wherein said metal plated layer is composed of at least one member selected from the group consisting of copper, nickel, chromium, zinc, cadmium, tin, lead, gold, silver, cobalt, antimony, bismuth and arsenic.
Claim 19
Dependent Claim
44 words
A metallized polyimide film obtained by the process of claim 11, wherein the thicknesses of the polyimide film, the thin metal vapor deposited film, and the metal plated layer are 5 to 200 μm, 50 to 50,000 Å, and 1 to 100 μm, respectively.
References Cited (Backward Citations)
JPS54141391A
Cited
JPS557805A
Cited
US4405678A
Cited
JPS6042817A
Cited
US4710403A
Cited
US4775556A
Cited
US4975327A
Cited
US4959121A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-14 | 1996-01-13 | 1996-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-14 | 2000-01-13 | 2000-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-14 | 2004-01-13 | 2004-07-14 | $7700.00 | Window Closed / Lapsed |