Microwave pcvd method for continuously forming a large area functional deposited film using a curved moving substrate web with microwave energy with a directivity in one direction perpendicular to the direction of microwave propagation
Assignee: Canon Inc
•
Filing: 1990-06-26
•
Granted: 1992-07-14
•
Expires: 2010-06-26
Abstract
Abstract A method for continuously forming a large area functional deposited film by a microwave plasma CVD process, said method comprises: continuously moving a substrate web in the longitudinal direction; establishing a substantially enclosed film-forming chamber having a film-forming space by curving and projecting said moving substrate web to form a columnar portion to be the circumferential wall of said film forming chamber; introducing a film-forming raw material gas through a gas feed means into said film-forming space; at the same time, radiating or propagating microwave energy into said film-forming space by using a microwave applicator means capable of radiating or propagating said microwave energy with a directivity in one direction perpendicular to the direction of microwave propagation, to thereby generate plasma in said film-forming space, whereby continuously forming a functional deposited film on the inner face of said continuoulsy moving circumferential wall which is exposed to said plasma.
Inventors
- 👤 Masahiro Kanai
- 👤 Jinsho Matsuyama
- 👤 Katsumi Nakagawa
- 👤 Toshimitsu Kariya
- 👤 Yasushi Fujioka
- 👤 Tetsuya Takei
- 👤 Hiroshi Echizen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:28
CPC Classifications
H; H10; H10F; H10F10/00; H10F10/10; H10F10/17; H10F10/172; C; C23; C23C; C23C16/00; C23C16/44; C23C16/50; C23C16/54; C23C16/545; H01; H01J; H01J37/00; H01J37/32; H01J37/32009; H01J37/32192; H01J37/32211; H01J37/3222; H01J37/32431; H01J37/32733; H01J37/32752; H01J37/32761; H01J37/3277; H10F71/00; H10F71/10; H10F71/107; H01J2237/00; H01J2237/32; H01J2237/33; H01J2237/332; H01J2237/3322; H01J2237/3325; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/548; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
147 words
A method for continuously forming a large area functional deposited film by a microwave plasma CVD process, said method comprises: continuously moving a substrate web in the longitudinal direction; establishing a substantially enclosed film-forming chamber having a film-forming space by curving and projecting said moving substrate web to form a columnar portion to be the circumferential wall of said film forming chamber; introducing a film-forming raw material gas through a gas feed means into said film-forming space; simultaneously, radiating or propagating microwave energy into said film-forming space by using a microwave applicator means capable of radiating or propagating said microwave energy with a directivity in one direction perpendicular to the direction of microwave propagation to thereby generate microwave plasma in said film-forming space, whereby continuously forming a functional deposited film on the inner face of said continuously moving circumferential wall to be exposed to said microwave plasma.
Claim 2
Independent Claim
147 words
A method for continuously forming a large area functional deposited film by a microwave plasma CVD process, said method comprises: continuously moving a substrate web in the longitudinal direction; establishing a substantially enclosed film-forming chamber having a film-forming space by curving and projecting said moving substrate web to form a columnar portion to be the circumferential wall of said film forming chamber; introducing a film-forming raw material gas through a gas feed means into said film-forming space; simultaneously, radiating or propagating microwave energy into said film-forming space by using a microwave applicator means capable of radiating or propagating said microwave energy with a directivity in one direction perpendicular to the direction of microwave propagation to thereby generate microwave plasma in said film-forming space, whereby continuously forming a functional deposited film on the inner face of said continuously moving circumferential wall to be exposed to said microwave plasma.
Claim 3
Dependent Claim
41 words
The method according to claim 1, wherein the film-forming chamber is configured such that does not permit microwave energy radiated or propagated into the film-forming space to leak outside said chamber and microwave plasma generated is confined within the film-forming space.
Claim 4
Dependent Claim
31 words
The method according to claim 1, wherein each of the two side faces of the columnar portion is sealed by a member capable of prohibiting microwave energy to be leaked therefrom.
Claim 5
Dependent Claim
68 words
The method according to claim 1, wherein the columnar portion is formed by curving the moving substrate web while being supported by means of a pair of supporting and transporting rollers while leaving a spacing of a desired width in the longitudinal direction between said pair of rollers and each of the two side end portions of the columnar portion is supported by a supporting and transporting ring.
Claim 6
Dependent Claim
31 words
The method according to claim 4, wherein each of the two side faces of the columnar portion is sealed by a member capable of prohibiting microwave energy to be leaked therefrom.
