Semiconductor device comprising a silicide layer, and method of making the device
Assignee: Nokia Bell Labs
•
Filing: 1991-04-11
•
Granted: 1992-06-16
•
Expires: 2011-04-11
Abstract
Abstract Disclosed is a method of making a Si-based semiconductor device comprising a contact region that comprises a thin (exemplarily less than 50 nm), substantially uniform silicide layer. The silicide preferably is CoSi 2 or TiSi 2 . The method comprises implantation of the appropriate metal ions into a Si body, the dose and the body temperature selected such that substantially complete amorphization of the implant volume results. Subsequently, the Si body is subjected to an annealing treatment that results in recrystallization of the implant volume and formation of the silicide layer. The layer extends to the surface of the body and contains essentially all of the implanted metal ions. The invention can advantageously be used in conjunction with extremely shallow junctions, such as will be of interest in short (e.g., <0.5 μm) channel CMOS devices.
Inventors
- 👤 Sarah A. Audet
- 👤 Conor S. Rafferty
- 👤 Kenneth T. Short
- 👤 Alice E. White
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:08
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10P30/208; Y; Y10; Y10S; Y10S148/00; Y10S148/003
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
209 words
A method of manufacturing an article comprising a single crystal Si body with a metal silicide-containing contact region on a major surface of the body, the method comprising a) providing the Si body; b) forming the contact region including forming a metal silicide layer; c) carrying out one or more further steps towards completion of the article; CHARACTERIZED IN THAT d) step b) comprises i) implanting metal ions into the portion of the Si body that is associated with the contact region, associated with the implantation being an energy, a dose and an implant volume, the dose and the Si body temperature selected such that substantially complete amorphization of the implant volume results, the energy selected such that the implant volume extends to the major surface, the metal ions selected from the group consisting of Co ions and Ti ions; and ii) annealing the Si body at a temperature and for a time selected to result in recrystallization of the implant volume and formation of a substantially uniform metal silicide layer that extends to the major surface and contains essentially all of said metal ions implanted into the body; wherein iii) the dose is selected such that the thickness of said metal silicide layer is less than 50 nm.
Claim 2
Independent Claim
209 words
A method of manufacturing an article comprising a single crystal Si body with a metal silicide-containing contact region on a major surface of the body, the method comprising a) providing the Si body; b) forming the contact region including forming a metal silicide layer; c) carrying out one or more further steps towards completion of the article; CHARACTERIZED IN THAT d) step b) comprises i) implanting metal ions into the portion of the Si body that is associated with the contact region, associated with the implantation being an energy, a dose and an implant volume, the dose and the Si body temperature selected such that substantially complete amorphization of the implant volume results, the energy selected such that the implant volume extends to the major surface, the metal ions selected from the group consisting of Co ions and Ti ions; and ii) annealing the Si body at a temperature and for a time selected to result in recrystallization of the implant volume and formation of a substantially uniform metal silicide layer that extends to the major surface and contains essentially all of said metal ions implanted into the body; wherein iii) the dose is selected such that the thickness of said metal silicide layer is less than 50 nm.
Claim 3
Dependent Claim
13 words
Method according to claim 1, wherein the major surface substantially has <100> orientation.
Claim 4
Dependent Claim
32 words
Method of claim 2, wherein the Si body during step d)i) is maintained at a temperature less than 100° C., and the ion dose is greater than 10 16 ions/cm 2 .
Claim 5
Dependent Claim
20 words
Method of claim 1, wherein step d)ii) comprises annealing the Si body at a temperature of 800° C. or less.
Claim 6
Dependent Claim
25 words
Method of claim 1, wherein step d)ii) comprises heating the Si body to a temperature above 800° C., for a time less than 60 seconds.
Claim 7
Dependent Claim
10 words
Method of claim 1, wherein the ions are Co ions.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-16 | 1995-12-16 | 1996-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-16 | 1999-12-16 | 2000-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-16 | 2003-12-16 | 2004-06-16 | $7700.00 | Window Closed / Lapsed |