Claim 7
Dependent Claim
33 words
The method according to claim 4, wherein the microwave energy is radiated or propagated through the spacing into the film-forming space by the microwave applicator means being arranged in vicinity to the spacing.
Claim 8
Dependent Claim
23 words
The method according to claim 6, wherein the microwave applicator means is encapsuled in an isolating means made of a microwave transmissive material.
Claim 9
Dependent Claim
27 words
The method according to claim 1, wherein the microwave applicator means is arranged in the film-forming space in parallel to the circumferential wall of the film-forming chamber.
Claim 10
Dependent Claim
23 words
The method according to claim 8, wherein the microwave applicator means is encapsuled in an isolating means made of a microwave transmissive material.
Claim 11
Dependent Claim
17 words
The method according to claim 1, wherein the film-forming space is maintained at a desired gas pressure.
Claim 12
Dependent Claim
17 words
The method according to claim 4, wherein gas in the film-forming space is exhausted through the spacing.
Claim 13
Dependent Claim
20 words
The method according to claim 1, wherein the inner surface of the columnar portion is maintained at a desired temperature.
Claim 14
Dependent Claim
28 words
The method according to claim 1, wherein a temperature controlling mechanism capable of heating or cooling the substrate web is arranged near the exterior of the columnar portion.
Claim 15
Dependent Claim
19 words
The method according to claim 1 which further comprises the step of controlling the potential of the microwave plasma.
Claim 16
Dependent Claim
32 words
The method according to claim 14, wherein the step of controlling the potential of the microwave plasma is carried out by using a bias voltage applying means isolated from the substrate web.
Claim 17
Dependent Claim
33 words
The method according to claim 15, wherein said bias voltage applying means is placed in the film-forming space such that at least part of said means comes to contact with microwave plasma generated.
Claim 18
Dependent Claim
24 words
The method according to claim 16, wherein a bias voltage of DC, AC or pulsating current is applied onto the bias voltage applying means.
Claim 19
Dependent Claim
19 words
The method according to claim 15, wherein the bias voltage applying means serves also as the gas feed means.
Claim 20
Dependent Claim
18 words
The method according to claim 15, wherein the bias voltage applying means comprises one or more bias bars.
Claim 21
Dependent Claim
28 words
The method according to claim 14, wherein the step of controlling the potential of microwave plasma is carried out by applying a bias voltage onto the substrate web.
Claim 22
Dependent Claim
36 words
The method according to claim 20, wherein the gas feed means is electrically grounded and is placed in the film-forming space such that at least part of said means comes to contact with microwave plasma generated.
Claim 23
Independent Claim
151 words
A method for continuously forming a large area functional deposited film by a microwave plasma CVD process, said method comprises: continuously moving a substrate web in the longitudinal direction; establishing a substantially enclosed film-forming chamber having a film-forming space by curving and projecting said moving substrate web to form a columnar portion to be the circumferential wall of said film forming chamber as the substrate web is moving; introducing a film-forming raw material gas through a gas feed means into said film-forming space; while simultaneously, radiating or propagating evanescent microwave energy into said film-forming space by using a microwave applicator means capable of radiating or propagating said microwave energy with a directivity in one direction of evanescent microwave energy propagation, to thereby generate plasma in said film-forming space, whereby continuously forming a functional deposited film on the inner face of said continuously moving circumferential wall which is exposed to said plasma.
Claim 24
Independent Claim
151 words
A method for continuously forming a large area functional deposited film by a microwave plasma CVD process, said method comprises: continuously moving a substrate web in the longitudinal direction; establishing a substantially enclosed film-forming chamber having a film-forming space by curving and projecting said moving substrate web to form a columnar portion to be the circumferential wall of said film forming chamber as the substrate web is moving; introducing a film-forming raw material gas through a gas feed means into said film-forming space; while simultaneously, radiating or propagating evanescent microwave energy into said film-forming space by using a microwave applicator means capable of radiating or propagating said microwave energy with a directivity in one direction of evanescent microwave energy propagation, to thereby generate plasma in said film-forming space, whereby continuously forming a functional deposited film on the inner face of said continuously moving circumferential wall which is exposed to said plasma.
References Cited (Backward Citations)
US4400409A
Cited
JPS61288074A
Cited
US4729341A
Cited
US4723507A
Cited
US4740385A
Cited
US4893584A
Cited
US4995341A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-14 | 1996-01-13 | 1996-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-14 | 2000-01-13 | 2000-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-14 | 2004-01-13 | 2004-07-14 | $7700.00 | Window Closed / Lapsed |